• Mechanism of unconventional superconductivity in FeSe has been intensely scrutinized recently because of a variety of exotic properties unprecedented for other iron-based superconductors. A central unanswered question concerns the origin of the interaction that causes the nematic transition at $T_s=90\,K$ without accompanying magnetic order. Elucidating the nature of spin excitations in the normal state is a key to addressing this issue. Here we report, from inelastic neutron-scattering measurements in FeSe single crystals, that high-energy spin excitation spectra of FeSe exhibit characteristic energy dependence with missing intensity at around 70-80$\,$meV, which are very different from other iron-based superconductors. Despite of the strongest electron correlations among the iron-based superconductor family, the spectra are qualitatively at variance with the local moment model and can be essentially described by the itinerant electron picture. Moreover, the dynamical spin susceptibility above $T_s$ is only weakly temperature dependent, which is in stark contrast to the Curie-Weiss behavior of the electronic nematic susceptibility, suggesting that the nematic transition is not likely driven by spin but by orbital degrees of freedom.
  • Low-energy electron excitation spectra were measured on a single crystal of a typical iron-based superconductor PrFeAsO$_{0.7}$ using resonant inelastic X-ray scattering (RIXS) at the Fe-$L_3$ edge. Characteristic RIXS features are clearly observed around 0.5, 1-1.5 and 2-3 eV energy losses. These excitations are analyzed microscopically with theoretical calculations using a 22-orbital model derived from first-principles electronic structure calculation. Based on the agreement with the experiment, the RIXS features are assigned to Fe-$d$ orbital excitations which, at low energies, are accompanied by spin flipping and dominated by Fe $d_{yz}$ and $d_{xz}$ orbital characters. Furthermore, our calculations suggest dispersive momentum dependence of the RIXS excitations below 0.5 eV, and predict remarkable splitting and merging of the lower-energy excitations in momentum space. Those excitations, which were not observed in the present experiment, highlight the potential of RIXS with an improved energy resolution to unravel new details of the electronic structure of the iron-based superconductors.
  • The effects of lithium absorption on the crystal structure and electronic properties of IrSi3, a binary silicide with a noncentrosymmetric crystal structure, were studied. X-ray and neutron diffraction experiments revealed that hexagonal IrSi3 (space group P6_3mc) transforms into trigonal Li2IrSi3 (space group P31c) upon lithium absorption. The structure of Li2IrSi3 is found to consist of a planar kagome network of silicon atoms with Li and Ir spaced at unequal distances between the kagome layers, resulting in a polar structure along the c-axis. Li2IrSi3 exhibited type-II superconductivity with a transition temperature Tc of 3.8 K, displaying a structure type that no previous superconductors have been reported to have.
  • We have performed neutron diffraction measurement on a single crystal of parent compound of iron-based superconductor, BaFe$_2$As$_2$ at 12~K. In order to investigate in-plane anisotropy of magnetic form factor in the antiferromagnetic phase, the detwinned single crystal is used in the measurement. The magnetic structure factor and magnetic form factor are well explained by the spin densities consisting of $3d_{yz}$ electrons with a fraction of about 40~\% and the electrons in the other four $3d$ orbitals with each fraction of about 15~\%. Such anisotropic magnetic form factor is qualitatively consistent with the anisotropic magnetic behaviors observed in the antiferromagnetic phase of the parent compound of iron-based superconductor.
  • Spatial phase separation into mesoscopic domains of non-magnetic [superconducting (SC) below Tc = 25.5 K] and two kinds of magnetic phases, one showing disordered spin density wave (d-SDW) order and another associated with glassy weak magnetism (WM), are observed below ~100 K by muon spin rotation (muSR) in LaFeAsO1-xFx for x = 0.057(3) which is near the boundary of these phases on the doping phase diagram. In contrast to the competing order observed in the regular SDW phase of Ba(Fe1-xCox)2As2, the WM domain exhibits cooperative coupling of superconducting and magnetic order parameters as inferred from strong diamagnetism and associated negative shift of muSR frequency just below Tc.
