Electric-field (E-field) control of magnetism enabled by multiferroics has
the potential to revolutionize the landscape of present memory devices plagued
with high energy dissipation. To date, this E-field controlled multiferroic
scheme at room temperature has only been demonstrated using BiFeO3 (BFO) films
grown on DyScO3 (refs 1 and 2), a unique and expensive substrate, which gives
rise to a particular ferroelectric domain pattern in BFO. Here, we demonstrate
reversible E-field-induced switching of the magnetic state of the Co layer in
Co/BFO (001) thin film heterostructures fabricated on SrTiO3 substrates. The
angular dependence of the coercivity and the remanent magnetization of the Co
layer indicates that its easy axis reversibly switches by 45{\deg} back and
forth between the (100) and the (110) crystallographic directions of SrTiO3 as
a result of alternating application of positive and negative voltage pulses on
BFO. The coercivity of the Co layer exhibits a hysteretic behavior between two
states as a function of voltage. To explain the observation, we have also
measured the exact canting angle of the antiferromagnetic G-type domain in BFO
films for the first time using neutron diffraction. These results suggest a
pathway to integrating BFO-based devices on Si wafers for implementing low
power consumption and non-volatile magnetoelectronic devices.
-
A joint measurement is presented of the branching fractions
$B^0_s\to\mu^+\mu^-$ and $B^0\to\mu^+\mu^-$ in proton-proton collisions at the
LHC by the CMS and LHCb experiments. The data samples were collected in 2011 at
a centre-of-mass energy of 7 TeV, and in 2012 at 8 TeV. The combined analysis
produces the first observation of the $B^0_s\to\mu^+\mu^-$ decay, with a
statistical significance exceeding six standard deviations, and the best
measurement of its branching fraction so far. Furthermore, evidence for the
$B^0\to\mu^+\mu^-$ decay is obtained with a statistical significance of three
standard deviations. The branching fraction measurements are statistically
compatible with SM predictions and impose stringent constraints on several
theories beyond the SM.
-
Photonic crystal nanocavities are used to enhance photoluminescence from
single-walled carbon nanotubes. Micelle-encapsulated nanotubes are deposited on
nanocavities within Si photonic crystal slabs and confocal microscopy is used
to characterize the devices. Photoluminescence spectra and images reveal
nanotube emission coupled to nanocavity modes. The cavity modes can be tuned
throughout the emission wavelengths of carbon nanotubes, demonstrating the
ability to enhance photoluminescence from a variety of chiralities.
-
Gate-voltage effects on photoluminescence spectra of suspended single-walled
carbon nanotubes are investigated. Photoluminescence microscopy and excitation
spectroscopy are used to identify individual nanotubes and to determine their
chiralities. Under an application of gate voltage, we observe slight blueshifts
in the emission energy and strong quenching of photoluminescence. The
blueshifts are similar for different chiralities investigated, suggesting
extrinsic mechanisms. In addition, we find that the photoluminescence intensity
quenches exponentially with gate voltage.
-
Direct measurements of the diffusion length of excitons in air-suspended
single-walled carbon nanotubes are reported. Photoluminescence microscopy is
used to identify individual nanotubes and to determine their lengths and chiral
indices. Exciton diffusion length is obtained by comparing the dependence of
photoluminescence intensity on the nanotube length to numerical solutions of
diffusion equations. We find that the diffusion length in these clean, as-grown
nanotubes is significantly longer than those reported for micelle-encapsulated
nanotubes.
-
Addition of only 1% of acetylene into ethanol was found to enhance the growth
rate of singlewalled carbon nanotubes (SWNTs) by up to ten times. Since
acetylene is a byproduct of the thermal decomposition of ethanol, this suggests
an alternative fast reaction pathway to the formation of SWNTs from ethanol via
byproducts of decomposition. This accelerated growth, however, only occurred in
the presence of ethanol, whereas pure acetylene at the same partial pressure
resulted in negligible growth and quickly deactivated the catalyst. The dormant
catalyst could be revived by reintroduction of ethanol, indicating that
catalyst deactivation is divided into reversible and irreversible stages.
-
We have measured a strictly linear pi-plasmon dispersion along the axis of
individualized single wall carbon nanotubes, which is completely different from
plasmon dispersions of graphite or bundled single wall carbon nanotubes.
Comparative ab initio studies on graphene based systems allow us to reproduce
the different dispersions. This suggests that individualized nanotubes provide
viable experimental access to collective electronic excitations of graphene,
and it validates the use of graphene to understand electronic excitations of
carbon nanotubes. In particular, the calculations reveal that local field
effects (LFE) cause a mixing of electronic transitions, including the 'Dirac
cone', resulting in the observed linear dispersion.
-
A parametric study of so-called "super growth" of single-walled carbon
nanotubes(SWNTs) was done by using combinatorial libraries of iron/aluminum
oxide catalysts. Millimeter-thick forests of nanotubes grew within 10 min, and
those grown by using catalysts with a thin Fe layer (about 0.5 nm) were SWNTs.
Although nanotube forests grew under a wide range of reaction conditions such
as gas composition and temperature, the window for SWNT was narrow. Fe
catalysts rapidly grew nanotubes only when supported on aluminum oxide.
Aluminum oxide, which is a well-known catalyst in hydrocarbon reforming, plays
an essential role in enhancing the nanotube growth rates.
