• We have performed an extensive study of single-crystals of the magneto-electric NdFe$_3$($^{11}$BO$_3$)$_4$ by means of a combination of single-crystal neutron diffraction and spherical neutron polarimetry. Our investigation did not detect significant deviations at low temperatures from space group R32 concerning the chemical structure. With respect to magnetic ordering our combined results demonstrate that in the commensurate magnetic phase below T$_N$~30 K all three magnetic Fe moments and the magnetic Nd moment are aligned ferromagnetically in the basal hexagonal plane but align antiferromagnetically between adjacent planes. The phase transition to the low-temperature incommensurate magnetic structure observed at T$_{IC}$~13.5 K appears to be continuous. By means of polarized neutron studies it could be shown that in the incommensurate magnetic phase the magnetic structure of NdFe$_3$($^{11}$BO$_3$)$_4$ is transformed into a long-period antiferromagnetic helix with single chirality. Close to the commensurate-incommensurate phase transition third-order harmonics were observed which in addition indicate the formation of magnetic solitons.
  • By means of magnetic susceptibility and specific heat measurements, x-ray and unpolarised neutron diffraction investigations on powder and single-crystal samples, simultaneous long-range antiferromagnetic Fe and Nd ordering in NdFe3(11BO3)4 with R 3 2 chemical structure has been found at temperatures below TN = 30.5(5) K down to 1.6 K. At temperatures down to 20 K to the propagation vector is khex = [0,0,3/2] and becomes slightly incommensurate at lower temperatures. Symmetry analysis yields magnetic spiral configurations with the magnetic moments oriented parallel to hexagonal basal plane according to the irreducible representations tau_3 in the commensurate case. This is in agreement with the easy directions of magnetisation perpendicular to the c-axis as determined by magnetic susceptibility measurements. At 1.6 K the magnetic Fe moment amounts to 4.9 muB close to the free ion moment of Fe3+. The magnetic Nd3+ moment saturates presumably due to crystal-field effects at 2.7 muB.
  • The magnetic ground-state of copper metaborate is investigated by means of elastic neutron scattering.The magnetic structure of CuB2O4 is incommensurate with respect to the chemical lattice at T=1.8K and undergoes a continuous phase transition to a non-collinear commensurate antiferromagnetic state which is realized at T=10K. Close to the phase transition higher-order magnetic satellites are observed. Coexistence of long-range and short range magnetic order observed in both magnetic phases. This suggests that the association of the Dzyialoshinskii-Moriya interaction, lattice symmetry and tetragonal anisotropy leads to the formation of a three-dimensional magnetic soliton lattice.