• We report the low-temperature properties of phase-pure single crystals of the half-Heusler compound CuMnSb grown by means of optical float-zoning. The magnetization, specific heat, electrical resistivity, and Hall effect of our single crystals exhibit an antiferromagnetic transition at $T_{\mathrm{N}} = 55~\mathrm{K}$ and a second anomaly at a temperature $T^{*} \approx 34~\mathrm{K}$. Powder and single-crystal neutron diffraction establish an ordered magnetic moment of $(3.9\pm0.1)~\mu_{\mathrm{B}}/\mathrm{f.u.}$, consistent with the effective moment inferred from the Curie-Weiss dependence of the susceptibility. Below $T_{\mathrm{N}}$, the Mn sublattice displays commensurate type-II antiferromagnetic order with propagation vectors and magnetic moments along $\langle111\rangle$ (magnetic space group $R[I]3c$). Surprisingly, below $T^{*}$, the moments tilt away from $\langle111\rangle$ by a finite angle $\delta \approx 11^{\circ}$, forming a canted antiferromagnetic structure without uniform magnetization consistent with magnetic space group $C[B]c$. Our results establish that type-II antiferromagnetism is not the zero-temperature magnetic ground state of CuMnSb as may be expected of the face-centered cubic Mn sublattice.
  • Centimeter-sized single crystals of Sr$_{1.5}$La$_{0.5}$RhO$_{4}$ were grown by the floating zone method at oxygen pressures of 20~bar. The quality of our single crystals was confirmed by X-ray Laue, powder and single crystal X-ray diffraction, neutron and X-ray absorbtion spectroscopy measurements. At $\sim$50% electron doping we observe RhO$_3$ octahedral rotations of $\sim$8.2$^{\circ}$ within the octahedral basal plane which are incompatible with space group I4/mmm. Our single crystal was further characterized by susceptibility, electrical transport and, finally, specific heat measurements showing a temperature dependent Debye temperature.
  • The tetragonal copper oxide Bi$_2$CuO$_4$ has an unusual crystal structure with a three-dimensional network of well separated CuO$_4$ plaquettes. This material was recently predicted to host electronic excitations with an unconventional spectrum and the spin structure of its magnetically ordered state appearing at T$_N$ $\sim$43 K remains controversial. Here we present the results of detailed studies of specific heat, magnetic and dielectric properties of Bi$_2$CuO$_4$ single crystals grown by the floating zone technique, combined with the polarized neutron scattering and high-resolution X-ray measurements. Our polarized neutron scattering data show Cu spins are parallel to the $ab$ plane. Below the onset of the long range antiferromagnetic ordering we observe an electric polarization induced by an applied magnetic field, which indicates inversion symmetry breaking by the ordered state of Cu spins. For the magnetic field applied perpendicular to the tetragonal axis, the spin-induced ferroelectricity is explained in terms of the linear magnetoelectric effect that occurs in a metastable magnetic state. A relatively small electric polarization induced by the field parallel to the tetragonal axis may indicate a more complex magnetic ordering in Bi$_2$CuO$_4$.
  • We report about the magnetic properties of antiferromagnetic (AF) MnO nanoparticles (NPs) with different sizes (6-19nm). Using a combination of polarized neutron scattering and magnetometry we were able to resolve previously observed peculiarities. Magnetometry, on the one hand, reveals a peak in the zero field cooled (ZFC) magnetization curves at low temperatures (~25K) but no feature around the N\'eel temperature at 118K. On the other hand, polarized neutron scattering shows the expected behavior of the AF order parameter vanishing around 118K. Moreover, hysteresis curves measured at various temperatures reveal an exchange bias effect indicating a coupling of an AF core to a ferromagnetic (FM)-like shell. ZFC data measured at various fields exclude a purely superparamagnetic (SPM) scenario. We conclude that the magnetic behavior of MnO particles can be explained by a superposition of SPM-like thermal fluctuations of the AF-N\'eel vector inside the AF core and a strong magnetic coupling to a ferrimagnetic Mn$_2$O$_3$ or Mn$_3$O$_4$ shell. In addition, we have studied heterodimer ('Janus') particles, where a FM FePt particle is attached to the AF MnO particle. Via the exchange bias effect, the magnetic moment of the FePt subunit is stabilized by the MnO.
