• Stabilized FeSe thin films in ambient pressure with tunable superconductivity would be a promising candidate for superconducting electronic devices yet its superconducting transition temperature (Tc) is below 10 K in bulk materials. By carefully controlling the depositions on twelve kinds of substrates using pulsed laser deposition technique, high quality single crystalline FeSe samples were fabricated with full width of half maximum 0.515? in the rocking curve and clear four-fold symmetry in phi-scan from x-ray diractions. The films have a maximum Tc 15 K on the CaF2 substrate and do not show obvious decay in the air for more than half a year. Slightly tuning the stoichiometry of the FeSe targets, the Tc becomes adjustable from 15 to < 2 K with quite narrow transition widths less than 2 K, and shows a positive relation with the out-of-plane (c-axis) lattice parameter of the films. However, there is no clear relation between the Tc and the surface atomic distance of the substrates. By reducing the thickness of the films, the Tc decreases and fades away in samples of less than 10 nm, suggesting that the strain effect is not responsible for the enhancement of Tc in our experiments.
  • We report the success in introducing Mn into (Li1-xFex)OHFe1-ySe superconducting crystals by applying two different hydrothermal routes, ion exchange (1-Step) and ion release/introduction (2-Step). The micro-region x-ray diffraction and energy dispersive x-ray spectroscopy analyses indicate that the Mn has been doped into the lattice, and its content in the 1-Step fabricated sample is higher than that in the 2-Step one. Magnetic susceptibility and electric transport properties reveal that Mn doping influences little on the superconducting transition, regardless of 1-Step or 2-Step routes. By contrast, the characteristic temperature, T*, where the negative Hall coefficient reaches its minimum, is significantly reduced by Mn doping. This implies that the reduction of the hole carriers contribution is obviously modified, and hence the hole band might have no direct relationship with the superconductivity in (Li1-xFex)OHFe1-ySe superconductors. Our present hydrothermal methods of ion exchange and ion release/introduction provide an efficient way for elements substitution/doping into (Li1-xFex)OHFe1-ySe superconductors, which will promote the in-depth investigations on the role of multiple electron and hole bands and their interplay with the high-temperature superconductivity in the FeSe-based superconductors.