• We performed optical studies on CaFeAsF single crystals, a parent compound of the 1111-type iron-based superconductors that undergoes a structural phase transition from tetragonal to orthorhombic at $T_s$ = 121 K and a magnetic one to a spin density wave (SDW) state at $T_N$ = 110 K. In the low temperature optical conductivity spectrum, after the subtraction of a narrow Drude peak, we observe a pronounced singularity around 300 cm$^{-1}$ that separates two regions of quasilinear conductivity. We outline that these characteristic absorption features are signatures of Dirac fermions, similar to what was previously reported for the BaFe$_2$As$_2$ system [1]. In support of this interpretation, we show that for the latter system this singular feature disappears rapidly upon electron and hole doping, as expected if it arises from a van Hove singularity in-between two Dirac cones. Finally, we show that one of the infrared-active phonon modes (the Fe-As mode at 250 cm$^{-1}$) develops a strongly asymmetric line shape in the SDW state and note that this behaviour can be explained in terms of a strong coupling with the Dirac fermions.
  • We measured the optical conductivity of superconducting single crystals of Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$ with $x$ ranging from 0.40 (optimal doping, $T_c = 39$ K) down to 0.20 (underdoped, $T_c = 16$ K), where a magnetic order coexists with superconductivity. In the normal state, the low-frequency optical conductivity can be described by an incoherent broad Drude component and a coherent narrow Drude component: the broad one is doping-independent, while the narrow one shows strong scattering in the heavily underdoped compound. In the superconducting state, the formation of the condensate leads to a low-frequency suppression of the optical conductivity spectral weight. In the heavily underdoped region, the superfluid density is significantly suppressed, and the weight of unpaired carriers rapidly increases. We attribute these results to changes in the superconducting gap across the phase diagram, which could show a nodal-to-nodeless transition due to the strong interplay between magnetism and superconductivity in underdoped Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$.
  • In iron-based superconductors, a spin-density-wave (SDW) magnetic order is suppressed with doping and unconventional superconductivity appears in close proximity to the SDW instability. The optical response of the SDW order shows clear gap features: substantial suppression in the low-frequency optical conductivity, alongside a spectral weight transfer from low to high frequencies. Here, we study the detailed temperature dependence of the optical response in three different series of the Ba122 system [Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$, Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$ and BaFe$_{2}$(As$_{1-x}$P$_{x}$)$_{2}$]. Intriguingly, we found that the suppression of the low-frequency optical conductivity and spectral weight transfer appear at a temperature $T^{\ast}$ much higher than the SDW transition temperature $T_{SDW}$. Since this behavior has the same optical feature and energy scale as the SDW order, we attribute it to SDW fluctuations. Furthermore, $T^{\ast}$ is suppressed with doping, closely following the doping dependence of the nematic fluctuations detected by other techniques. These results suggest that the magnetic and nematic orders have an intimate relationship, in favor of the magnetic-fluctuation-driven nematicity scenario in iron-based superconductors.
  • We measured the polarized optical conductivity of URu$_2$Si$_2$ from room temperature down to 5 K, covering the Kondo state, the coherent Kondo liquid regime, and the hidden-order phase. The normal state is characterized by an anisotropic behavior between the ab plane and c axis responses. The ab plane optical conductivity is strongly influenced by the formation of the coherent Kondo liquid: a sharp Drude peak develops and a hybridization gap at 12 meV leads to a spectral weight transfer to mid-infrared energies. The c axis conductivity has a different behavior: the Drude peak already exists at 300 K and no particular anomaly or gap signature appears in the coherent Kondo liquid regime. When entering the hidden-order state, both polarizations see a dramatic decrease in the Drude spectral weight and scattering rate, compatible with a loss of about 50 % of the carriers at the Fermi level. At the same time a density-wave like gap appears along both polarizations at about 6.5 meV at 5 K. This gap closes respecting a mean field thermal evolution in the ab plane. Along the c axis it remains roughly constant and it "fills up" rather than closing.
  • We measured the optical conductivity of superconducting LiFeAs. In the superconducting state, the formation of the condensate leads to a spectral-weight loss and yields a penetration depth of 225 nm. No sharp signature of the superconducting gap is observed. This suggests that the system is likely in the clean limit. A Drude-Lorentz parametrization of the data in the normal state reveals a quasiparticle scattering rate supportive of spin fluctuations and proximity to a quantum critical point.
