• ### Thermal Expansion Coefficients of Bi$_2$Se$_3$ and Sb$_2$Te$_3$ Crystals from 10 K to 270 K(1112.1608)

Dec. 30, 2011 cond-mat.mtrl-sci
Lattice constant of Bi$_2$Se$_3$ and Sb$_2$Te$_3$ crystals is determined by X-ray powder diffraction measurement in a wide temperature range. Linear thermal expansion coefficients ($\alpha$) of the crystals are extracted, and considerable anisotropy between $\alpha_\parallel$ and $\alpha_\perp$ is observed. The low temperature values of $\alpha$ can be fit well by the Debye model, while an anomalous behavior at above 150 K is evidenced and explained. Gr\"uneisen parameters of the materials are also estimated at room temperature.
• ### Temperature dependence of Raman-active optical phonons in Bi_2Se_3 and Sb_2Te_3(1112.1364)

Inelastic light scattering spectra of Bi_2Se_3 and Sb_2Te_3 single crystals have been measured over the temperature range from 5 K to 300 K. The temperature dependence of dominant A^{2}_{1g} phonons shows similar behavior in both materials. The temperature dependence of the peak position and linewidth is analyzed considering the anharmonic decay of optical phonons and the material thermal expansion. This work suggests that Raman spectroscopy can be used for thermometry in Bi_2Se_3- and Sb_2Te_3-based devices in a wide temperature range.