• ### Polaronic transport and thermoelectricity in Fe$_{1-x}$Co$_x$Sb$_2$S$_4$ ($x$ = 0, 0.1, and 0.2)(1804.07776)

April 20, 2018 cond-mat.str-el
We report a study of Co-doped berthierite Fe$_{1-x}$Co$_x$Sb$_2$S$_4$ ($x$ = 0, 0.1, and 0.2). The alloy series of Fe$_{1-x}$Co$_x$Sb$_2$S$_4$ crystallize in an orthorhombic structure with the Pnma space group, similar to FeSb$_2$, and show semiconducting behavior. The large discrepancy between activation energy for conductivity, $E_\rho$ (146 $\sim$ 270 meV), and thermopower, $E_S$ (47 $\sim$ 108 meV), indicates the polaronic transport mechanism. Bulk magnetization and heat capacity measurements of pure FeSb$_2$S$_4$ ($x$ = 0) exhibit a broad antiferromagnetic (AFM) transition ($T_N$ = 46 K) followed by an additional weak transition ($T^*$ = 50 K). Transition temperatures ($T_N$ and $T^*$) slightly decrease with increasing Co content $x$. This is also reflected in the thermal conductivity measurement, indicating strong spin-lattice coupling. Fe$_{1-x}$Co$_x$Sb$_2$S$_4$ shows relatively high value of thermopower (up to $\sim$ 624 $\mu$V K$^{-1}$ at 300 K) and thermal conductivity much lower when compared to FeSb$_{2}$, a feature desired for potential applications based on FeSb$_{2}$ materials.
• ### Large magnetoresistance in type-II Weyl semimetal WP$_2$(1708.08877)

We report magnetotransport study on type-II Weyl semimetal WP$_2$ single crystals. Magnetoresistance (MR) exhibits a nonsaturating $H^{n}$ field dependence (14,300\% at 2 K and 9 T) whereas systematic violation of Kohler's rule was observed. Quantum oscillations reveal a complex multiband electronic structure. The cyclotron effective mass close to the mass of free electron m$_e$ was observed in quantum oscillations along $b$-axis, while reduced effective mass of about 0.5$m_e$ was observed in $a$-axis quantum oscillations, suggesting Fermi surface anisotropy. Temperature dependence of the resistivity shows a large upturn that cannot be explained by the multi-band magnetoresistance of conventional metals. Even though crystal structure of WP$_{2}$ is not layered as in transition metal dichalcogenides, quantum oscillations suggest partial two-dimensional character.
• ### Wide temperature span of entropy change in first-order metamagnetic MnCo1-xFexSi(1306.3582)

Sept. 25, 2013 cond-mat.mtrl-sci
The crystal structure and magnetic properties of MnCoxFe1-xSi (x=0-0.5) compounds were investigated. With increasing Fe content, the unit cell changes anisotropically and the magnetic property evolves gradually: Curie temperature decreases continuously, the first-order metamagnetic transition from a low-temperature helical antiferromagnetic state to a high-temperature ferromagnetic state disappears gradually and then a spin-glass-like state and another antiferromagnetic state emerge in the low temperature region. The Curie transition leads to a moderate conventional entropy change. The metamagnetic transition not only yields a larger negative magnetocaloric effect at lower applied fields than in MnCoSi but also produces a very large temperature span (103 K for H=5 T) of delta S(T), which results in a large refrigerant capacity. These phenomena were explained in terms of crystal structure change and magnetoelastic coupling mechanism. The low-cost MnCo1-xFexSi compounds are promising candidates for near room temperature magnetic refrigeration applications because of the large isothermal entropy change and the wide working temperature span.