• We have investigated the superconducting ground state of the newly discovered superconductor ThFeAsN with a tetragonal layered crystal structure using resistivity, magnetization, heat capacity and transverse-field (TF) muon-spin rotation ($\mu$SR) measurements. Our resistivity and magnetization measurements reveal an onset of bulk superconductivity with $T_{\bf c}\sim$ 30 K. The heat capacity results show a very small anomaly, $\Delta$C$_{ele}$$\sim$0.214 (J/mol-K) at $T_{\bf c}\sim$ 30 K and exhibits exponential behavior below $T_{\bf c}$, which fits better to two superconducting gaps rather than a single gap. Further a nonlinear magnetic field dependence of the electronic specific heat coefficient $\gamma$(H) has been found in the low temperature limit, which indicates that the smaller energy gap is nodal. Our analysis of the TF-$\mu$SR results shows that the temperature dependence of the superfluid density is better described by a two-gap model either isotropic $s$+$s$-wave or $s$+$d$-wave than a single gap isotropic $s$-wave model for the superconducting gap, consistent with other Fe-based superconductors. The combine $\gamma$(H) and TF-$\mu$SR results confirm $s$+$d$-wave model for the gap structure of ThFeAsN. The observation of two gaps in ThFeAsN suggests multiband nature of the superconductivity possibly arising from the d-bands of Fe ions. Furthermore, from our TF-$\mu$SR study we have estimated the magnetic penetration depth, in the polycrystalline sample, of $\lambda_{\mathrm{L}}$$(0)$ = 375 nm, superconducting carrier density $n_s = 4.6 \times 10^{27}~ $m$^{-3}$, and carrier's effective-mass $m^*$ = 2.205\textit{m}$_{e}$. We will compare the results of our present study with those reported for the Fe-pnictide family of superconductors.
  • We report neutron diffraction and transport results on the newly discovered superconducting nitride ThFeAsN with $T_c=$ 30 K. No magnetic transition, but a weak structural distortion around 160 K, is observed cooling from 300 K to 6 K. Analysis on the resistivity, Hall transport and crystal structure suggests this material behaves as an electron optimally doped pnictide superconductors due to extra electrons from nitrogen deficiency or oxygen occupancy at the nitrogen site, which together with the low arsenic height may enhance the electron itinerancy and reduce the electron correlations, thus suppress the static magnetic order.
  • We report the first nitrogen-containing iron-pnictide superconductor ThFeAsN, which is synthesized by a solid-state reaction in an evacuated container. The compound crystallizes in a ZrCuSiAs-type structure with the space group P4/nmm and lattice parameters a=4.0367(1) {\AA} and c=8.5262(2) {\AA} at 300 K. The electrical resistivity and dc magnetic susceptibility measurements indicate superconductivity at 30 K for the nominally undoped ThFeAsN.
  • We performed $^{31}$P-NMR measurements on LaFe(As$_{1-x}$P$_{x}$)O to investigate the relationship between antiferromagnetism and superconductivity. The antiferromagnetic (AFM) ordering temperature $T_{\rm N}$ and the moment $\mu_{\rm ord}$ are continuously suppressed with increasing P content $x$ and disappear at $x = 0.3$ where bulk superconductivity appears. At this superconducting $x = 0.3$, quantum critical AFM fluctuations are observed, indicative of the intimate relationship between superconductivity and low-energy AFM fluctuations associated with the quantum-critical point in LaFe(As$_{1-x}$P$_{x}$)O. The relationship is similar to those observed in other isovalent-substitution systems, e.g., BaFe$_{2}$(As$_{1-x}$P$_{x}$)$_{2}$ and SrFe$_{2}$(As$_{1-x}$P$_{x}$)$_{2}$, with the "122" structure. Moreover, the AFM order reappears with further P substitution ($x > 0.4$). The variation of the ground state with respect to the P substitution is considered to be linked to the change in the band character of Fe-3$d$ orbitals around the Fermi level.
