• ### Stabilization of highly polar BiFeO$_3$-like structure: a new interface design route for enhanced ferroelectricity in artificial perovskite superlattices(1507.00415)

Feb. 16, 2016 cond-mat.mtrl-sci
In ABO3 perovskites, oxygen octahedron rotations are common structural distortions that can promote large ferroelectricity in BiFeO3 with an R3c structure [1], but suppress ferroelectricity in CaTiO3 with a Pbnm symmetry [2]. For many CaTiO3-like perovskites, the BiFeO3 structure is a metastable phase. Here, we report the stabilization of the highly-polar BiFeO3-like phase of CaTiO3 in a BaTiO3/CaTiO3 superlattice grown on a SrTiO3 substrate. The stabilization is realized by a reconstruction of oxygen octahedron rotations at the interface from the pattern of nonpolar bulk CaTiO3 to a different pattern that is characteristic of a BiFeO3 phase. The reconstruction is interpreted through a combination of amplitude-contrast sub 0.1nm high-resolution transmission electron microscopy and first-principles theories of the structure, energetics, and polarization of the superlattice and its constituents. We further predict a number of new artificial ferroelectric materials demonstrating that nonpolar perovskites can be turned into ferroelectrics via this interface mechanism. Therefore, a large number of perovskites with the CaTiO3 structure type, which include many magnetic representatives, are now good candidates as novel highly-polar multiferroic materials [3].
• ### Strain-Induced Hybrid Improper Ferroelectricity in Simple Perovskites from First Principles(1306.1839)

Aug. 25, 2013 cond-mat.mtrl-sci
We performed first principles calculations for epitaxially strained orthorhombic CaTiO$_3$. The computational results reveal the existence of a metastable ferroelectric phase at compressive strain with unexpected in-plane polarization. Symmetry analysis indicates that two distortion modes at the X point combine to induce the polarization, leading to characterization as a hybrid improper ferroelectric. Our work demonstrates a mechanism for improper ferroelectricity in simple perovskites without the need for symmetry lowering by layering or cation ordering.