• Self-supported electrocatalysts being generated and employed directly as electrode for energy conversion has been intensively pursued in the fields of materials chemistry and energy. Herein, we report a synthetic strategy to prepare freestanding hierarchically structured, nitrogen-doped nanoporous graphitic carbon membranes functionalized with Janus-type Co/CoP nanocrystals (termed as HNDCM-Co/CoP), which were successfully applied as a highly-efficient, binder-free electrode in hydrogen evolution reaction (HER). Benefited from multiple structural merits, such as high degree of graphitization, three-dimensionally interconnected micro-/meso-/macropores, uniform nitrogen-doping, well-dispersed Co/CoP nanocrystals as well as the confinement effect of the thin carbon layer on the nanocrystals, HNDCM-Co/CoP exhibited superior electrocatalytic activity and long-term operation stability for HER under both acid and alkaline conditions. As a proof-of-concept of practical usage, a macroscopic piece of HNDCM-Co/CoP of 5.6 cm x 4 cm x 60 um in size was prepared in our laboratory. Driven by a solar cell, electroreduction of water in alkaline condition (pH 14) was performed, and H2 has been produced at a rate of 16 ml/min, demonstrating its potential as real-life energy conversion systems.
  • Nanoporous graphitic carbon membranes with defined chemical composition and pore architecture are novel nanomaterials that are actively pursued. Compared to easy-to-make porous carbon powders that dominate the porous carbon research and applications in energy generation/conversion and environmental remediation, porous carbon membranes are synthetically more challenging though rather appealing from an application perspective due to their structural integrity, interconnectivity and purity. Here we report a simple bottom-up approach to fabricate large-size, freestanding, porous carbon membranes that feature an unusual single-crystal-like graphitic order and hierarchical pore architecture plus favorable nitrogen doping. When loaded with cobalt nanoparticles, such carbon membranes serve as high-performance carbon-based non-noble metal electrocatalyst for overall water splitting.
  • Organolead trihalide perovskites have drawn substantial interest for applications in photovoltaic and optoelectronic devices due to their low processing cost and remarkable physical properties. However, perovskite thin films still suffer from low carrier mobility, limiting their device performance and application potential. Here we report that embedding single-walled carbon nanotubes into halide perovskite films can significantly enhance the hole and electron mobilities to record-high values of 595.3 and 108.7 cm2 V-1 s-1, respectively. In the ambipolar phototransistors with such hybrid channels, photo-carriers generated in the light-absorbing perovskite matrix are transported by the carbon nanotubes, leading to ultrahigh detectivity of 6 * 1014 Jones and responsivity of 1 * 104 A W-1. We find that the perovskite precursor in dimethylformamide solution serve as an excellent stabilizer for the dispersion of carbon nanotubes, which potentially extend the scope of applications of perovskites in solution-processed functional composites. The unprecedented high performances underscore the perovskite/carbon nanotubes hybrids as an emerging class of functional materials in optoelectronic and other applications.
  • Organolead halide perovskites have attracted substantial attention due to their excellent physical properties, which enable them to serve as the active material in emerging hybrid solid-state solar cells. Here we investigate the phototransistors based on hybrid perovskite films, and provide direct evidence for their superior carrier transport property with ambipolar characteristics. The field-effect mobilities for triiodide perovskites at room temperature are measured as 0.18 (0.17) cm2 V-1 s-1 for holes (electrons), which increase to 1.24 (1.01) cm2 V-1 s-1 for mixed halide perovskites. The photoresponsivity of our hybrid perovskite devices reaches 320 A W-1, which is among the largest values reported for phototransistors. Importantly, the phototransistors exhibit an ultrafast photoresponse speed of less than 10 {\mu}s. The solution-based process and excellent device performance strongly underscore hybrid perovskites as promising material candidates for photoelectronic applications.