• ### Reinforcement of interfacial superconductivity in a Bi2Te3/Fe1+yTe heterostructure under hydrostatic pressure(1703.04291)

June 5, 2017 cond-mat.supr-con
We investigate the hydrostatic pressure dependence of interfacial superconductivity occurring at the atomically sharp interface between two non-superconducting materials: the topological insulator (TI) Bi2Te3 and the parent compound Fe1+yTe of the chalcogenide iron based superconductors. Under pressure, a significant increase in the superconducting transition temperature Tc is observed. We trace the pressure dependence of a superconducting twin gap structure by Andreev reflection point contact spectroscopy (PCARS), which shows that a large superconducting gap associated with the interfacial superconductivity increases along with Tc. A second smaller gap, which is attributed to proximity-induced superconductivity in the TI layer, increases first, but then reaches a maximum and appears to be gradually suppressed at higher pressure. We interpret our data in the context of a pressure-induced doping effect of the interface, in which charge is transferred from the TI layer to the interface and the interfacial superconductivity is enhanced. This demonstrates the important role of the TI in the interfacial superconductivity mechanism.
• ### Highly responsive ground state of PbTaSe$_2$: structural phase transition and evolution of superconductivity under pressure(1702.00258)

Feb. 1, 2017 cond-mat.supr-con
Transport and magnetic studies of PbTaSe$_2$ under pressure suggest existence of two superconducting phases with the low temperature phase boundary at $\sim 0.25$ GPa that is defined by a very sharp, first order, phase transition. The first order phase transition line can be followed via pressure dependent resistivity measurements, and is found to be near 0.12 GPa near room temperature. Transmission electron microscopy and x-ray diffraction at elevated temperatures confirm that this first order phase transition is structural and occurs at ambient pressure near $\sim 425$ K. The new, high temperature / high pressure phase has a similar crystal structure and slightly lower unit cell volume relative to the ambient pressure, room temperature structure. Based on first-principles calculations this structure is suggested to be obtained by shifting the Pb atoms from the $1a$ to $1e$ Wyckoff position without changing the positions of Ta and Se atoms. PbTaSe$_2$ has an exceptionally pressure sensitive, structural phase transition with $\Delta T_s/\Delta P \approx - 1700$ K/GPa near 4 K, this first order transition causes an $\sim 1$ K ($\sim 25 \%$) step - like decrease in $T_c$ as pressure is increased through 0.25 GPa.