• We report the first experimental results of the magnetoresistance, Hall effect, and quantum Shubnikov-de Haas oscillations on single crystals of ZrTe, which was recently predicted to be a new type of topological semimetal hosting both triply degenerate crossing points and Weyl fermion state. The analysis of Hall effect and quantum oscillations indicate that ZrTe is a multiband system with low carrier density, high carrier mobility, small cross-sectional area of Fermi surface, and light cyclotron effective mass, as observed in many topological semimetals. Meanwhile, the angular dependence of the magnetoresistance and the quantum-oscillation frequencies further suggest that ZrTe possesses a three-dimensional Fermi surface that is rather complex. Our results provide a new platform to realize exotic quantum phenomena related to the new three-component fermions distinct from Dirac and Weyl fermions.
  • We report the magnetoresistance (MR), Hall effect, and de Haas-van Alphen (dHvA) effect studies of the single crystals of tungsten carbide, WC, which is predicted to be a new type of topological semimetal with triply degenerate nodes. With the magnetic field rotated in the plane perpendicular to the current, WC shows field induced metal to insulator like transition and large nonsaturating quadratic MR at low temperature. As the magnetic field parallel to the current, a pronounced negative longitudinal MR only can be observed when the current flows along the certain direction. Hall effect indicates WC is a perfect compensated semimetal, which may be related to the large nonsaturating quadratic MR. The analysis of dHvA oscillations reveals that WC is a multiband system with small cross-sectional areas of Fermi surface and light cyclotron effective masses. Our results indicate that WC is an ideal platform to study the recently proposed New Fermions with triply degenerate crossing points.
  • We have investigated the magnetoresistance (MR) and Hall resistivity properties of the single crystals of tantalum sulfide, Ta3S2, which was recently predicted to be a new type II Weyl semimetal. Large MR (up to ~8000% at 2 K and 16 T), field-induced metal-insulator-like transition and nonlinear Hall resistivity are observed at low temperatures. The large MR shows a strong dependence on the field orientation, leading to a giant anisotropic magnetoresistance (AMR) effect. For the field applied along the b-axis (B//b), MR exhibits quadratic field dependence at low fields and tends towards saturation at high fields; while for B//a, MR presents quadratic field dependence at low fields and becomes linear at high fields without any trend towards saturation. The analysis of the Hall resistivity data indicates the coexistence of a large number of electrons with low mobility and a small number of holes with high mobility. Shubnikov-de Haas (SdH) oscillation analysis reveals three fundamental frequencies originated from the three-dimensional (3D) Fermi surface (FS) pockets. We find that the semi-classical multiband model is sufficient to account for the experimentally observed MR in Ta3S2.
  • There is a long-standing confusion concerning the physical origin of the anomalous resistivity peak in transition metal pentatelluride HfTe5. Several mechanisms, like the formation of charge density wave or polaron, have been proposed, but so far no conclusive evidence has been presented. In this work, we investigate the unusual temperature dependence of magneto-transport properties in HfTe5. We find that a three dimensional topological Dirac semimetal state emerges only at around Tp (at which the resistivity shows a pronounced peak), as manifested by a large negative magnetoresistance. This accidental Dirac semimetal state mediates the topological quantum phase transition between the two distinct weak and strong topological insulator phases in HfTe5. Our work not only provides the first evidence of a temperature-induced critical topological phase transition in HfTe5, but also gives a reasonable explanation on the long-lasting question.
  • The interplay between magnetism and superconductivity is one of the dominant themes in the study of unconventional superconductors, such as high-Tc cuprates, iron pnictides and heavy fermions. In such systems, the same d- or f-electrons tend to form magnetically ordered states and participate in building up a high density of states at the Fermi level, which is responsible for the superconductivity. Charge-density-wave (CDW) is another fascinating collective quantum phenomenon in some low dimensional materials, like the prototypical transition-metal poly-chalcogenides, in which CDW instability is frequently found to accompany with superconducting transition at low temperatures. Remarkably, similar to the antiferromagnetic superconductors, superconductivity can also be achieved upon suppression of CDW order via chemical doping or applied pressure in 1T-TiSe2. However, in these CDW superconductors, the two ground states are believed to occur in different parts of Fermi surface (FS) sheets, derived mainly from chalcogen p-states and transition metal d-states, respectively. The origin of superconductivity and its interplay with CDW instability has not yet been unambiguously determined. Here we report on the discovery of bulk superconductivity in Pd-intercalated CDW RETen (RE=rare earth; n=2.5, 3) compounds, which belong to a large family of rare-earth poly-chalcogenides with CDW instability usually developing in the planar square nets of tellurium at remarkably high transition temperature and the electronic properties are also dominated by chalcogen p-orbitals. Our study demonstrates that the intercalation of palladium leads to the suppression of the CDW order and the emergence of the superconductivity. Our finding could provide an ideal model system for comprehensive studies of the interplay between CDW and superconductivity.