-
Often a modification of microscopic symmetry in a system can result in a
dramatic change in its macroscopic properties. Here we report that symmetry
breaking by a tube-threading magnetic field can drastically increase the
photoluminescence quantum yield of semiconducting single-walled carbon
nanotubes, by as much as a factor of six, at low temperatures. To explain this
striking connection between seemingly unrelated properties, we have developed a
comprehensive theoretical model based on magnetic-field-dependent
one-dimensional exciton band structure and the interplay of strong Coulomb
interactions and the Aharonov-Bohm effect. This conclusively explains our data
as the first experimental observation of dark excitons 5-10 meV below the
bright excitons in single-walled carbon nanotubes. We predict that this quantum
yield increase can be made much larger in disorder-free samples.
-
We have performed polarization-dependent ultrafast pump-probe spectroscopy of
a film of aligned single-walled carbon nanotube bundles. By taking into account
imperfect nanotube alignment as well as anisotropic absorption cross sections,
we quantitatively determined distinctly different photo-bleaching dynamics for
polarizations parallel and perpendicular to the tube axis. For perpendicular
polarization, we observe a slow (1.0-1.5 ps) relaxation process, previously
unobserved in randomly-oriented nanotube bundles. We attribute this slower
dynamics to the excitation and relaxation of surface plasmons in the radial
direction of the nanotube bundles.
-
The static and dynamic magnetic properties of an $S=1/2$ stacked triangular
antiferromagnet RbCuCl$_{3}$ with a helical spin structure due to lattice
distortion were investigated by susceptibility, high-field magnetization
process and ESR measurements. The susceptibilities were analyzed by
high-temperature expansion approximation in terms of ferromagnetic intrachain
coupling and the antiferromagnetic interchain coupling. The magnetization
saturates at $H_{\rm s}\approx 66.8$ T at 1.5 K, the value of which is twice
that of CsCuCl$_3$. A small magnetization jump indicative of a phase transition
was observed at $H_{\rm c}=21.2$ T $\approx (1/3)H_{\rm s}$ for $H{\perp}c$.
ESR modes observed for $H\parallel c$ are well described by the calculation
based on the helical spin structure. From the present measurements, the
ferromagnetic intrachain and two kinds of antiferromagnetic interchain exchange
interactions, and the planar anisotropy energy were determined as $J_0/k_{\rm
B}=25.7$ K, $J_1/k_{\rm B}=-10.6$ K, $J_1'/k_{\rm B}=-17.4$ K, and
${\Delta}J_0/k_{\rm B}=-0.45$ K, respectively.
A joint measurement is presented of the branching fractions $B^0_s\to\mu^+\mu^-$ and $B^0\to\mu^+\mu^-$ in proton-proton collisions at the LHC by the CMS and LHCb experiments. The data samples were collected in 2011 at a centre-of-mass energy of 7 TeV, and in 2012 at 8 TeV. The combined analysis produces the first observation of the $B^0_s\to\mu^+\mu^-$ decay, with a statistical significance exceeding six standard deviations, and the best measurement of its branching fraction so far. Furthermore, evidence for the $B^0\to\mu^+\mu^-$ decay is obtained with a statistical significance of three standard deviations. The branching fraction measurements are statistically compatible with SM predictions and impose stringent constraints on several theories beyond the SM.
Photonic crystal nanocavities are used to enhance photoluminescence from single-walled carbon nanotubes. Micelle-encapsulated nanotubes are deposited on nanocavities within Si photonic crystal slabs and confocal microscopy is used to characterize the devices. Photoluminescence spectra and images reveal nanotube emission coupled to nanocavity modes. The cavity modes can be tuned throughout the emission wavelengths of carbon nanotubes, demonstrating the ability to enhance photoluminescence from a variety of chiralities.
Gate-voltage effects on photoluminescence spectra of suspended single-walled carbon nanotubes are investigated. Photoluminescence microscopy and excitation spectroscopy are used to identify individual nanotubes and to determine their chiralities. Under an application of gate voltage, we observe slight blueshifts in the emission energy and strong quenching of photoluminescence. The blueshifts are similar for different chiralities investigated, suggesting extrinsic mechanisms. In addition, we find that the photoluminescence intensity quenches exponentially with gate voltage.
Direct measurements of the diffusion length of excitons in air-suspended single-walled carbon nanotubes are reported. Photoluminescence microscopy is used to identify individual nanotubes and to determine their lengths and chiral indices. Exciton diffusion length is obtained by comparing the dependence of photoluminescence intensity on the nanotube length to numerical solutions of diffusion equations. We find that the diffusion length in these clean, as-grown nanotubes is significantly longer than those reported for micelle-encapsulated nanotubes.
We have measured a strictly linear pi-plasmon dispersion along the axis of individualized single wall carbon nanotubes, which is completely different from plasmon dispersions of graphite or bundled single wall carbon nanotubes. Comparative ab initio studies on graphene based systems allow us to reproduce the different dispersions. This suggests that individualized nanotubes provide viable experimental access to collective electronic excitations of graphene, and it validates the use of graphene to understand electronic excitations of carbon nanotubes. In particular, the calculations reveal that local field effects (LFE) cause a mixing of electronic transitions, including the 'Dirac cone', resulting in the observed linear dispersion.