• Previous experimental results have shown important differences between iron selenide and arsenide superconductors, which seem to suggest that the high temperature superconductivity in these two subgroups of iron-based family may arise from different electronic ground states. Here, we report the complete phase diagram of a newly synthesized superconducting (SC) system (Li1-xFex)OHFeSe with a similar structure to FeAs-based superconductors. In the non-SC samples, an antiferromagnetic (AFM) spin-density-wave (SDW) transition occurs at ~127 K. This is the first example to demonstrate such an SDW phase in FeSe-based superconductor system. Transmission electron microscopy (TEM) shows that a well-known sqrr(5) x sqrr(5) iron vacancy ordered state, resulting in an AFM order at ~ 500K in AyFe2-xSe2 (A = metal ions) superconductor system, is absent in both non-SC and SC samples, but a unique superstructure with a modulation wave vector q=1/2(1, 1, 0), identical to that seen in SC phase of KyFe2-xSe2, is dominant in the optimal SC sample (with an SC transition temperature Tc = 40 K). Hence, we conclude that the high-Tc superconductivity in (Li1-xFex)OHFeSe stems from the similarly weak AFM fluctuations as FeAs-based superconductors, suggesting a universal physical picture for both iron selenide and arsenide superconductors.