  • A series of polycrystalline SmFeAs1-xOx bulks was prepared to systematically investigate the influence of sample density on flux pinning properties. Different sample densities were achieved by controlling the pelletizing pressure. The superconducting volume fraction, the critical current densities Jcm and the flux pinning force densities Fp were estimated from the magnetization measurements. Experimental results manifest that: (1) the superconducting volume fraction decreases with the decreasing of sample density. (2) The Jcm values have the similar trend except for the sample with very high density may due to different connectivity and pinning mechanism. Moreover, The Jcm(B) curve develops a peak effect at approximately the same field at which the high-density sample shows a kink. (3) The Fp(B) curve of the high-density sample shows a low-field peak and a high-field peak at several temperatures, which can be explained by improved intergranular current, while only one peak can be observed in Fp(B) of the low-density samples. Based on the scaling behaviour of flux pinning force densities, the main intragranular pinning is normal point pinning.
  • Temperature dependent resistivity of the iron-based superconductor NdFeAsO0.88F0.12 was measured under different applied fields and excitation currents. Arrhenius plot shows an anomalous tail effect, which contains obvious two resistivity dropping stages. The first is caused by the normal superconducting transition, and the second is supposed to be related to the weak-link between the grains. A model for the resistivity dropping related to the weak-link behavior is proposed, which is based on the Josephson junctions formed by the impurities in grain boundaries like FeAs, Sm2O3 and cracks together with the adjacent grains. These Josephson junctions can be easily broken by the applied fields and the excitations currents, leading to the anomalous resistivity tail in many polycrystalline iron-based superconductors. The calculated resistivity dropping agrees well with the experimental data, which manifests the correctness of the explanation of the obtained anomalous tail effect.
  • High-quality polycrystalline SmFeAsO0.75 was synthesized with a superconducting transition width less than 1 K, and the electronic behavior was systematically studied by transport and specific heat measurements. An obvious superconducting jump was witnessed, together with a very small normalized superconducting jump, which is much smaller than expected by the BCS theory. A strong temperature dependent Hall coefficient was found and attributed to the partial gapping of the Fermi surface up to the temperature of 160 K which was predicted and supported by the emergence of the pseudogap. The charge-carrier density as well as the effective mass were also obtained and discussed in detail.
  • We present extensive 75As NMR and NQR data on the superconducting arsenides PrFeAs0.89F0.11 (Tc=45 K), LaFeAsO0.92F0.08 (Tc=27 K), LiFeAs (Tc = 17 K) and Ba0.72K0.28Fe2As2 (Tc = 31.5 K) single crystal, and compare with the nickel analog LaNiAsO0.9F0.1 (Tc=4.0 K) . In contrast to LaNiAsO0.9F0.1 where the superconducting gap is shown to be isotropic, the spin lattice relaxation rate 1/T1 in the Fe-arsenides decreases below Tc with no coherence peak and shows a step-wise variation at low temperatures. The Knight shift decreases below Tc and shows a step-wise T variation as well. These results indicate spinsinglet superconductivity with multiple gaps in the Fe-arsenides. The Fe antiferromagnetic spin fluctuations are anisotropic and weaker compared to underdoped copper-oxides or cobalt-oxide superconductors, while there is no significant electron correlations in LaNiAsO0.9F0.1. We will discuss the implications of these results and highlight the importance of the Fermi surface topology.
  • Both DC and AC magnetization measurements were performed on the NdFeAsO0.88F0.12 superconductor to investigate the influence of magnetism on the superconducting properties of this system. The crossover of the ZFC and FC magnetic susceptibility curves under 7.5KOe was observed. The imaginary component of the first harmonics of the AC magnetic susceptibility, increases with the increasing DC field below 10K and shows frequency dependency under 7.5KOe at low temperature. The paramagnetism of Nd3+ ions tilts the magnetic hysteresis loops and broadens the hysteresis width. After correction for the paramagnetism, the field and temperature dependence of intrinsic Jcm was obtained and compared with the experimentally obtained total Jcm. The origin of the abnormal behavior of magnetization was investigated and attributed to a magnetic background, which was speculated to be caused by the spin-glass state. However, this magnetic background does not affect the flux pinning properties in this sample. The related mechanism was discussed.
  • We report a direct current transport study of the local intergrain connections in a polycrystalline SmFeAsO0.85 (Sm1111) bulk, for which we earlier estimated significant intergranular critical current density Jc. Our combined low temperature laser scanning microscopy (LTLSM) and scanning electron microscopy observations revealed only few grain-to-grain transport current paths, most of which switched off when a magnetic field was applied. These regions typically occur where current crosses Fe-As, which is a normal-metal wetting-phase that surrounds Sm1111 grains, producing a dense array of superconducting-normal-superconducting contacts. Our study points out the need to reduce the amount of grain boundary-wetting Fe-As phase, as well as the crack density within pnictide grains, as these defects produce a multiply connected current-blocking network.
