Recently, the iridate double perovskite Sr$_2$YIrO$_6$ has attracted
considerable attention due to the report of unexpected magnetism in this
Ir$^{5+}$ (5d$^4$) material, in which according to the J$_{eff}$ model, a
non-magnetic ground state is expected. However, in recent works on
polycrystalline samples of the series Ba$_{2-x}$Sr$_x$YIrO$_6$ no indication of
magnetic transitions have been found. We present a structural, magnetic and
thermodynamic characterization of Sr$_2$YIrO$_6$ single crystals, with emphasis
on the temperature and magnetic field dependence of the specific heat. Here, we
demonstrate the clue role of single crystal X-ray diffraction on the structural
characterization of the Sr$_2$YIrO$_6$ double perovskite crystals by reporting
the detection of a $\sqrt{2}a \times \sqrt{2}a \times 1c$ supercell, where $a$,
$b$ and $c$ are the unit cell dimensions of the reported monoclinic subcell. In
agreement with the expected non-magnetic ground state of Ir$^{5+}$ (5d$^4$) in
Sr$_2$YIrO$_6$, no magnetic transition is observed down to 430~mK. Moreover,
our results suggest that the low temperature anomaly observed in the specific
heat is not related to the onset of long-range magnetic order. Instead, it is
identified as a Schottky anomaly caused by paramagnetic impurities present in
the sample, of the order of $n \sim 0.5(2)$ \%. These impurities lead to
non-negligible spin correlations, which nonetheless, are not associated with
long-range magnetic ordering.
Recently, the iridate double perovskite Sr$_2$YIrO$_6$ has attracted considerable attention due to the report of unexpected magnetism in this Ir$^{5+}$ (5d$^4$) material, in which according to the J$_{eff}$ model, a non-magnetic ground state is expected. However, in recent works on polycrystalline samples of the series Ba$_{2-x}$Sr$_x$YIrO$_6$ no indication of magnetic transitions have been found. We present a structural, magnetic and thermodynamic characterization of Sr$_2$YIrO$_6$ single crystals, with emphasis on the temperature and magnetic field dependence of the specific heat. Here, we demonstrate the clue role of single crystal X-ray diffraction on the structural characterization of the Sr$_2$YIrO$_6$ double perovskite crystals by reporting the detection of a $\sqrt{2}a \times \sqrt{2}a \times 1c$ supercell, where $a$, $b$ and $c$ are the unit cell dimensions of the reported monoclinic subcell. In agreement with the expected non-magnetic ground state of Ir$^{5+}$ (5d$^4$) in Sr$_2$YIrO$_6$, no magnetic transition is observed down to 430~mK. Moreover, our results suggest that the low temperature anomaly observed in the specific heat is not related to the onset of long-range magnetic order. Instead, it is identified as a Schottky anomaly caused by paramagnetic impurities present in the sample, of the order of $n \sim 0.5(2)$ \%. These impurities lead to non-negligible spin correlations, which nonetheless, are not associated with long-range magnetic ordering.
The ALICE Collaboration has measured inclusive J/psi production in pp collisions at a center of mass energy sqrt(s)=2.76 TeV at the LHC. The results presented in this Letter refer to the rapidity ranges |y|<0.9 and 2.5<y<4 and have been obtained by measuring the electron and muon pair decay channels, respectively. The integrated luminosities for the two channels are L^e_int=1.1 nb^-1 and L^mu_int=19.9 nb^-1, and the corresponding signal statistics are N_J/psi^e+e-=59 +/- 14 and N_J/psi^mu+mu-=1364 +/- 53. We present dsigma_J/psi/dy for the two rapidity regions under study and, for the forward-y range, d^2sigma_J/psi/dydp_t in the transverse momentum domain 0<p_t<8 GeV/c. The results are compared with previously published results at sqrt(s)=7 TeV and with theoretical calculations.