• ### Superconductivity at 44 K in K intercalated FeSe system with excess Fe(1203.1533)

We report here that a new superconducting phase with much higher Tc has been found in K intercalated FeSe compound with excess Fe. We successfully grew crystals by precisely controlling the starting amount of Fe. Besides the superconducting (SC) transition at ~30 K, we observed a sharp drop in resistivity and a kink in susceptibility at 44 K. By combining thermodynamic measurements with electron spin resonance (ESR), we demonstrate that this is a new SC transition. Structural analysis unambiguously reveals two phases coexisting in the crystals, which are responsible respectively for the SC transitions at 30 and 44 K. The structural experiments and first-principles calculations consistently indicate that the 44 K SC phase is close to a 122 structure, but with an unexpectedly large c-axis of 18.10 {\AA}. We further find a novel monotonic dependence of the maximum Tc on the separation of neighbouring FeSe layers.
• ### Raman scattering in iron-based superconductors(1210.2889)

Iron-based superconducting layered compounds have the second highest transition temperature after cuprate superconductors. Their discovery is a milestone in the history of high-temperature superconductivity and will have profound implications for high-temperature superconducting mechanism as well as industrial applications. Raman scattering has been extensively applied to correlated electron systems including the new superconductors due to its unique ability to probe multiple primary excitations and their coupling. In this review, we will give a brief summary of the existing Raman experiments in the iron-based materials and their implication for pairing mechanism in particular. And we will also address some open issues from the experiments.
• ### Effect of iron content and potassium substitution in A$_{0.8}$Fe$_{1.6}$Se$_2$ (A = K, Rb, Tl) superconductors: a Raman-scattering investigation(1105.1198)

June 13, 2012 cond-mat.supr-con
We have performed Raman-scattering measurements on high-quality single crystals of the superconductors K$_{0.8}$Fe$_{1.6}$Se$_2$ ($T_c$ = 32 K), Tl$_{0.5}$K$_{0.3}$Fe$_{1.6}$Se$_2$ ($T_c$ = 29 K), and Tl$_{0.5}$Rb$_{0.3}$Fe$_{1.6}$Se$_2$ ($T_c$ = 31 K), as well as of the insulating compound KFe$_{1.5}$Se$_2$. To interpret our results, we have made first-principles calculations for the phonon modes in the ordered iron-vacancy structure of K$_{0.8}$Fe$_{1.6}$Se$_2$. The modes we observe can be assigned very well from our symmetry analysis and calculations, allowing us to compare Raman-active phonons in the AFeSe compounds. We find a clear frequency difference in most phonon modes between the superconducting and non-superconducting potassium crystals, indicating the fundamental influence of iron content. By contrast, substitution of K by Tl or Rb in A$_{0.8}$Fe$_{1.6}$Se$_2$ causes no substantial frequency shift for any modes above 60 cm$^{-1}$, demonstrating that the alkali-type metal has little effect on the microstructure of the FeSe layer. Several additional modes appear below 60 cm$^{-1}$ in Tl- and Rb-substituted samples, which are vibrations of heavier Tl and Rb ions. Finally, our calculations reveal the presence of "chiral" phonon modes, whose origin lies in the chiral nature of the K$_{0.8}$Fe$_{1.6}$Se$_2$ structure.
• ### Two-magnon Raman scattering in A$_{0.8}$Fe$_{1.6}$Se$_2$ systems: competition between superconductivity and antiferromagnetic order(1106.2706)

April 28, 2012 cond-mat.supr-con
We have performed Raman-scattering measurements on high-quality single crystals of A$_{0.8}$Fe$_{1.6}$Se$_2$ superconductors of several compositions. We find a broad, asymmetric peak around 1600 cm$^{-1}$ (200 meV), which we identify as a two-magnon process involving optical magnons. The intensity of the two-magnon peak falls sharply on entering the superconducting phase. This effect, which is entirely absent in the non-superconducting system KFe$_{1.5}$Se$_2$, requires a strong mutual exclusion between antiferromagnetism and superconductivity arising from proximity effects within regions of microscale phase separation.
• ### Vacancy ordering and phonon spectrum in the Fe superconductor K$_{0.8}$Fe$_{1.6}$Se$_2$(1101.2168)

We have performed Raman-scattering measurements on a high-quality single crystal of the recently discovered Fe-based superconductor K$_{0.8}$Fe$_{1.6}$Se$_2$ ($T_c$ = 32 K). At least thirteen phonon modes were observed in the wave number range 10$-$300 cm$^{-1}$. The spectra possess a four-fold symmetry indicative of bulk vacancy order in the Fe-deficient planes. We perform a vibration analysis based on first-principles calculations, which both confirms the ordered structure and allows a complete mode assignment. We observe an anomaly at $T_c$ in the 180 cm$^{-1}$ $A_g$ mode, which indicates a rather specific type of electron-phonon coupling.
• ### Raman phonons of $\alpha$-FeTe and Fe$_{1.03}$Se$_{0.3}$Te$_{0.7}$ single crystals(0811.2350)

April 11, 2009 cond-mat.supr-con
The polarized Raman scattering spectra of nonsuperconducting $\alpha$-FeTe and of the newly discovered, As-free superconductor Fe$_{1.03}$Se$_{0.3}$Te$_{0.7}$ are measured at room temperature on single crystals. The phonon modes are assigned by combining symmetry analysis with first-principles calculations. In the parent compound $\alpha$-FeTe, the A$_{1g}$ mode of the Te atom and the B$_{1g}$ mode of the Fe atom are observed clearly, while in superconducting Fe$_{1.03}$Se$_{0.3}$Te$_{0.7}$, only a softened Fe B$_{1g}$ mode can be seen. No electron-phonon coupling feature can be distinguished in the spectra of the two samples. By contrast, the spectra of the superconducting system show a slight enhancement below 300$cm^{-1}$, which may be of electronic origin.
• ### Raman spectra in iron-based quaternary CeO$_{1-x}$F$_x$FeAs and LaO$_{1-x}$F$_x$FeAs(0806.0885)

Raman spectra have been measured on iron-based quaternary CeO$_{1-x}$F$_x$FeAs and LaO$_{1-x}$F$_x$FeAs with varying fluorine doping at room temperatures. A group analysis has been made to clarify the optical modes. Based on the first principle calculations, the observed phonon modes can be assigned accordingly. In LaO$_{1-x}$F$_x$FeAs, the E$_g$ and A$_{1g}$ modes related to the vibrations of La, are suppressed with increasing F doping. However F doping only has a small effect on the E$_g$ and A$_{1g}$ modes of Fe and As. The Raman modes of La and As are absent in rare-earth substituted CeO$_{1-x}$F$_x$FeAs, and the E$_g$ mode of oxygen, corresponding to the in-plane vibration of oxygen, moves to around 450 cm$^{-1}$ and shows a very sharp peak. Electronic scattering background is low and electron-phonon coupling is not evident for the observed phonon modes. Three features are found above 500 cm$^{-1}$, which may be associated with multi-phonon process. Nevertheless it is also possible that they are related to magnetic fluctuations or interband transitions of d orbitals considering their energies.