• A large and high-quality single crystal (Li0.84Fe0.16)OHFe0.98Se, the optimal superconductor of newly reported (Li1-xFex)OHFe1-ySe system, has been successfully synthesized via a hydrothermal ion-exchange technique. The superconducting transition temperature (Tc) of 42 K is determined by magnetic susceptibility and electric resistivity measurements, and the zero-temperature upper critical magnetic fields are evaluated as 79 and 313 Tesla for the field along the c-axis and the ab-plane, respectively. The ratio of out-of-plane to in-plane electric resistivity,\r{ho}c/\r{ho}ab, is found to increases with decreasing temperature and to reach a high value of 2500 at 50 K, with an evident kink occurring at a characteristic temperature T*=120 K. The negative in-plane Hall coefficient indicates that electron carriers dominate in the charge transport, and the hole contribution is significantly reduced as the temperature is lowered to approach T*. From T* down to Tc, we observe the linear temperature dependences of the in-plane electric resistivity and the magnetic susceptibility for the FeSe layers. Our findings thus reveal that the normal state of (Li0.84Fe0.16)OHFe0.98Se becomes highly two-dimensional and anomalous prior to the superconducting transition, providing a new insight into the mechanism of high-Tc superconductivity.
  • The mechanism of high temperature superconductivity in the iron-based superconductors remains an outstanding issue in condensed matter physics. The electronic structure, in particular the Fermi surface topology, is considered to play an essential role in dictating the superconductivity. Recent revelation of distinct electronic structure and possible high temperature superconductivity with a transition temperature Tc above 65 K in the single-layer FeSe films grown on the SrTiO3 substrate provides key information on the roles of Fermi surface topology and interface in inducing or enhancing superconductivity. Here we report high resolution angle-resolved photoemission measurement on the electronic structure and superconducting gap of a novel FeSe-based superconductor, (Li0.84Fe0.16)OHFe0.98Se, with a Tc at 41 K. We find that this single-phase bulk superconductor shows remarkably similar electronic behaviors to that of the superconducting single-layer FeSe/SrTiO3 film in terms of Fermi surface topology, band structure and nearly isotropic superconducting gap without nodes. These observations provide significant insights in understanding high temperature superconductivity in the single-layer FeSe/SrTiO3 film in particular, and the mechanism of superconductivity in the iron-based superconductors in general.
  • Previous experimental results have shown important differences between iron selenide and arsenide superconductors, which seem to suggest that the high temperature superconductivity in these two subgroups of iron-based family may arise from different electronic ground states. Here, we report the complete phase diagram of a newly synthesized superconducting (SC) system (Li1-xFex)OHFeSe with a similar structure to FeAs-based superconductors. In the non-SC samples, an antiferromagnetic (AFM) spin-density-wave (SDW) transition occurs at ~127 K. This is the first example to demonstrate such an SDW phase in FeSe-based superconductor system. Transmission electron microscopy (TEM) shows that a well-known sqrr(5) x sqrr(5) iron vacancy ordered state, resulting in an AFM order at ~ 500K in AyFe2-xSe2 (A = metal ions) superconductor system, is absent in both non-SC and SC samples, but a unique superstructure with a modulation wave vector q=1/2(1, 1, 0), identical to that seen in SC phase of KyFe2-xSe2, is dominant in the optimal SC sample (with an SC transition temperature Tc = 40 K). Hence, we conclude that the high-Tc superconductivity in (Li1-xFex)OHFeSe stems from the similarly weak AFM fluctuations as FeAs-based superconductors, suggesting a universal physical picture for both iron selenide and arsenide superconductors.
  • A flux-free solution to the growth of large and composition homogeneous superconducting FeSe crystal is reported for the first time, which is based on the traveling-solvent floating-zone technique. The size of the crystal samples prepared by this approach is up to 15x6x2 mm3, being far bigger than previously reported in all dimensions, and the main phase of the crystals is of a single preferred orientation along the tetragonal (101) plane. X-ray diffraction analysis identifies the main phase to be the superconducting tetragonal \b{eta}-FeSe. The superconducting transition temperature (TC) is determined to be 9.4 K by AC magnetic susceptibility and electronic transport measurements. A nearly perfect diamagnetic shielding of -97% is observed, indicating a bulk superconductivity in the crystal sample.