  • Phonons in single crystals of PrFeAsO_{1-y} are investigated using high-resolution inelastic x-ray scattering and ab initio pseudopotential calculations. Extensive measurements of several samples at temperatures spanning the magnetic ordering temperature and the superconducting transition temperature show that there are some changes in phonon spectra with temperature and/or doping. We compare our measurements with several ab initio pseudopotential models (nonmagnetic tetragonal, oxygen-deficient O_{7/8} supercell, magnetic orthorhombic, and magnetic tetragonal) and find that the experimentally observed changes are much smaller than the differences between the experimental data and the calculations. Agreement is improved if magnetism is included in the calculations via the local spin density approximation, as the Fe atomic motions parallel to the ferromagnetic ordering direction are softened. However, the antiferromagnetically polarized modes remain hard, and in disagreement with the experimental data. In fact, given the increasing evidence for anisotropy in the iron pnictide materials, the phonon response is surprisingly isotropic. We consider several modifications of the ab initio calculations to improve the agreement with the experimental data. Improved agreement is found by setting the matrix to zero (clipping the bond) between nearest-neighbor antiferromagnetically aligned Fe atoms in the magnetic calculation, or by softening only the in-plane nearest-neighbor Fe-As force constant in the nonmagnetic calculation. We discuss these results in the context of other measurements, especially of phonons, for several FeAs systems. Fluctuating magnetism may be a partial explanation for the failure of the calculations, but seems incomplete in the face of the similarity of the measured phonon response in all the systems investigated here including those known to have static magnetism.
  • We report Fe K beta x-ray emission spectroscopy study of local magnetic moments in various iron based superconductors in their paramagnetic phases. Local magnetic moments are found in all samples studied: PrFeAsO, Ba(Fe,Co)2As2, LiFeAs, Fe1+x(Te,Se), and A2Fe4Se5 (A=K, Rb, and Cs). The moment size varies significantly across different families. Specifically, all iron pnictides samples have local moments of about 1 $\mu_B$/Fe, while FeTe and K2Fe4Se5 families have much larger local moments of ~2$\mu_B$/Fe, ~3.3$\mu_B$/Fe, respectively. In addition, we find that neither carrier doping nor temperature change affects the local moment size.
  • We have performed powder neutron diffraction on the new superconductor, CeNi$_{0.8}$Bi$_2$ with a superconducting transtion temperature $T_\textrm{c} \sim$ 4.2 K. The structural parameters of this compound at room temperature are determined by Rietveld analysis. Below about 5 K, the clear magnetic Bragg peaks with propagation vector $q$=(0 0 0) are observed. The observed intensities of magnetic Bragg peaks can be explained by the magnetic structure that the two Ce moments in the unit cell are antiparallel along c axis. The magnetic Bragg peaks are observed in the superconducting state, indicating the coexistence of the antiferromagnetic ordering and the superconductivity in this compound. The intensity of magnetic Bragg peak monotonously increases with decreasing temperature below $T_\textrm{N}$ and does not exhibit apparent anomaly at $T_\textrm{c}$, obviously different from cases of heavy fermion superconductors in which the magnetic ordering and the superconductivity coexist, for example, Cd-doped CeCoIn$_5$. These results suggest that the 4$f$ electron of the Ce atom is not coupled with the superconducting carrier, and the magnetic ordering is almost independent of the superconductivity in CeNi$_{0.8}$Bi$_2$.
  • We have performed an angle-resolved photoemission spectroscopy (ARPES) study of the iron-based superconductor PrFeAsO_{0.7} and examined the Fermi surfaces and band dispersions near the Fermi level. Heavily hole-doped electronic states have been observed due to the polar nature of the cleaved surfaces. Nevertheless, we have found that the ARPES spectra basically agree with band dispersions calculated in the local density approximation (LDA) if the bandwidth is reduced by a factor of ~2.5 and then the chemical potential is lowered by ~70 meV. Comparison with previous ARPES results on LaFePO reveals that the energy positions of the d_{3z^2-r^2}- and d_{yz,zx}-derived bands are considerably different between the two materials, which we attribute to the different pnictogen height as predicted by the LDA calculation.