  • Zero field cooled (ZFC)/Field Cooled (FC) magnetization curves of a bulk MnO single crystal show a peculiar peak at low temperatures (~40K) similar to the low temperature peak observed in MnO nanoparticles. In order to investigate the origin of this peak, the spin structure of a MnO single crystal has been studied and compared with a single phase powder sample using magnetometry and polarized neutron scattering. Both magnetometry and polarized neutron diffraction results confirm the antiferromagnetic (AF) phase transition at the N\'eel temperature T_N of 118K, in both powder and single crystal form. However, the low temperature peak in the ZFC/FC magnetization curves is not observed in single phase MnO powder. To better understand the observed behavior, ac susceptibility measurements have been employed. We conclude that the clear peak in the magnetic signal from the single crystal originates from a small amount of ferrimagnetic (FiM) Mn2O3 or Mn3O4 impurities, which is grown at the interfaces between MnO crystal twins.
  • The magnetic ground state of the Eu$^{2+}$ moments in a series of Eu(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$ single crystals grown from the Sn flux has been investigated in detail by neutron diffraction measurements. Combined with the results from the macroscopic properties (resistivity, magnetic susceptibility and specific heat) measurements, a phase diagram describing how the Eu magnetic order evolves with Co doping in Eu(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$ is established. The ground-state magnetic structure of the Eu$^{2+}$ spins is found to develop from the A-type antiferromagnetic (AFM) order in the parent compound, via the A-type canted AFM structure with some net ferromagnetic (FM) moment component along the crystallographic $\mathit{c}$ direction at intermediate Co doping levels, finally to the pure FM order at relatively high Co doping levels. The ordering temperature of Eu declines linearly at first, reaches the minimum value of 16.5(2) K around $\mathit{x}$ = 0.100(4), and then reverses upwards with further Co doping. The doping-induced modification of the indirect Ruderman-Kittel-Kasuya-Yosida (RKKY) interaction between the Eu$^{2+}$ moments, which is mediated by the conduction $\mathit{d}$ electrons on the (Fe,Co)As layers, as well as the change of the strength of the direct interaction between the Eu$^{2+}$ and Fe$^{2+}$ moments, might be responsible for the change of the magnetic ground state and the ordering temperature of the Eu sublattice. In addition, for Eu(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$ single crystals with 0.10 $\leqslant$ $\mathit{x}$ $\leqslant$ 0.18, strong ferromagnetism from the Eu sublattice is well developed in the superconducting state, where a spontaneous vortex state is expected to account for the compromise between the two competing phenomena.
  • CaFe$_{2}$O$_{4}$ is a $S={5\over 2}$ anisotropic antiferromagnet based upon zig-zag chains having two competing magnetic structures, denoted as the A ($\uparrow \uparrow \downarrow \downarrow$) and B ($\uparrow \downarrow \uparrow \downarrow$) phases, which differ by the $c$-axis stacking of ferromagnetic stripes. We apply neutron scattering to demonstrate that the competing A and B phase order parameters results in magnetic antiphase boundaries along $c$ which freeze on the timescale of $\sim$ 1 ns at the onset of magnetic order at 200 K. Using high resolution neutron spectroscopy, we find quantized spin wave levels and measure 9 such excitations localized in regions $\sim$ 1-2 $c$-axis lattice constants in size. We discuss these in the context of solitary magnons predicted to exist in anisotropic systems. The magnetic anisotropy affords both competing A+B orders as well as localization of spin excitations in a classical magnet.