• We demonstrate that combining standing-wave (SW) excitation with resonant inelastic x-ray scattering (RIXS) can lead to depth resolution and interface sensitivity for studying orbital and magnetic excitations in correlated oxide heterostructures. Here we demonstrate SW-RIXS by applying it to multilayer heterostructures consisting of a superconductor La$_{1.85}$Sr$_{0.15}$CuO$_{4}$ (LSCO) and a half-metallic ferromagnet La$_{0.67}$Sr$_{0.33}$MnO$_{3}$ (LSMO). We observe different depth distribution of the RIXS excitations. Local probing of the dd excitations indicates that the d$_{z2}$ excitations arise from the bottom LSCO/LSMO interface via direct CuO$_{2}$-(La,Sr)O-MnO$_{2}$ bonding, while the d$_{xy}$ and d$_{xz}$/d$_{yz}$ arise from the deeper "bulk" LSCO region. In addition, the magnetic excitations are found to arise from the LSCO/LSMO interfaces. SW-RIXS measurements of correlated oxide heterostructures should provide unique layer-resolved insights concerning their orbital and magnetic excitations, as well as a challenge for RIXS theory to specifically deal with interface effects.
  • Thickness driven electronic phase transitions are broadly observed in different types of functional perovskite heterostructures. However, uncertainty remains whether these effects are solely due to spatial confinement, broken symmetry or rather to a change of structure with varying film thickness. Here, we present direct evidence for the relaxation of oxygen 2p and Mn 3d orbital (p-d) hybridization coupled to the layer dependent octahedral tilts within a La2/3Sr1/3MnO3 film driven by interfacial octahedral coupling. An enhanced Curie temperature is achieved by reducing the octahedral tilting via interface structure engineering. Atomically resolved lattice, electronic and magnetic structures together with X-ray absorption spectroscopy demonstrate the central role of thickness dependent p-d hybridization in the widely observed dimensionality effects present in correlated oxide heterostructures.
  • Interface engineering is an extremely useful tool for systematically investigating materials and the various ways materials interact with each other. We describe different interface engineering strategies designed to reveal the origin of the electric and magnetic dead-layer at La0.67Sr0.33MnO3 interfaces. La0.67Sr0.33MnO3 is a key example of a strongly correlated peroskite oxide material in which a subtle balance of competing interactions gives rise to a ferromagnetic metallic groundstate. This balance, however, is easily disrupted at interfaces. We systematically vary the dopant profile, the disorder and the oxygen octahedra rotations at the interface to investigate which mechanism is responsible for the dead layer. We find that the magnetic dead layer can be completely eliminated by compositional interface engineering such that the polar discontinuity at the interface is removed. This, however, leaves the electrical dead-layer largely intact. We find that deformations in the oxygen octahedra network at the interface are the dominant cause for the electrical dead layer.
  • We present a study of the thickness dependence of magnetism and electrical conductivity in ultra thin La0.67Sr0.33MnO3 films grown on SrTiO3 (110) substrates. We found a critical thickness of 10 unit cells below which the conductivity of the films disappeared and simultaneously the Curie temperature (TC) increased, indicating a magnetic insulating phase at room temperature. These samples have a TC of about 560 K with a significant saturation magnetization of 1.2 +- 0.2 muB/Mn. The canted antiferromagnetic insulating phase in ultra thin films of n< 10 coincides with the occurrence of a higher symmetry structural phase with a different oxygen octahedra rotation pattern. Such a strain engineered phase is an interesting candidate for an insulating tunneling barrier in room temperature spin polarized tunneling devices.
  • Perovskite oxide heteroepitaxy receives much attention because of the possibility to com- bine the diverse functionalities of perovskite oxide building blocks. A general boundary con- dition for the epitaxy is the presence of polar discontinuities at heterointerfaces. These polar discontinuities result in reconstructions, often creating new functionalities at the interface. However, for a significant number of materials these reconstructions are unwanted as they alter the intrinsic materials properties at the interface. Therefore, a strategy to eliminate this reconstruction of the polar discontinuity at the interfaces is required. We show that the use of compositional interface engineering can prevent the reconstruction at the La0.67Sr0.33MnO3/SrTiO3 (LSMO/STO) interface. The polar discontinuity at this interface can be removed by the insertion of a single La0.33Sr0.67O layer, resulting in improved interface magnetization and electrical conductivity.
  • When comparing a set of La0.67Sr0.33MnO3 (LSMO) samples, the Curie temperature (TC) of the samples is an important figure of merit for the sample quality. Therefore, a reliable method to determine TC is required. Here, a method based on the analysis of the magnetization loops is proposed.
  • We demonstrate a direct correlation between the domain structure of multiferroic BiFeO3 thin films and exchange bias of Co0.9Fe0.1/BiFeO3 heterostructures. Two distinct types of interactions, an enhancement of the coercive field (exchange enhancement) and an enhancement of the coercive field combined with large shifts of the hysteresis loop (exchange bias), have been observed in these heterostructures, which depend directly on the type and crystallography of the nanoscale (2 nm) domain walls in the BiFeO3 film. We show that the magnitude of the exchange bias interaction scales with the length of 109 degree ferroelectric domain walls in the BiFeO3 thin films which have been probed via piezoresponse force microscopy and x-ray magnetic circular dichroism.