  • We performed inelastic neutron scattering on powder sample of the P-doped iron-based superconductor BaFe2(As0.65P0.35)2 with Tc = 30K, whose superconducting (SC) order parameter is expected to have line nodes. We have observed spin resonance at Q $\sim$ 1.2{\AA}^{-1} and E=12 meV in the SC state. The resonance enhancement, which can be a measure of the area of sign reversal between the hole and electron Fermi surfaces (FSs), is comparable to those of other iron-based superconductors without line nodes. This fact indicates that the sign reversal between the FSs is still dominant in this system, and the line nodes should create only limited area of sign-reversal on a single FS. Hence the system can hold relatively high-Tc. Comparison with theoretical calculation indicates horizontal line nodes may be a candidate to reproduce the observation.
  • An optimally doped iron-based superconductor LaFeAsO$_{0.92}$F$_{0.08}$ with $T_c = 29$ K has been studied by inelastic powder neutron scattering. The magnetic excitation at $Q=1.15$ \AA$^{-1}$ is enhanced below $T_c$, leading to a peak at $E_{res}\sim13$ meV as the resonance mode, in addition to the formation of a gap at low energy below the crossover energy $\Delta_{c}\sim10 meV$. The peak energy at $Q=1.15$ \AA$^{-1}$ corresponds to $5.2 k_B T_c$ in good agreement with the other values of resonance mode observed in the various iron-based superconductors, even in the high-$T_c$ cuprates. Although the phonon density of states has a peak at the same energy as the resonance mode in the present superconductor, the $Q$-dependence is consistent with the resonance being of predominately magnetic origin.
  • Low energy spin fluctuations are studied for the electron-doped Fe-based superconductor LaFeAsO(1-x)F(x) by inelastic neutron scattering up to the energy transfer of w = 15 meV using polycrystalline samples. Superconducting samples (x=0.057, Tc=25 K and x=0.082, Tc=29 K) show dynamical spin susceptibility chi"(w) almost comparable with the parent sample's. However chi"(w) is almost vanished in the x=0.158 sample where the superconductivity is highly suppressed. These results are compatible with the theoretical suggestions that the spin fluctuation plays an important role for the superconductivity.
  • Characteristic normal-state charge transport is found in the oxygen-deficient iron-arsenides LnFeAsO1-y (Ln: La and Nd) with the highest Tc's among known Fe-based superconductors. The effect of "doping" in this system is mainly on the carrier scattering, quite distinct from that in high-Tc cuprates. In the superconducting regime of the La system with maximum Tc = 28 K, the low-temperature resistivity is dominated by a T^2 term. On the other hand, in the Nd system with Tc higher than 40 K, the carriers are subject to stronger scattering showing T-linear resistivity and small magnetoresistance. Such strong scattering appears crucial for high-Tc superconductivity in the iron-based system.
  • Local magnetic measurements are used to quantitatively characterize heterogeneity and flux line pinning in PrFeAsO_1-y and NdFeAs(O,F) superconducting single crystals. In spite of spatial fluctuations of the critical current density on the macroscopic scale, it is shown that the major contribution comes from collective pinning of vortex lines by microscopic defects by the mean-free path fluctuation mechanism. The defect density extracted from experiment corresponds to the dopant atom density, which means that dopant atoms play an important role both in vortex pinning and in quasiparticle scattering. In the studied underdoped PrFeAsO_1-y and NdFeAs(O,F) crystals, there is a background of strong pinning, which we attribute to spatial variations of the dopant atom density on the scale of a few dozen to one hundred nm. These variations do not go beyond 5% - we therefore do not find any evidence for coexistence of the superconducting and the antiferromagnetic phase. The critical current density in sub-T fields is characterized by the presence of a peak effect, the location of which in the (B,T)-plane is consistent with an order-disorder transition of the vortex lattice.