  • We have studied a quinary Fe-based superconductor Sr$_2$VFeAsO$_3$ by the measurements of x-ray diffraction, x-ray absorption, M\"{o}ssbauer spectrum, resistivity, magnetization and specific heat. This apparently undoped oxyarsenide is shown to be self doped via electron transfer from the V$^{3+}$ ions. We observed successive magnetic transitions within the VO$_2$ layers: an antiferromagnetic transition at 150 K followed by a weak ferromagnetic transition at 55 K. The spin orderings within the VO$_2$ planes are discussed based on mixed valence of V$^{3+}$ and V$^{4+}$.
  • We report the antimony (Sb) doping effect in a prototype system of iron-based supercon-ductors LaFeAsO1-yFy (y=0, 0.1, 0.15). X-ray powder diffraction indicates that the lattice pa-rameters increase with Sb content within the doping limit. Rietveld structural refinements show that, with the partial substitution of Sb for As, while the thickness of the Fe2As2 layers increases significantly, that of the La2O2 layers shrinks simultaneously. So a negative chemical pressure is indeed "applied" to the superconducting-active Fe2As2 layers, in con-trast to the effect of positive chemical pressure by the phosphorus doping. Electrical resis-tance and magnetic susceptibility measurements indicate that, while the Sb doping hardly influences the SDW anomaly in LaFeAsO, it recovers SDW order for the optimally-doped sample of y=0.1. In the meantime, the superconducting transition temperature can be raised up to 30 K in LaFeAs1-xSbxO1-yFy with x=0.1 and y=0.15. The Sb doping effects are discussed in term of both J1-J2 model and Fermi Surface (FS) nesting scenario.
  • We report the measurements of resistivity and magnetization under magnetic fields parallel and perpendicular to the basal plane, respectively, on a cobalt-doped Eu(Fe$_{0.89}$Co$_{0.11}$)$_{2}$As$_{2}$ single crystal. We observed a resistivity drop at $T_c\sim$ 21 K, which shifts toward lower temperatures under external fields, suggesting a superconducting transition. The upper critical fields near $T_c$ show large anisotropy, in contrast with those of other '122' FeAs-based superconductors. Low-field magnetic susceptibility data also show evidence of superconductivity below 21 K. Instead of expected zero-resistance below $T_c$, however, a resistivity reentrance appears at 17 K under zero field, coincident with the magnetic ordering of Eu$^{2+}$ moments. Based on the temperature and field dependences of anisotropic magnetization, a helical magnetic structure for the Eu$^{2+}$ spins is proposed. External magnetic fields easily changes the helimagnetism into a ferromagnetism with fully polarized Eu$^{2+}$ spins, accompanying by disappearance of the resistivity reentrance. Therefore, superconductivity coexists with ferromagnetic state of Eu$^{2+}$ spins under relatively low magnetic field. The magnetic and superconducting phase diagrams are finally summarized for both $H\parallel ab$ and $H\parallel c$.
  • We report bulk superconductivity induced by an isovalent doping of phosphorus in BaFe$_{2}$(As$_{1-x}$P$_{x}$)$_{2}$. The P-for-As substitution results in shrinkage of lattice, especially for the FeAs block layers. The resistivity anomaly associated with the spin-density-wave (SDW) transition in the undoped compound is gradually suppressed by the P doping. Superconductivity with the maximum $T_c$ of 30 K emerges at $x$=0.32, coinciding with a magnetic quantum critical point (QCP) which is evidenced by the disappearance of SDW order and the linear temperature-dependent resistivity in the normal state. The $T_c$ values were found to decrease with further P doping, and no superconductivity was observed down to 2 K for $x\geq$ 0.77. The appearance of superconductivity in the vicinity of QCP hints to the superconductivity mechanism in iron-based arsenides.
  • We report the realization of superconductivity by an isovalent doping with phosphorus in LaFeAsO. X-ray diffraction shows that, with the partial substitution of P for As, the Fe$_2$As$_2$ layers are squeezed while the La$_2$O$_2$ layers are stretched along the c-axis. Electrical resistance and magnetization measurements show emergence of bulk superconductivity at $\sim$10 K for the optimally-doped LaFeAs$_{1-x}$P$_{x}$O ($x=0.25\sim0.3$). The upper critical fields at zero temperature is estimated to be 27 T, much higher than that of the LaFePO superconductor. The occurrence of superconductivity is discussed in terms of chemical pressures and bond covalency.
