• Yb$_2$Si$_2$Al may be a prototype for exploring different aspects of the Shastry-Sutherland lattice, formed by planes of orthogonally coupled Yb ions. Measurements of the magnetic susceptibility find incoherently fluctuating Yb$^{3+}$ moments coexisting with a weakly correlated metallic state that is confirmed by measurements of the electrical resistivity. Increasing signs of Kondo coherence are found with decreasing temperature, including an enhanced Sommerfeld coefficient and Kadowaki-Woods ratio that signal that the metallic state found at the lowest temperatures is a Fermi liquid where correlations have become significantly stronger. A pronounced peak in the electronic and magnetic specific heat indicates that the coupling of the Yb moments to the conduction electrons leads to an effective Kondo temperature that is approximately 30 K. The valence of Yb$_2$Si$_2$Al has been investigated with electron spectroscopy methods. Yb$_2$Si$_2$Al is found to be strongly intermediate valent ($v_F=2.68(2)$ at 80 K). Taken together, these experimental data are consistent with a scenario where a coherent Kondo lattice forms in Yb$_2$Si$_2$Al from an incoherently fluctuating ensemble of Yb moments with incomplete Kondo compensation, and strong intermediate valence character.
  • The spin and orbital magnetic moments of the Fe3O4 epitaxial ultrathin film synthesized by plasma assisted simultaneous oxidization on MgO(100) have been studied with X-ray magnetic circular dichroism (XMCD). The ultrathin film retains a rather large total magnetic moment, i.e. (2.7+-0.15) uB/f.u., which is ~ 70% of that for the bulk-like Fe3O4. A significant unquenched orbital moment up to (0.54+-0.05) uB/f.u. was observed, which could come from the symmetry breaking at the Fe3O4/MgO interface. Such sizable orbital moment will add capacities to the Fe3O4-based spintronics devices in the magnetization reversal by the electric field.
  • Nanoscale Fe3O4 epitaxial thin film has been synthesized on MgO/GaAs(100) spintronic heterostructure, and studied with X-ray magnetic circular dichroism (XMCD). We have observed a total magnetic moment of (3.32 +- 0.1) uB/f.u., retaining 83% of the bulk value. Unquenched orbital moment of (0.47 +- 0.05) uB/f.u. has been confirmed by carefully applying the sum rule. The results offer direct experimental evidence of the bulk-like total magnetic moment and a large orbital moment in the nanoscale fully epitaxial Fe3O4/MgO/GaAs(100) heterostructure, which is significant for spintronics applications.
  • The growth dynamics of submonolayer coverages of Cobalt during buffer layer assisted growth on Ag(111) and Pt(111) substrates is investigated by variable temperature scanning tunneling microscopy in the temperature range between 80 and 150 Kelvin. It is found that attractive cluster-substrate interactions can govern the cluster formation on the Xe buffer layer, if the Xe layer is sufficiently thin. The interpretation of the microscopy results are supported by x-ray magnetic circular dichroism which monitors the effect of cluster-substrate interactions on the formation of magnetic moments and magnetic anisotropy of Co nanocluster during the different stages of growth. {\it Ab-initio} calculations show that the cluster magnetism is controlled by the interface anisotropy, leading to perpendicular magnetization for Co on Pt(111). Limits of and new potential for nanocluster fabrication by buffer layer assisted growth are discussed.
  • Magnetite, Fe$_3$O$_4$, displays a highly complex low temperature crystal structure that may be charge and orbitally ordered. Many of the recent experimental claims of such ordering rely on resonant soft x-ray diffraction at the oxygen K and iron L edges. We have re-examined this system and undertaken soft x-ray diffraction experiments on a high-quality single crystal. Contrary to previous claims in the literature, we show that the intensity observed at the Bragg forbidden (001/2)$_c$ reflection can be explained purely in terms of the low-temperature structural displacements around the resonant atoms. This does not necessarily mean that magnetite is not charge or orbitally ordered, but rather that the present sensitivity of resonant soft x-ray experiments does not allow conclusive demonstration of such ordering.
  • We report on the measurement of element-specific magnetic resonance spectra at gigahertz frequencies using x-ray magnetic circular dichroism (XMCD). We investigate the ferrimagnetic precession of Gd and Fe ions in Gd-substituted Yttrium Iron Garnet, showing that the resonant field and linewidth of Gd precisely coincide with Fe up to the nonlinear regime of parametric excitations. The opposite sign of the Gd x-ray magnetic resonance signal with respect to Fe is consistent with dynamic antiferromagnetic alignment of the two ionic species. Further, we investigate a bilayer metal film, Ni$_{80}$Fe$_{20}$(5 nm)/Ni(50 nm), where the coupled resonance modes of Ni and Ni$_{80}$Fe$_{20}$ are separately resolved, revealing shifts in the resonance fields of individual layers but no mutual driving effects. Energy-dependent dynamic XMCD measurements are introduced, combining x-ray absorption and magnetic resonance spectroscopies.
  • The magnetism of quench-condensed Ru and Rh impurities and metal films on Ag(100) and Pt(997) has been studied using x-ray magnetic circular dichroism. In the coverage range between 0.22 ML and 2.0 ML no dichroic signal was detected at the M3,2 absorption edges of Ru on Ag(100) at a temperature of 5 K in the presence of an applied magnetic field. The same was found for coverages between 0.12 ML and 0.5 ML of Rh on Ag(100) and Pt(997). It is concluded that the magnetic moments of single impurities, small clusters of various shape and monolayers of the 4d metals are below the detection limit of 0.04 muB per atom. These results provide an unambiguous determination of the local magnetic moment of Ru and Rh deposited on nonmagnetic transition-metal surfaces, which are in contrast with theoretical predictions.
  • Resonant soft x-ray diffraction has been used to probe the temperature dependent orbital and magnetic structure of $\mathrm{LaSr_{2}Mn_{2}O_7}$. Previous crystallographic studies have shown that this material has almost no MnO$_{6}$ oxygen displacement due to Jahn-Teller distortions at low temperatures. Within the low-temperature A-type antiferromagnetic phase, we found strong intensity at the $({1/4},{1/4},0)$ orbital and $LaSr_{2}Mn_{2}O_7$ magnetic reflections. This shows that even in the near absence of Jahn-Teller distortion, this compound is strongly orbitally ordered. A fit to the Mn $L$-edge resonance spectra demonstrates the presence of orbital ordering of the Mn$^{3+}$ ions with virtually no Jahn-Teller crystal field in addition to possible Mn$^{3+}$ and Mn$^{2+}$~like valence fluctuations.
  • We report resonant x-ray scattering data of the orbital and magnetic ordering at low temperatures at the Mn $L_{\rm 2,3}$ edges in \lsmo. The orderings display complex energy features close to the Mn absorption edges. Systematic modeling with atomic multiplet crystal field calculations was used to extract meaningful information regarding the interplay of spin, orbital and Jahn-Teller order. These calculations provide a good general agreement with the observed energy dependence of the scattered intensity {for a} dominant orbital ordering of the $ d_{x^2 - z^2} / d_{y^2 - z^2} $ type. In addition, the origins of various spectral features are identified. The temperature dependence of the orbital and magnetic ordering was measured and displays a strong interplay between the magnetic and orbital order parameters.