  • A high-quality PrFeAsO$_{1-\delta}$ single crystal ($T_{\rm c}=44$ K) has been investigated by the magnetic torque. Antiferromagnetism of the Pr$^{3+}$ ions was found to coexist with superconductivity in PrFeAsO$_{1-\delta}$ at temperatures below $T_\mathrm{N}=14$ K. We predict a magnetic structure that is not in accordance with earlier neutron studies performed using polycrystalline nonsuperconducting specimens. As the temperature decreases, the superconducting anisotropy $\gamma\sim 4$ of PrFeAsO$_{1-\delta}$ increases near $T_c$ and tends to decrease slightly at lower temperatures.
  • The c-axis transport properties of a high-pressure synthesized PrFeAsO0.7 single crystal are studied using s-shaped junctions. Resistivity anisotropy of about 120 detected at 50 K shows the presence of strong anisotropy in the electronic states. The obtained critical current density for the c-axis of 2.9*10^5 A/cm^2 is two orders of magnitude larger than that in Bi2Sr1.6La0.4CuO6+d. The appearance of a hysteresis in the current-voltage curve below T_c is the manifestation of the intrinsic Josephson effect similar to that in cuprate superconductors. The suppression of the critical current-normal resistance (I_cR_n) product is explained by an inspecular transport in s_pm-wave pair potential.
  • Resonant inelastic x-ray scattering (RIXS) spectra at the Fe K-edge were measured for a single crystal of the iron oxypnictide superconductor PrFeAsO0.7 (Tc=42 K). They disclose a weak, broad feature centered around 4.5 eV energy loss, which is slightly resonantly enhanced when the incident energy is tuned in the vicinity of the 4p white line. We tentatively ascribe it to the charge-transfer excitation between As 4p and Fe 3d.
  • We have studied the lower critical fields H_{c1} of superconducting iron oxipnictide PrFeAsO_{1-y} single crystals for H parallel and perpendicular to the ab-planes. Measurements of the local magnetic induction at positions straddling the sample edge by using a miniature Hall-sensor array clearly resolve the first flux penetration from the Meissner state. The temperature dependence of H_{c1} for H || c is well scaled by the in-plane penetration depth without showing any unusual behavior, in contrast to previous reports. The anisotropy of penetration lengths at low temperatures is estimated to be ~ 2.5, which is much smaller than the anisotropy of the coherence lengths. This is indicative of multiband superconductivity in this system, in which the active band for superconductivity is more anisotropic. We also point out that the local induction measured at a position near the center of the crystal, which has been used in a number of reports for the determination of H_{c1}, might seriously overestimate the obtained H_{c1}-value.
  • In-plane microwave penetration depth $\lambda_{ab}$ and quaiparticle conductivity at 28 GHz are measured in underdoped single crystals of the Fe-based superconductor PrFeAsO$_{1-y}$ ($T_c\approx 35$ K) by using a sensitive superconducting cavity resonator. $\lambda_{ab}(T)$ shows flat dependence at low temperatures, which is incompatible with the presence of nodes in the superconducting gap $\Delta({\bf k})$. The temperature dependence of the superfluid density demonstrates that the gap is non-zero ($\Delta/k_BT_c\gtrsim 1.6$) all over the Fermi surface. The microwave conductivity below $T_c$ exhibits an enhancement larger than the coherence peak, reminiscent of high-$T_c$ cuprate superconductors.
  • The lattice dynamics of LaFeAsO_{1-x}F_{x} (x=0, 0.1) and PrFeAsO_{1-y} (y~0.1) are investigated using inelastic x-ray scattering and ab-initio calculation. Measurements of powder samples provide an approximation to the phonon DOS, while dispersion is measured from a single crystal of PrFeAsO_{1-y}. A model that agrees reasonably well with all of the data at room temperature is built from results of ab-initio calculations by softening the strength of the Fe-As bond by 30%.
  • The finite size effects of the nanoparticles to the atomic pair distribution functions (PDF) are discussed by calculating the radial distribution functions (RDF) on nanoparticles with various shapes, such as sheet, belt, rod, tube and sphere, assuming continua. Their characteristics are shown depending on the shapes and the sizes of the nanoparticles. Alternately, these PDFs can be used to measure the shapes and the sizes of ordered lattice part inside of any materials such as nanoparticles and bulks.