We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2
(BFAP) single crystals by small-angle neutron scattering (SANS). With the field
along the c-axis, a nearly isotropic hexagonal VL was formed in the field range
from 1 to 16 T, which is a record for this technique in the pnictides, and no
symmetry changes in the VL were observed. The temperature-dependence of the VL
signal was measured and confirms the presence of (non d-wave) nodes in the
superconducting gap structure for measurements at 5 T and below. The nodal
effects were suppressed at high fields. At low fields, a VL reorientation
transition was observed between 1 T and 3 T, with the VL orientation changing
by 45{\deg}. Below 1 T, the VL structure was strongly affected by pinning and
the diffraction pattern had a fourfold symmetry. We suggest that this (and
possibly also the VL reorientation) is due to pinning to defects aligned with
the crystal structure, rather than being intrinsic.
-
We present small angle neutron scattering studies of the vortex lattice (VL)
in CeCoIn5 with magnetic fields applied parallel (H) to the antinodal [100] and
nodal [110] directions. For H || [100], a single VL orientation is observed,
while a 90 degree reorientation transition is found for H || [110]. For both
field orientations and VL configurations we find a distorted hexagonal VL with
an anisotropy, Gamma = 2.0 +/- 0.05. The VL form factor shows strong Pauli
paramagnetic effects similar to what have previously been reported for H ||
[001]. At high fields, above which the upper critical field (Hc2) becomes a
first-order transition, an increased disordering of the VL is observed.
-
Understanding the mechanism and symmetry of electron pairing in iron-based
superconductors represents an important challenge in condensed matter physics
[1-3]. The observation of magnetic flux lines - "vortices" - in a
superconductor can contribute to this issue, because the spatial variation of
magnetic field reflects the pairing. Unlike many other iron pnictides, our
KFe2As2 crystals have very weak vortex pinning, allowing
small-angle-neutron-scattering (SANS) observations of the intrinsic vortex
lattice (VL). We observe nearly isotropic hexagonal packing of vortices,
without VL-symmetry transitions up to high fields along the fourfold c-axis of
the crystals, indicating rather small anisotropy of the superconducting
properties around this axis. This rules out gap nodes parallel to the c-axis,
and thus d-wave and also anisotropic s-wave pairing [2, 3]. The strong
temperature-dependence of the intensity down to T<<Tc indicates either widely
different full gaps on different Fermi surface sheets, or nodal lines
perpendicular to the axis.
-
From small-angle neutron scattering studies of the flux line lattice (FLL) in
CeCoIn5, with magnetic field applied parallel to the crystal c-axis, we obtain
the field- and temperature-dependence of the FLL form factor, which is a
measure of the spatial variation of the field in the mixed state. We extend our
earlier work [A.D. Bianchi et al. 2008 Science 319, 177] to temperatures up to
1250 mK. Over the entire temperature range, paramagnetism in the flux line
cores results in an increase of the form factor with field. Near H_c2 the form
factor decreases again, and our results indicate that this fall-off extends
outside the proposed FFLO region. Instead, we attribute the decrease to a
paramagnetic suppression of Cooper pairing. At higher temperatures, a gradual
crossover towards more conventional mixed state behavior is observed.
We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16 T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal was measured and confirms the presence of (non d-wave) nodes in the superconducting gap structure for measurements at 5 T and below. The nodal effects were suppressed at high fields. At low fields, a VL reorientation transition was observed between 1 T and 3 T, with the VL orientation changing by 45{\deg}. Below 1 T, the VL structure was strongly affected by pinning and the diffraction pattern had a fourfold symmetry. We suggest that this (and possibly also the VL reorientation) is due to pinning to defects aligned with the crystal structure, rather than being intrinsic.
We present small angle neutron scattering studies of the vortex lattice (VL) in CeCoIn5 with magnetic fields applied parallel (H) to the antinodal [100] and nodal [110] directions. For H || [100], a single VL orientation is observed, while a 90 degree reorientation transition is found for H || [110]. For both field orientations and VL configurations we find a distorted hexagonal VL with an anisotropy, Gamma = 2.0 +/- 0.05. The VL form factor shows strong Pauli paramagnetic effects similar to what have previously been reported for H || [001]. At high fields, above which the upper critical field (Hc2) becomes a first-order transition, an increased disordering of the VL is observed.
Understanding the mechanism and symmetry of electron pairing in iron-based superconductors represents an important challenge in condensed matter physics [1-3]. The observation of magnetic flux lines - "vortices" - in a superconductor can contribute to this issue, because the spatial variation of magnetic field reflects the pairing. Unlike many other iron pnictides, our KFe2As2 crystals have very weak vortex pinning, allowing small-angle-neutron-scattering (SANS) observations of the intrinsic vortex lattice (VL). We observe nearly isotropic hexagonal packing of vortices, without VL-symmetry transitions up to high fields along the fourfold c-axis of the crystals, indicating rather small anisotropy of the superconducting properties around this axis. This rules out gap nodes parallel to the c-axis, and thus d-wave and also anisotropic s-wave pairing [2, 3]. The strong temperature-dependence of the intensity down to T<<Tc indicates either widely different full gaps on different Fermi surface sheets, or nodal lines perpendicular to the axis.
From small-angle neutron scattering studies of the flux line lattice (FLL) in CeCoIn5, with magnetic field applied parallel to the crystal c-axis, we obtain the field- and temperature-dependence of the FLL form factor, which is a measure of the spatial variation of the field in the mixed state. We extend our earlier work [A.D. Bianchi et al. 2008 Science 319, 177] to temperatures up to 1250 mK. Over the entire temperature range, paramagnetism in the flux line cores results in an increase of the form factor with field. Near H_c2 the form factor decreases again, and our results indicate that this fall-off extends outside the proposed FFLO region. Instead, we attribute the decrease to a paramagnetic suppression of Cooper pairing. At higher temperatures, a gradual crossover towards more conventional mixed state behavior is observed.