• The solid solution Eu(Ga_1-xAl_x)_4 was grown in single crystal form to reveal a rich variety of crystallographic, magnetic, and electronic properties that differ from the isostructural end compounds EuGa_4 and EuAl_4, despite the similar covalent radii and electronic configurations of Ga and Al. Here we report the onset of magnetic spin reorientation and metamagnetic transitions for x = 0 - 1 evidenced by magnetization and temperature-dependent specific heat measurements. T_N changes non-monotonously with x, and it reaches a maximum around 20 K for x = 0.50, where the a lattice parameter also shows an extreme (minimum) value. Anomalies in the temperature-dependent resistivity consistent with charge density wave behavior exist for x = 0.50 and 1 only. Density functional theory calculations show increased polarization between the Ga-Al covalent bonds in the x = 0.50 structure compared to the end compounds, such that crystallographic order and chemical pressure are proposed as the causes of the charge density wave behavior.
  • We describe the synthesis, materials characterization and dynamic nuclear polarization (DNP) of amorphous and crystalline silicon nanoparticles for use as hyperpolarized magnetic resonance imaging (MRI) agents. The particles were synthesized by means of a metathesis reaction between sodium silicide (Na4Si4) and silicon tetrachloride (SiCl4) and were surface functionalized with a variety of passivating ligands. The synthesis scheme results in particles of diameter ~10 nm with long size-adjusted 29Si spin lattice relaxation (T1) times (> 600 s), which are retained after hyperpolarization by low temperature DNP.
  • Currently, magnetic iron oxide nanoparticles are the only nano-sized magnetic resonance imaging (MRI) contrast agents approved for clinical use, yet commercial manufacturing of these agents has been limited or discontinued. Though there is still widespread demand for these particles both for clinical use and research, they are difficult to obtain commercially, and complicated syntheses make in-house preparation infeasible for most biological research labs or clinics. To make commercial production viable and increase accessibility of these products, it is crucial to develop simple, rapid, and reproducible preparations of biocompatible iron oxide nanoparticles. Here, we report a rapid, straightforward microwave-assisted synthesis of superparamagnetic dextran-coated iron oxide nanoparticles. The nanoparticles were produced in two hydrodynamic sizes with differing core morphologies by varying the synthetic method as either a two-step or single step process. A striking benefit of these methods is the ability to obtain swift and consistent results without the necessity for air, pH, or temperature sensitive techniques; therefore, reaction times and complex manufacturing processes are greatly reduced as compared to conventional synthetic methods. This is a great benefit for cost-effective translation to commercial production. The nanoparticles are found to be superparamagnetic and exhibit properties consistent for use in MRI. In addition, the dextran coating imparts the water-solubility and biocompatibility necessary for in vivo utilization.
  • Layered d-metal pnictide oxides are a unique class of compounds which consists of characteristic d-metal pnictide layers and metal oxide layers. More than 100 of these layered compounds, including the recently discovered Fe-based superconducting pnictide oxides, can be classified into 9 structure types. These structure types and the chemical and physical properties of the characteristic d-metal pnictide layers and metal oxide layers of the layered d-metal pnictide oxides are reviewed and discussed. Furthermore, possible approaches to design new superconductors based on these layered d-metal pnictide oxides are proposed.
  • We have studied the intrinsic normal and superconducting properties of the oxypnictide LaFePO. These samples exhibit bulk superconductivity and the evidence suggests that stoichiometric LaFePO is indeed superconducting, in contrast to other reports. We find that superconductivity is independent of the interplane residual resistivity $\rho_0$ and discuss the implications of this on the nature of the superconducting order parameter. Finally we find that, unlike $T_c$, other properties in single-crystal LaFePO including the resistivity and magnetoresistance, can be very sensitive to disorder.
  • Fe/Au nanoparticles have been chemically synthesized through a reverse micelle reaction and investigated by both conventional and synchrotron based x-ray diffraction and by magnetic and Moessbauer spectral studies. The powder x-ray diffraction patterns reveal both the presence of crystalline alpha-iron and gold and the absence of any crystalline iron oxides or other crystalline products. First-order reversal curves, along with the major hysteresis loops of the Fe/Au nanoparticles have been measured as a function of time in order to investigate the evolution of their magnetic properties. The iron-57 Moessbauer spectra of both uncoated iron nanoparticles and the Fe/Au nanoparticles have been measured at 78 and 295 K and indicate that two major iron containing components are present, namely the expected alpha-iron and the unexpected amorphous Fe1-xBx alloy; several poorly crystallized ordered iron(III) oxide components as well as paramagnetic iron(II) and iron(III) components are also observed. These results indicate that the Fe-core/Au-shell nanoparticles synthesized through reverse micelles are far more complex that had been believed.
  • We report the chemical synthesis of Fe-core/Au-shell nanoparticles by a reverse micelle method, and the investigation of their growth mechanisms and oxidation-resistant characteristics. The core-shell structure and the presence of the Fe & Au phases have been confirmed by transmission electron microscopy, energy dispersive spectroscopy, X-ray diffraction, Mossbauer spectroscopy, and inductively coupled plasma techniques. Additionally, atomic-resolution Z-contrast imaging and electron energy loss spectroscopy (EELS) in a scanning transmission electron microscope (STEM) have been used to study details of the growth processes. The Au-shell grows by nucleating on the Fe-core surface before coalescing. The magnetic moments of such nanoparticles, in the loose powder form, decrease over time due to oxidation. The less than ideal oxidation-resistance of the Au shell may have been caused by the rough Au surfaces. However, in the pressed pellet form, electrical transport measurements show that the particles are fairly stable, as the resistance of the pellet does not change appreciably over time.
  • We present results from a Monte Carlo investigation of a simple bilayer model with geometrically frustrated interactions similar to those found in the mixed layer pnictide oxides $(Sr_{2}Mn_{3}Pn_{2}O_{2}, Pn=As,Sb).$ Our model is composed of two inequivalent square lattices with nearest neighbor intra- and interlayer interactions. We find a ground state composed of two independent N\'{e}el ordered layers when the interlayer exchange is an order of magnitude weaker than the intralayer exchange, as suggested by experiment. We observe this result independent of the number of layers in our model. We find evidence for local orthogonal order between the layers, but it occurs in regions of parameter space that are not experimentally realized. We conclude that frustration caused by nearest neighbor interactions in the mixed layer pnictide oxides is not sufficient to explain the long--range orthogonal order that is observed experimentally, and that it is likely that other terms (e.g., local anisotropies) in the Hamiltonian are required to explain the magnetic behavior.