• The interplay between superconductivity and charge density waves (CDW) in $H$-NbSe2 is not fully understood despite decades of study. Artificially introduced disorder can tip the delicate balance between two competing forms of long-range order, and reveal the underlying interactions that give rise to them. Here we introduce disorders by electron irradiation and measure in-plane resistivity, Hall resistivity, X-ray scattering, and London penetration depth. With increasing disorder, $T_{\textrm{c}}$ varies nonmonotonically, whereas $T_{\textrm{CDW}}$ monotonically decreases and becomes unresolvable above a critical irradiation dose where $T_{\textrm{c}}$ drops sharply. Our results imply that CDW order initially competes with superconductivity, but eventually assists it. We argue that at the transition where the long-range CDW order disappears, the cooperation with superconductivity is dramatically suppressed. X-ray scattering and Hall resistivity measurements reveal that the short-range CDW survives above the transition. Superconductivity persists to much higher dose levels, consistent with fully gapped superconductivity and moderate interband pairing.
  • The microscopic details of the suppression of antiferromagnetic order in the Kondo-lattice series Ce$_{1-x}$La$_{x}$Cu$_{2}$Ge$_{2}$ due to nonmagnetic dilution by La are revealed through neutron diffraction results for $x=0.20$, $0.40$, $0.75$, and $0.85$. Magnetic Bragg peaks are found for $0.20\le x\le0.75$, and both the N\'{e}el temperature, $T_{\textrm{N}}$, and the ordered magnetic moment per Ce, $\mu$, linearly decrease with increasing $x$. The reduction in $\mu$ points to strong hybridization of the increasingly diluted Ce $4f$ electrons, and we find a remarkable quadratic dependence of $\mu$ on the Kondo-coherence temperature. We discuss our results in terms of local-moment- versus itinerant-type magnetism and mean-field theory, and show that Ce$_{1-x}$La$_{x}$Cu$_{2}$Ge$_{2}$ provides an exceptional opportunity to quantitatively study competing magnetic interactions in a Kondo lattice.
  • Magnetism is widely considered to be a key ingredient of unconventional superconductivity. In contrast to cuprate high-temperature superconductors, antiferromagnetism in Fe-based superconductors (FeSCs) is characterized by a pair of magnetic propagation vectors. Consequently, three different types of magnetic order are possible. Of theses, only stripe-type spin-density wave (SSDW) and spin-charge-density wave (SCDW) orders have been observed. A realization of the proposed spin-vortex crystal (SVC) order is noticeably absent. We report a magnetic phase consistent with the hedgehog variation of SVC order in Ni- and Co-doped CaKFe4As4 based on thermodynamic, transport, structural and local magnetic probes combined with symmetry analysis. The exotic SVC phase is stabilized by the reduced symmetry of the CaKFe4As4 structure. Our results suggest that the possible magnetic ground states in FeSCs have very similar energies, providing an enlarged configuration space for magnetic fluctuations to promote high-temperature superconductivity.
  • Neutron diffraction and magnetic susceptibility studies of a polycrystalline SrCr$_2$As$_2$ sample reveal that this compound is an itinerant G-type antiferromagnet below the N${\rm \acute{e}}$el temperature $T_{\textrm N}$ = 590(5) K with the Cr magnetic moments aligned along the tetragonal $c$ axis. The system remains tetragonal to the lowest measured temperature ($\sim$12 K). The lattice parameter ratio $c/a$ and the magnetic moment saturate at about the same temperature below $\sim$ 200 K, indicating a possible magnetoelastic coupling. The ordered moment, $\mu=1.9(1)~\mu_{\rm B}$/Cr, measured at $T = 12$ K, is significantly reduced compared to its localized value ($4~\mu_{\rm B}$/Cr) due to the itinerant character brought about by the hybridization between the Cr $3d$ and As $4p$ orbitals.
  • Magnetization, neutron diffraction, and high-energy x-ray diffraction results for Sn-flux grown single-crystal samples of Ca(Co$_{1-x}$Fe$_{x}$)$_{y}$As$_{2}$, $0\leq x\leq1$, $1.86\leq y \leq 2$, are presented and reveal that A-type antiferromagnetic order, with ordered moments lying along the $c$ axis, persists for $x\lesssim0.12(1)$. The antiferromagnetic order is smoothly suppressed with increasing $x$, with both the ordered moment and N\'{e}el temperature linearly decreasing. Stripe-type antiferromagnetic order does not occur for $x\leq0.25$, nor does ferromagnetic order for $x$ up to at least $x=0.104$, and a smooth crossover from the collapsed-tetragonal (cT) phase of CaCo$_{1.86}$As$_{2}$ to the tetragonal (T) phase of CaFe$_{2}$As$_{2}$ occurs. These results suggest that hole doping CaCo$_{1.86}$As$_{2}$ has a less dramatic effect on the magnetism and structure than steric effects due to substituting Sr for Ca.