  • The effect of K, Co and P dopings on the lattice dynamics in the BaFe$_2$As$_2$ system is studied by infrared spectroscopy. We focus on the phonon at $\sim$ 253 cm$^{-1}$, the highest energy in-plane infrared-active Fe-As mode in BaFe$_2$As$_2$. Our studies show that the Co and P dopings lead to a blue shift of this phonon in frequency, which can be simply interpreted by the change of lattice parameters induced by doping. In sharp contrast, an unusual red shift of the same mode was observed in the K-doped compound, at odds with the above explanation. This anomalous behavior in K-doped BaFe$_2$As$_2$ is more likely associated with the coupling between lattice vibrations and other channels, such as charge or spin. This coupling scenario is also supported by the asymmetric line shape and intensity growth of the phonon in the K-doped compound.
  • We measured the in-plane optical conductivity of a nearly optimally doped (Ba,K)Fe2As2 single crystal with Tc = 39.1 K. Upon entering the superconducting state the optical conductivity below ~20 meV vanishes, strongly suggesting a fully gapped system. A BCS-like fit requires two different isotropic gaps to describe the optical response of this material. The temperature dependence of the gaps and the penetration depth suggest a strong interband coupling, but no impurity scattering induced pair breaking is present. This contrasts to the large residual conductivity observed in optimally doped Ba(Fe,Co)2As2 and strongly supports an s(+/-) gap symmetry for these compounds.
  • Superconducting Pr$_2$CuO$_x$, $x\simeq 4$ films with $T^\prime$ structure and a $T_c$ of 27 K have been investigated by millimeter-wave transmission and broadband (infrared-to-ultraviolet) reflectivity measurements in the normal and superconducting state. The results obtained by both experimental methods show a consistent picture of the superconducting condensate formation below $T_c$. An Eliashberg analysis of the data proves $d$-wave superconductivity and unitary-limit impurity scattering of the charge carriers below $T_{c}$. The derived electron-exchange boson interaction spectral function $I^2\chi(\omega)$ shows only marginal changes at the superconducting transition with the mass enhancement factor $\lambda$, the first inverse moment of $I^2\chi(\omega)$, being equal to 4.16 at 30 K and to 4.25 at 4 K.
  • Superconducting Pr$_2$CuO$_x$, $x\simeq 4$ (PCO) films with $T^\prime$ structure and a $T_c$ of 27 K have been investigated by various optical methods in a wide frequency (7 - 55000 cm$^{-1}$) and temperature (2 to 300 K) range. The optical spectra do not reveal any indication of a normal-state gap formation. A Drude-like peak centered at zero frequency dominates the optical conductivity below 150 K. At higher temperatures, it shifts to finite frequencies. The detailed analysis of the low-frequency conductivity reveals that the Drude peak and a far-infrared (FIR) peak centered at about 300 cm$^{-1}$ persist at all temperatures. The FIR-peak spectral weight is found to grow at the expense of the Drude spectral weight with increasing temperature. The temperature dependence of the penetration depth follows a behavior typical for $d$-wave superconductors. The absolute value of the penetration depth for zero temperature is 1.6 $\mu$m, indicating a rather low density of the superconducting condensate.
  • We report the observation of a pseudogap in the \emph{ab}-plane optical conductivity of underdoped Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$ ($x = 0.2$ and 0.12) single crystals. Both samples show prominent gaps opened by a spin density wave (SDW) order and superconductivity at the transition temperatures $T_{\it SDW}$ and $T_c$, respectively. In addition, we observe an evident pseudogap below $T^{\ast} \sim$ 75 K, a temperature much lower than $T_{\it SDW}$ but much higher than $T_{c}$. A spectral weight analysis shows that the pseudogap is closely connected to the superconducting gap, indicating the possibility of its being a precursor of superconductivity. The doping dependence of the gaps is also supportive of such a scenario.
  • Fermi showed that electrons, as a result of their quantum nature, form a gas of particles where the temperature and density follow the so called Fermi distribution. In a metal, as shown by Landau, that despite their strong Coulomb interaction with each other and the positive background ions, the electrons continue to act like free quantum mechanical particles but with enhanced masses. This state of matter, the Landau-Fermi liquid, is recognized experimentally by an electrical resistivity that is proportional to the square of the absolute temperature plus a term proportional to the square of the frequency of the applied field. Calculations show that, if electron-electron scattering dominates the resistivity in a Landau Fermi liquid, the ratio of the two terms, $b$ has the universal value of {\em b} = 4. We find that in the normal state of the heavy Fermion metal URu$_2$Si$_2$, instead of the Fermi liquid value of 4 the coefficient $b$ =1 $\pm$ 0.1. This unexpected result implies that the electrons in this material are experiencing a unique scattering process. This scattering is intrinsic and we suggest that, the uranium $f$ electrons do not hybridize to form a coherent Fermi liquid but instead act like a dense array of elastic impurities, interacting incoherently with the charge carriers. This behavior is not restricted to URu$_2$Si$_2$. Fermi liquid like states with $b \neq$ 4 have been observed in a number of disparate systems but the significance of this result has not been recognized.