  • Using x-ray absorption and resonant inelastic x-ray scattering, charge dynamics at and near the Fe $L$ edges is investigated in Fe pnictide materials, and contrasted to that measured in other Fe compounds. It is shown that the XAS and RIXS spectra for 122 and 1111 Fe pnictides are each qualitatively similar to Fe metal. Cluster diagonalization, multiplet, and density-functional calculations show that Coulomb correlations are much smaller than in the cuprates, highlighting the role of Fe metallicity and strong covalency in these materials. Best agreement with experiment is obtained using Hubbard parameters $U\lesssim 2$eV and $J\approx 0.8$eV.
  • Thermally activated flux flow and vortex glass transition of recently discovered SmFeAsO$_{0.9}$F$_{0.1}$ superconductor are studied in magnetic fields up to 9.0 T. The thermally activated energy is analyzed in two analytic methods, of which one is conventional and generally used, while the other is closer to the theoretical description. The thermally activated energy values determined from both methods are discussed and compared. In addition, several critical magnetic fields determined from resistivity measurements are presented and discussed.
  • In order to understand why the inter- and intra-granular current densities of polycrystalline superconducting oxypnictides differ by three orders of magnitude, we have conducted combined magneto-optical and microstructural examinations of representative randomly oriented polycrystalline Nd and Sm single-layer oxypnictides. Magneto optical images show that the highest Jc values are observed within single grains oriented with their c axes perpendicular to the observation plane, implying that the intragranular current is anisotropic. The much lower intergranular Jc is at least partially due to many extrinsic factors, because cracks and a ubiquitous wetting As-Fe phase are found at many grain boundaries. However, some grain boundaries are structurally clean under high resolution transmission electron microscopy examination. Because the whole-sample global Jc(5K) values of the two samples examined are 1000-4000 A/cm2, some 10-40 times that found in random, polycrystalline YBa2Cu3O7-x, it appears that the dominant obstruction to intergranular current flow of many present samples is extrinsic, though some intrinsic limitation of current flow across grain boundaries cannot yet be ruled out.
  • We use powder neutron diffraction to study the spin and lattice structures of polycrystalline samples of nonsuperconducting PrFeAsO and superconducting PrFeAsO0.85F0.15 and PrFeAsO0.85. We find that PrFeAsO exhibits an abrupt structural phase transitions at 153 K, followed by static long range antiferromagnetic order at 127 K. Both the structural distortion and magnetic order are identical to other rare-earth oxypnictides. Electron-doping the system with either Fluorine or oxygen deficiency suppresses the structural distortion and static long range antiferromagnetic order, therefore placing these materials into the same class of FeAs-based superconductors.
  • Early studies have found quasi-reversible magnetization curves in polycrystalline bulk rare-earth iron oxypnictides that suggest either wide-spread obstacles to intergranular current or very weak vortex pinning. In the present study of polycrystalline samarium and neodymium rare-earth iron oxypnictide samples made by high pressure synthesis, the hysteretic magnetization is significantly enhanced. Magneto optical imaging and study of the field dependence of the remanent magnetization as a function of particle size both show that global currents over the whole sample do exist but that the intergranular and intragranular current densities have distinctively different temperature dependences and differ in magnitude by about 1000. Assuming that the highest current density loops are restricted to circulation only within grains leads to values of ~5 MA/cm2 at 5 K and self field, while whole-sample current densities, though two orders of magnitude lower are 1000-10000 A/cm2, some two orders of magnitude higher than in random polycrystalline cuprates. We cannot yet be certain whether this large difference in global and intragrain current density is intrinsic to the oxypnictides or due to extrinsic barriers to current flow, because the samples contain significant second phase, some of which wets the grain boundaries and produces evidences of SNS proximity effect in the whole sample critical current.
  • High resolution photoemission measurements have been carried out on non-superconducting LaOFeAs parent compound and various superconducting R(O1-xFx)FeAs (R=La, Ce and Pr) compounds. We found that the parent LaOFeAs compound shows a metallic character. Through extensive measurements, we have identified several common features in the electronic structure of these Fe-based compounds: (1). 0.2 eV feature in the valence band; (2). A universal 13~16 meV feature; (3). A clear Fermi cutoff showing zero leading-edge shift in the superconducting state;(4). Lack of superconducting coherence peak(s); (5). Near EF spectral weight suppression with decreasing temperature. These universal features can provide important information about band structure, superconducting gap and pseudogap in these Fe-based materials.
