• The phenomenon of phase separation into antiferromagnetic (AFM) and superconducting (SC) or normal-state regions has great implication for the origin of high-temperature (high-Tc) superconductivity. However, the occurrence of an intrinsic antiferromagnetism above the Tc of (Li, Fe)OHFeSe superconductor is questioned. Here we report a systematic study on a series of (Li, Fe)OHFeSe single crystal samples with Tc up to ~41 K. We observe an evident drop in the static magnetization at Tafm ~125 K, in some of the SC (Tc < ~38 K, cell parameter c < ~9.27 {\AA}) and non-SC samples. We verify that this AFM signal is intrinsic to (Li, Fe)OHFeSe. Thus, our observations indicate mesoscopic-to-macroscopic coexistence of an AFM state with the normal (below Tafm) or SC (below Tc) state in (Li, Fe)OHFeSe. We explain such coexistence by electronic phase separation, similar to that in high-Tc cuprates and iron arsenides. However, such an AFM signal can be absent in some other samples of (Li, Fe)OHFeSe, particularly it is never observed in the SC samples of Tc > ~38 K, owing to a spatial scale of the phase separation too small for the macroscopic magnetic probe. For this case, we propose a microscopic electronic phase separation. It is suggested that the microscopic static phase separation reaches vanishing point in high-Tc (Li, Fe)OHFeSe, by the occurrence of two-dimensional AFM spin fluctuations below nearly the same temperature as Tafm reported previously for a (Li, Fe)OHFeSe (Tc ~42 K) single crystal. A complete phase diagram is thus established. Our study provides key information of the underlying physics for high-Tc superconductivity.
  • The superconducting film of (Li1-xFex)OHFeSe is reported for the first time. The thin film exhibits a small in-plane crystal mosaic of 0.22 deg, in terms of the FWHM (full-width-at-half-maximum) of x-ray rocking curve, and an excellent out-of-plane orientation by x-ray phi-scan. Its bulk superconducting transition temperature (Tc) of 42.4 K is characterized by both zero electrical resistance and diamagnetization measurements. The upper critical field (Hc2) is estimated to be 79.5 T and 443 T, respectively, for the magnetic field perpendicular and parallel to the ab plane. Moreover, a large critical current density (Jc) of a value over 0.5 MA/cm2 is achieved at ~20 K. Such a (Li1-xFex)OHFeSe film is therefore not only important to the fundamental research for understanding the high-Tc mechanism, but also promising in the field of high-Tc superconductivity application, especially in high-performance electronic devices and large scientific facilities such as superconducting accelerator.
  • We report the success in introducing Mn into (Li1-xFex)OHFe1-ySe superconducting crystals by applying two different hydrothermal routes, ion exchange (1-Step) and ion release/introduction (2-Step). The micro-region x-ray diffraction and energy dispersive x-ray spectroscopy analyses indicate that the Mn has been doped into the lattice, and its content in the 1-Step fabricated sample is higher than that in the 2-Step one. Magnetic susceptibility and electric transport properties reveal that Mn doping influences little on the superconducting transition, regardless of 1-Step or 2-Step routes. By contrast, the characteristic temperature, T*, where the negative Hall coefficient reaches its minimum, is significantly reduced by Mn doping. This implies that the reduction of the hole carriers contribution is obviously modified, and hence the hole band might have no direct relationship with the superconductivity in (Li1-xFex)OHFe1-ySe superconductors. Our present hydrothermal methods of ion exchange and ion release/introduction provide an efficient way for elements substitution/doping into (Li1-xFex)OHFe1-ySe superconductors, which will promote the in-depth investigations on the role of multiple electron and hole bands and their interplay with the high-temperature superconductivity in the FeSe-based superconductors.
  • The role played by the insulating intermediate (Li$_{0.84}$Fe$_{0.16}$)OH layer on magnetic and superconducting properties of (Li$_{0.84}$Fe$_{0.16}$)OHFe$_{0.98}$Se was studied by means of muon-spin rotation. It was found that it is not only enhances the coupling between the FeSe layers for temperatures below $\simeq 10$ K, but becomes superconducting by itself due to the proximity to the FeSe ones. Superconductivity in (Li$_{0.84}$Fe$_{0.16}$)OH layers is most probably filamentary-like and the energy gap value, depending on the order parameter symmetry, does not exceed 1-1.5 meV.