  • We have studied Ni-substitution effect in LaFe$_{1-x}$Ni$_{x}$AsO ($0\leq x \leq0.1$) by the measurements of x-ray diffraction, electrical resistivity, magnetic susceptibility, and heat capacity. The nickel doping drastically suppresses the resistivity anomaly associated with spin-density-wave ordering in the parent compound. Superconductivity emerges in a narrow region of $0.03\leq x \leq0.06$ with the maximum $T_c$ of 6.5 K at $x$=0.04, where enhanced magnetic susceptibility shows up. The upper critical field at zero temperature is estimated to exceed the Pauli paramagnetic limit. The much lowered $T_c$ in comparison with LaFeAsO$_{1-x}$F$_{x}$ system is discussed.
  • We report Zn-doping effect in the parent and F-doped LaFeAsO oxy-arsenides. Slight Zn doping in LaFe$_{1-x}$Zn$_{x}$AsO drastically suppresses the resistivity anomaly around 150 K associated with the antiferromagnetic (AFM) spin density wave (SDW) in the parent compound. The measurements of magnetic susceptibility and thermopower confirm further the effect of Zn doping on AFM order. Meanwhile Zn doping does not affect or even enhances the $T_c$ of LaFe$_{1-x}$Zn$_{x}$AsO$_{0.9}$F$_{0.1}$, in contrast to the effect of Zn doping in high-$T_c$ cuprates. We found that the solubility of Zn content ($x$) is limited to less than 0.1 in both systems and further Zn doping (i.e., $x$ $\geq$ 0.1) causes phase separation. Our study clearly indicates that the non-magnetic impurity of Zn$^{2+}$ ions doped in the Fe$_2$As$_2$ layers affects selectively the AFM order, and superconductivity remains robust against the Zn doping in the F-doped superconductors.
  • We present a systematic study on the physical properties of EuFe$_{2-x}$Ni$_{x}$As$_{2}$ (0$\leq$\emph{x}$\leq$0.2) by electrical resistivity, magnetic susceptibility and thermopower measurements. The undoped compound EuFe$_{2}$As$_{2}$ undergoes a spin-density-wave (SDW) transition associated with Fe moments at 195 K, followed by antiferromagnetic (AFM) ordering of Eu$^{2+}$ moments at 20 K. Ni doping at the Fe site simultaneously suppresses the SDW transition and AFM ordering of Eu$^{2+}$ moments. For $x\geq$0.06, the magnetic ordering of Eu$^{2+}$ moments evolves from antiferromagnetic to ferromagnetic (FM). The SDW transition is completely suppressed for $x\geq$0.16, however, no superconducting transition was observed down to 2 K. The possible origins of the AFM-to-FM transition and the absence of superconductivity in EuFe$_{2-x}$Ni$_{x}$As$_{2}$ system are discussed.
  • We have studied EuFe$_{2}$(As$_{0.7}$P$_{0.3}$)$_{2}$ by the measurements of x-ray diffraction, electrical resistivity, thermopower, magnetic susceptibility, magnetoresistance and specific heat. Partial substitution of As with P results in the shrinkage of lattice, which generates chemical pressure to the system. It is found that EuFe$_{2}$(As$_{0.7}$P$_{0.3}$)$_{2}$ undergoes a superconducting transition at 26 K, followed by ferromagnetic ordering of Eu$^{2+}$ moments at 20 K. This finding is the first observation of superconductivity stabilized by internal chemical pressure, and supplies a rare example showing coexistence of superconductivity and ferromagnetism in the ferro-arsenide family.