  • High resolution photoemission measurements have been carried out on non-superconducting SmOFeAs parent compound and superconducting Sm(O$_{1-x}$F$_x$)FeAs (x=0.12, and 0.15) compounds. The momentum-integrated spectra exhibit a clear Fermi cutoff that shows little leading-edge shift in the superconducting state which suggests the Fermi surface sheet(s) around the $\Gamma$ point may not be gapped in this multiband superconductors. A robust feature at 13 meV is identified in all these samples. Spectral weight suppression near E$_F$ with decreasing temperature is observed in both undoped and doped samples that points to a possible existence of a pseudogap in these Fe-based compounds.
  • Magnetization measurements in the low field region have been carefully performed on a well-shaped cylindrical and an ellipsoidal sample of superconductor $MgCNi_3$. Data from both samples show almost the same results. The lower critical field $H_{c1}$ and the London penetration depth $\lambda$ are thus derived. It is found that the result of normalized superfluid density $\lambda^2(0)/\lambda^2(T)$ of $MgCNi_3$ can be well described by BCS prediction with the expectation for an isotropic s-wave superconductivity.
  • The mechanical relaxation spectra of a superconducting and a non-superconducting MgCNi3 samples were measured from liquid nitrogen temperature to room temperature at frequency of kilohertz. There are two internal friction peaks (at 300 K labeled as P1 and 125 K as P2) for the superconducting sample. For the non-superconducting one, the position of P1 shifts to 250 K, while P2 is almost completely depressed. It is found that the peak position of P2 shifts towards higher temperature under higher measuring frequency. The calculated activation energy is 0.13eV. We propose an explanation relating P2 to the carbon atom jumping among the off-center positions. And further we expect that the behaviors of carbon atoms maybe correspond to the normal state crossovers around 150 K and 50 K observed by many other experiments.
  • The effect of radiation-induced disordering in a nuclear reactor (fast neutrons fluence \Phi = 5\cdot10^{19} cm^2, T_{\text{irr}} = 340 K) on resistivity \rho, superconducting transition temperature T_C and upper critical field H_{C_2} of polycrystalline MgCNi_3 samples was investigated. It was found that T_C decreases under irradiation from 6.5 to 2.9 K and completely recovers after annealing at 600 ^\circC. Temperature dependences \rho(T) are characteristic of compounds with strong electron-phonon interaction. The dH_{C_2}/dT behaviour testifies to a considerable decrease in density of electronic state at Fermi level N(E_F) in the course of disordering.
  • The structural properties of MgB2 superconductors have been analyzed by means of convergent-beam electron diffraction, high-resolution transmission-electron microscopy, and theoretical simulations. The MgB2 crystal has been identified to have a hexagonal structure with the space group of P6/mmm. Microstructural features of MgB6 materials depend evidently upon the synthesis pressures. Stacking faults and grain boundaries in a sample with the critical current density greater than 105A/cm2 have been extensively investigated.
  • Magnetic critical current density and relaxation rate have been measured on $MgB_2$ bulks from 1.6 K to $T_c$ at magnetic fields up to 8 Tesla. A vortex phase diagram is depicted based on these measurement. Two phase boundaries $H_{irr}^{bulk}(T)$ and $H_{irr}^{g}(T)$ characterizing different irreversible flux motions are found. The $H_{irr}^{bulk}(T)$ is characterized by the appearance of the linear resistivity and is attributed to quantum vortex melting induced by quantum fluctuation of vortices in the rather clean system. The second boundary $ H_{irr}^g(T) $ reflects the irreversible flux motion in some local regions due to either very strong pinning or the surface barrier on the tiny grains.
  • By using transport and magnetic measurement, the upper critical field $H_{c2}(T)$ and the irreversibility line $H_{irr}(T)$ has been determined. A big separation between $H_{c2}(0)$ and $H_{irr}(0)$ has been found showing the existence of a quantum vortex liquid state induced by quantum fluctuation of vortices in the new superconductor $MgB_2$. Further investigation on the magnetic relaxation shows that both the quantum tunneling and the thermally activated flux creep weakly depends on temperature. But when the melting field $H_{irr}$ is approached, a drastic rising of the relaxation rate is observed. This may imply that the melting of the vortex matter at a finite temperature is also induced by the quantum fluctuation of vortices.
  • The lower critical field $H_{c1}$ has been carefully measured on a well shaped cylindrical sample of the new superconductor $MgB_2$ fabricated by high pressure synthesis. The penetration depth $\lambda$ is calculated from the $H_{c1}$ data. It is found that a linear relation of $H_{c1}(T)$ appears in whole temperature region below $T_c$. Furthermore a finite slope of $dH_{c1}/dT$ and $d\lambda(T)/dT$ remains down to the lowest temperature (2 K). These are inconsistent with the expectation for a widely thought s-wave superconductivity in $MgB_2$.