• In this work we explore the overall structural behaviour of the [(CH3)2NH2][Mn(HCOO)3] multiferroic compound across the temperature range where its ferroelectric transition takes place by means of calorimetry, thermal expansion measurements and variable temperature powder and single crystal X-ray diffraction. The results clearly proof the presence of structural phase transition at Tt ~187 K (temperature at which the dielectric transition occurs) that involves a symmetry change from R-3c to Cc, twinning of the crystals, a discontinuous variation of the unit cell parameters and unit cell volume, and a sharp first-order-like anomaly in the thermal expansion. In addition, the calorimetric results show a 3-fold order-disorder transition. The calculated pressure dependence of the transition temperature is rather large (dTt/dP = 4.6 $\pm$ 0.1 K/kbar), so that it should be feasible to shift it to room temperature using adequate thermodynamic conditions, for instance by application of external pressure.
  • We present a new member of the multiferroic oxides, Lu$_2$MnCoO$_6$, which we have investigated using X-ray diffraction, neutron diffraction, specific heat, magnetization, electric polarization, and dielectric constant measurements. This material possesses an electric polarization strongly coupled to a net magnetization below 35 K, despite the antiferromagnetic ordering of the $S = 3/2$ Mn$^{4+}$ and Co$^{2+}$ spins in an $\uparrow \uparrow \downarrow \downarrow$ configuration along the c-direction. We discuss the magnetic order in terms of a condensation of domain boundaries between $\uparrow \uparrow$ and $\downarrow \downarrow$ ferromagnetic domains, with each domain boundary producing a net electric polarization due to spatial inversion symmetry breaking. In an applied magnetic field the domain boundaries slide, controlling the size of the net magnetization, electric polarization, and magnetoelectric coupling.
  • We are reporting the dielectric response of La1.5Sr0.5NiO4, a system that presents a charge-ordered state above room temperature and a rearrangement of its charge-order pattern in the temperature region 160-200 K. A careful analysis of the role of the electric contacts used, sample thickness and grain size on the experimental data allows us to determine that this material exhibits high values of intrinsic dielectric constant. The variation of the dielectric constant with temperature shows a maximum in the region of the rearrangement of the charge-order pattern, which constitutes an evidence of the link between both phenomena.