  • A large and high-quality single crystal (Li0.84Fe0.16)OHFe0.98Se, the optimal superconductor of newly reported (Li1-xFex)OHFe1-ySe system, has been successfully synthesized via a hydrothermal ion-exchange technique. The superconducting transition temperature (Tc) of 42 K is determined by magnetic susceptibility and electric resistivity measurements, and the zero-temperature upper critical magnetic fields are evaluated as 79 and 313 Tesla for the field along the c-axis and the ab-plane, respectively. The ratio of out-of-plane to in-plane electric resistivity,\r{ho}c/\r{ho}ab, is found to increases with decreasing temperature and to reach a high value of 2500 at 50 K, with an evident kink occurring at a characteristic temperature T*=120 K. The negative in-plane Hall coefficient indicates that electron carriers dominate in the charge transport, and the hole contribution is significantly reduced as the temperature is lowered to approach T*. From T* down to Tc, we observe the linear temperature dependences of the in-plane electric resistivity and the magnetic susceptibility for the FeSe layers. Our findings thus reveal that the normal state of (Li0.84Fe0.16)OHFe0.98Se becomes highly two-dimensional and anomalous prior to the superconducting transition, providing a new insight into the mechanism of high-Tc superconductivity.
  • The mechanism of high temperature superconductivity in the iron-based superconductors remains an outstanding issue in condensed matter physics. The electronic structure, in particular the Fermi surface topology, is considered to play an essential role in dictating the superconductivity. Recent revelation of distinct electronic structure and possible high temperature superconductivity with a transition temperature Tc above 65 K in the single-layer FeSe films grown on the SrTiO3 substrate provides key information on the roles of Fermi surface topology and interface in inducing or enhancing superconductivity. Here we report high resolution angle-resolved photoemission measurement on the electronic structure and superconducting gap of a novel FeSe-based superconductor, (Li0.84Fe0.16)OHFe0.98Se, with a Tc at 41 K. We find that this single-phase bulk superconductor shows remarkably similar electronic behaviors to that of the superconducting single-layer FeSe/SrTiO3 film in terms of Fermi surface topology, band structure and nearly isotropic superconducting gap without nodes. These observations provide significant insights in understanding high temperature superconductivity in the single-layer FeSe/SrTiO3 film in particular, and the mechanism of superconductivity in the iron-based superconductors in general.
  • Previous experimental results have shown important differences between iron selenide and arsenide superconductors, which seem to suggest that the high temperature superconductivity in these two subgroups of iron-based family may arise from different electronic ground states. Here, we report the complete phase diagram of a newly synthesized superconducting (SC) system (Li1-xFex)OHFeSe with a similar structure to FeAs-based superconductors. In the non-SC samples, an antiferromagnetic (AFM) spin-density-wave (SDW) transition occurs at ~127 K. This is the first example to demonstrate such an SDW phase in FeSe-based superconductor system. Transmission electron microscopy (TEM) shows that a well-known sqrr(5) x sqrr(5) iron vacancy ordered state, resulting in an AFM order at ~ 500K in AyFe2-xSe2 (A = metal ions) superconductor system, is absent in both non-SC and SC samples, but a unique superstructure with a modulation wave vector q=1/2(1, 1, 0), identical to that seen in SC phase of KyFe2-xSe2, is dominant in the optimal SC sample (with an SC transition temperature Tc = 40 K). Hence, we conclude that the high-Tc superconductivity in (Li1-xFex)OHFeSe stems from the similarly weak AFM fluctuations as FeAs-based superconductors, suggesting a universal physical picture for both iron selenide and arsenide superconductors.
  • A flux-free solution to the growth of large and composition homogeneous superconducting FeSe crystal is reported for the first time, which is based on the traveling-solvent floating-zone technique. The size of the crystal samples prepared by this approach is up to 15x6x2 mm3, being far bigger than previously reported in all dimensions, and the main phase of the crystals is of a single preferred orientation along the tetragonal (101) plane. X-ray diffraction analysis identifies the main phase to be the superconducting tetragonal \b{eta}-FeSe. The superconducting transition temperature (TC) is determined to be 9.4 K by AC magnetic susceptibility and electronic transport measurements. A nearly perfect diamagnetic shielding of -97% is observed, indicating a bulk superconductivity in the crystal sample.