  • We determined the optical conductivity of Bi(2)Sr(2-x)La(x)CuO(6) at dopings covering the phase diagram from the underdoped to the overdoped regimes. The frequency dependent scattering rate shows a pseudogap extending into the overdoped regime. We found that the effective mass enhancement calculated from the optical conductivity is constant throughout the phase diagram. Conversely, the effective optical charge density varies almost linearly with doping. Our results suggest that the low frequency electrodynamics of Bi(2)Sr(2-x)La(x)CuO(6) is not strongly affected by the long range Mott transition.
  • We measured the temperature dependent infrared reflectivity spectra of TbMnO3 with the electric field of light polarized along each of the three crystallographic axes. We analyzed the effect, on the phonon spectra, of the different phase transitions occurring in this material. We show that the antiferromagnetic transition at TN renormalizes the phonon parameters along the three directions. Our data indicate that the electromagnon, observed along the a direction, has an important contribution to the building of the dielectric constant. Only one phonon, observed along the c-axis, has anomalies at the ferroelectric transition. This phonon is built mostly from Mn vibrations, suggesting that Mn displacements are closely related to the formation of the ferroelectric order.
  • The optical conductivity of Ba(Fe$_{0.92}$Co$_{0.08}$)$_2$As$_2$ shows a clear signature of the superconducting gap, but a simple $s$-wave description fails in accounting for the low frequency response. This task is achieved by introducing an extra Drude peak in the superconducting state representing sub-gap absorption, other than thermally broken pairs. This extra peak and the coexisting $s$-wave response respect the total sum rule indicating a common origin for the carriers. We discuss the possible origins for this absorption as (i) quasiparticles due to pair-breaking from interband impurity scattering in a two band $s_{\pm}$ gap symmetry model, which includes (ii) the possible existence of impurity levels within an isotropic gap model; or (iii) an indication that one of the bands is highly anisotropic.
  • We measured the temperature dependent infrared reflectivity spectra of MnF2 between 4 K and room temperature. We show that the phonon spectrum undergoes a strong renormalization at TN. The ab-initio calculation we performed on this compound accurately predict the magnitude and the direction of the phonon parameters changes across the antiferromagnetic transition, showing that they are mainly induced by the magnetic order. In this material, we found that the dielectric constant is mostly from phonon origin. The large change in the lattice parameters with temperature seen by X-ray diffraction as well as the A2u phonon softening below TN indicate that magnetic order induced distortions in MnF2 are compatible with the ferroelectric instabilities observed in TiO2, FeF2 and other rutile-type fluorides. This study also shows the anomalous temperature evolution of the lower energy Eu mode in the paramagnetic phase, which can be compared to that of the B1g one seen by Raman spectroscopy in many isostructural materials. This was interpreted as being a precursor of a phase transition from rutile to CaCl2 structure which was observed under pressure in ZnF2.
  • The optical properties of single crystal Pr_{1.85}Ce_{0.15}CuO_4 have been measured over a wide frequency range above and below the critical temperature (T_c \simeq 20 K). In the normal state the coherent part of the conductivity is described by the Drude model, from which the scattering rate just above T_c is determined to be 1/\tau \simeq 80 cm^{-1}. The condition that \hbar/\tau \approx 2k_B T near T_c appears to be a general result in many of the cuprate superconductors. Below T_c the formation of a superconducting energy gap is clearly visible in the reflectance, from which the gap maximum is estimated to be \Delta_0 \simeq 35 cm^{-1} (4.3 meV). The ability to observe the superconducting energy gap in the optical properties favors the nonmonotonic over the monotonic description of the d-wave gap. The penetration depth for T\ll T_c is \lambda \simeq 2000 \AA, which when taken with the estimated value for the dc conductivity just above T_c of \sigma_{dc} \simeq 35 \times 10^3 \Omega^{-1}cm^{-1} places this material on the general scaling line for the cuprates defined by 1/\lambda^2 \propto \sigma_{dc}(T\simeq T_c) \times T_c. This result is consistent with the observation that 1/\tau \approx 2\Delta_0, which implies that the material is not in the clean limit.
  • The doping and temperature dependent conductivity of electron-doped cuprates is analysed. The variation of kinetic energy with doping is shown to imply that the materials are approximately as strongly correlated as the hole-doped materials. The optical spectrum is fit to a quasiparticle scattering model; while the model fits the optical data well, gross inconsistencies with photoemission data are found, implying the presence of a large, strongly doping dependent Landau parameter.