• The electric transport properties of superconducting FeSe0.3Te0.7/Au c-axis (S/N) junctions, fabricated by using Pulsed Laser Deposition technique, have been investigated in the temperature range of 2 K to the superconducting transition temperature TC ~ 13.5 K, and in the presence of applied magnetic fields from 0 to 9 T. A large zero bias conductance peak has always been observed in the conductance spectra of several batches of junctions. In addition, we have also found several gap-like features. Using the extended BTK theory with the currently favored nodeless S+- wave symmetry, our conductance spectrum can be reproduced quite well in the low bias range with {\Delta}1 = 4 meV, and {\Delta}2 = 6 meV at 2 K. However the experimental conductance spectrum is substantially below the calculated one in the high bias range. Furthermore, there is a conductance minimum at about 20 meV, which may be the reason for the discrepancy.
  • A new multiferroic material, CuBr2, is reported for the first time. CuBr2 has not only a high transition temperature (close to liquid nitrogen temperature) but also low dielectric loss and strong magnetoelectric coupling. These findings reveal the importance of anion effects in the search for the high temperature multiferroics materials among these low-dimensional spin systems.
  • X-ray absorption spectroscopy(XAS) Ru L-edge and O K-edge measurements on single crystals of Sr2YRu1-xCuxO6 (x=0.01-0.05) solid solutions show that Cu replaces Ru in the lattice which results in a lattice distortion and itinerant holes that increase with increasing x. Powder X-ray diffraction (XRD) measurements confirm the lattice distortion through changes in the lattice parameters. Magnetic measurements reveal an antiferromagnetic transition at 32 K in the crystals with x=0 and a diamagnetic transition at 32 K for x \geq 0.01indicative of superconductivity in the zero field cooled (ZFC) curves. The field cooled (FC) curves show a weak ferromagnetic character with x=0 and a ferromagnetic transition at 30 K and an antiferromagnetic transition at 23 K in the presence of Cu. The peak at 30 K in the ac susceptibility measurements indicates a spin-glass behavior. The low field part of the M-H curve for x=0.05 crystal indicates weak superconductivity. The shifting of the M-H curve on FC indicates spin-glass state. In conjunction with the XAS results the magnetic behavior is explained in terms of a spontaneous vortex state as a result of the non-freezing Ru5+ spins.
  • X-ray absorption spectroscopy (XAS) Fe K-edge spectra of the FeSex (x=1-0.8) single crystals cleaved in situ in vacuum reveal characteristic Fe 4sp states, a lattice distortion and the Se K-edge spectra point to a strong Fe 3d-Se 4p hybridization giving rise to itinerant charge carriers. A formal charge of ~1.8+ for Fe and ~2.2- for Se were evaluated from these spectra in the FeSex (x=0.88). The charge balance between Fe and Se is assigned itinerant electrons located in the Fe-Se hybridization bond. As x decreases the 4p hole count increases and a crystal structure distortion is observed that in turn causes the Fe separation in the ab plane change from 4p orbital to varying (modulating) coordination. Powder x-ray diffraction (XRD) measurements also show a slight increase in lattice parameters as x decreases (increasing Se deficiency).
  • Magnetic field dependence of low temperature specific heat of spinel oxide superconductor LiTi_2O_4 has been elaborately investigated. In the normal state, the obtained electronic coefficient of specific heat gamma_n = 19.15 mJ/mol K2, the Debye temperature is 657 K and some other parameters are compared with those reported earlier. The superconducting transition at Tc ~ 11.4 K is very sharp (DeltaTc ~ 0.3 K) and the estimated delataC/gamma_nTc is ~ 1.78. In the superconducting state, the best fit of data leads to the electronic specific heat C_es/Gamma_nTc = 9.87 exp (-1.58 Tc/T) without field and gamma(H) ~ H^0.95 with fields. In addition, Hc2(0) ~ 11.7 T, Hc(0) ~ 0.32 T, xi_GL(0) ~ 5.5 nm, lambda_GL(0) ~ 160 nm, and Hc1(0) ~ 26 mT are estimated from Werthamer-Helfand-Hohenberg (WHH) theory or other relevant relations. All results from the present study indicate that LiTi2O4 can be well described by a typical type-II, BCS-like, moderate coupling, and fully gapped superconductor in the dirty limit. It is further suggested that LiTi2O4 is a moderately electron-electron correlated system.