  • We report the measurements of anisotropic magnetization and magnetoresistance on single crystals of EuFe$_2$As$_2$, a parent compound of ferro-arsenide high-temperature superconductor. Apart from the antiferromagnetic (AFM) spin-density-wave transition at 186 K associated with Fe moments, the compound undergoes another magnetic phase transition at 19 K due to AFM ordering of Eu$^{2+}$ spins ($J=S=7/2$). The latter AFM state exhibits metamagnetic transition under magnetic fields. Upon applying magnetic field with $H\parallel c$ at 2 K, the magnetization increases linearly to 7.0 $\mu_{B}$/f.u. at $\mu_{0}H$=1.7 T, then keeps at this value of saturated Eu$^{2+}$ moments under higher fields. In the case of $H\parallel ab$, the magnetization increases step-like to 6.6 $\mu_{B}$/f.u. with small magnetic hysteresis. A metamagnetic phase was identified with the saturated moments of 4.4 $\mu_{B}$/f.u. The metamagnetic transition accompanies with negative in-plane magnetoresistance, reflecting the influence of Eu$^{2+}$ moments ordering on the electrical conduction of FeAs layers. The results were explained in terms of spin-reorientation and spin-reversal based on an $A$-type AFM structure for Eu$^{2+}$ spins. The magnetic phase diagram has been established.
  • Ternary iron arsenide EuFe$_2$As$_2$ with ThCr$_2$Si$_2$-type structure has been studied by magnetic susceptibility, resistivity, thermopower, Hall and specific heat measurements. The compound undergoes two magnetic phase transitions at about 200 K and 20 K, respectively. The former was found to be accompanied with a slight drop in magnetic susceptibility (after subtracting the Curie-Weiss paramagnetic contribution), a rapid decrease in resistivity, a large jump in thermopower and a sharp peak in specific heat with decreasing temperature, all of which point to a spin-density-wave-like antiferromagnetic transition. The latter was proposed to be associated with an A-type antiferromagnetic ordering of Eu$^{2+}$ moments. Comparing with the physical properties of the iso-structural compounds BaFe$_2$As$_2$ and SrFe$_2$As$_2$, we expect that superconductivity could be induced in EuFe$_2$As$_2$ through appropriate doping.
  • Chemical doping has recently become a very important strategy to induce superconductivity especially in complex compounds. Distinguished examples include Ba-doped La$_2$CuO$_4$ (the first high temperature superconductor), K-doped BaBiO$_3$, K-doped C$_{60}$ and Na$_{x}$CoO$_{2}\cdot y$H$_{2}$O. The most recent example is F-doped LaFeAsO, which leads to a new class of high temperature superconductors. One notes that all the above dopants are non-magnetic, because magnetic atoms generally break superconducting Cooper pairs. In addition, the doping site was out of the (super)conducting structural unit (layer or framework). Here we report that superconductivity was realized by doping magnetic element cobalt into the (super)conducting-active Fe$_2$As$_2$ layers in LaFe$_{1-x}$Co$_{x}$AsO. At surprisingly small Co-doping level of $x$=0.025, the antiferromagnetic spin-density-wave transition in the parent compound is completely suppressed, and superconductivity with $T_c\sim $ 10 K emerges. With increasing Co content, $T_c$ shows a maximum of 13 K at $x\sim 0.075$, and then drops to below 2 K at $x$=0.15. This result suggests essential differences between previous cuprate superconductor and the present iron-based arsenide one.
  • Following the discovery of superconductivity in an iron-based arsenide LaO1-xFxFeAs with a superconducting transition temperature (Tc) of 26 K[1], Tc was pushed up surprisingly to above 40 K by either applying pressure[2] or replacing La with Sm[3], Ce[4], Nd[5] and Pr[6]. The maximum Tc has climbed to 55 K, observed in SmO1-xFxFeAs[7, 8] and SmFeAsO1-x[9]. The value of Tc was found to increase with decreasing lattice parameters in LnFeAsO1-xFx (Ln stands for the lanthanide elements) at an apparently optimal doping level. However, the F- doping in GdFeAsO is particularly difficult[10,11] due to the lattice mismatch between the Gd2O2 layers and Fe2As2 layers. Here we report observation of superconductivity with Tc as high as 56 K by the Th4+ substitution for Gd3+ in GdFeAsO. The incorporation of relatively large Th4+ ions relaxes the lattice mismatch, hence induces the high temperature superconductivity.