  • BaMn$_{2}$As$_{2}$ is an antiferromagnetic insulator where a metal-insulator transition occurs with hole doping via the substitution of Ba with K. The metal-insulator transition causes only a small suppression of the N\'eel temperature ($T_\mathrm{N}$) and the ordered moment, suggesting that doped holes interact weakly with the Mn spin system. Powder inelastic neutron scattering measurements were performed on three different powder samples of Ba$_{1-x}$K$_{x}$Mn$_{2}$As$_{2}$ with $x=$0, 0.125 and 0.25 to study the effect of hole doping and metallization on the spin dynamics of these compounds. We compare the neutron intensities to a linear spin wave theory approximation to the $J_{1}-J_{2}-J_{c}$ Heisenberg model. Hole doping is found to introduce only minor modifications to the exchange energies and spin gap. The changes observed in the exchange constants are consistent with the small drop of $T_\mathrm{N}$ with doping.
  • We study the effect of applied strain as a physical control parameter for the phase transitions of Ca(Fe1-xCox)2As2 using resistivity, magnetization, x-ray diffraction and 57Fe M\"ossbauer spectroscopy. Biaxial strain, namely compression of the basal plane of the tetragonal unit cell, is created through firm bonding of samples to a rigid substrate, via differential thermal expansion. This strain is shown to induce a magneto-structural phase transition in originally paramagnetic samples; and superconductivity in previously non-superconducting ones. The magneto-structural transition is gradual as a consequence of using strain instead of pressure or stress as a tuning parameter.
  • Single crystalline, single phase CaKFe$_{4}$As$_{4}$ has been grown out of a high temperature, quaternary melt. Temperature dependent measurements of x-ray diffraction, anisotropic electrical resistivity, elastoresistivity, thermoelectric power, Hall effect, magnetization and specific heat, combined with field dependent measurements of electrical resistivity and field and pressure dependent measurements of magnetization indicate that CaKFe$_{4}$As$_{4}$ is an ordered, stoichiometric, Fe-based superconductor with a superconducting critical temperature, $T_c$ = 35.0 $\pm$ 0.2 K. Other than superconductivity, there is no indication of any other phase transition for 1.8 K $\leq T \leq$ 300 K. All of these thermodynamic and transport data reveal striking similarities to that found for optimally- or slightly over-doped (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$, suggesting that stoichiometric CaKFe$_4$As$_4$ is intrinsically close to what is referred to as "optimal-doped" on a generalized, Fe-based superconductor, phase diagram. The anisotropic superconducting upper critical field, $H_{c\text{2}}(T)$, of CaKFe$_{4}$As$_{4}$ was determined up to 630 kOe. The anisotropy parameter $\gamma(T)=H_{c\text{2}}^{\perp}/H_{c\text{2}}^{\|}$, for $H$ applied perpendicular and parallel to the c-axis, decreases from $\simeq 2.5$ at $T_c$ to $\simeq 1.5$ at 25 K which can be explained by interplay of paramagnetic pairbreaking and orbital effects. The slopes of $dH_{c\text{2}}^{\|}/dT\simeq-44$ kOe/K and $dH_{c\text{2}}^{\perp}/dT \simeq-109$ kOe/K at $T_c$ yield an electron mass anisotropy of $m_{\perp}/m_{\|}\simeq 1/6$ and short Ginzburg-Landau coherence lengths $\xi_{\|}(0)\simeq 5.8 \text{\AA}$ and $\xi_{\perp}(0)\simeq 14.3 \text{\AA}$. The value of $H_{c\text{2}}^{\perp}(0)$ can be extrapolated to $\simeq 920$ kOe, well above the BCS paramagnetic limit.
  • Fe pnictides and related materials have been a topic of intense research for understanding the complex interplay between magnetism and superconductivity. Here we report on the magnetic structure of SrMn$_{2}$As$_{2}$ that crystallizes in a trigonal structure ($P\bar{3}m1$) and undergoes an antiferromagnetic (AFM) transition at $T_{\textrm c}$ $= 118(2)$ K. The magnetic susceptibility remains nearly constant at temperatures $T \le T_{\textrm N}$ with $\textbf{H}\parallel \textbf{c}$ whereas it decreases significantly with $\textbf{H}\parallel \textbf{ab}$. This shows that the ordered Mn moments lie in the $\textbf{ab}$-plane instead of aligning along the $\textbf{c}$-axis as in tetragonal BaMn$_{2}$As$_{2}$. Single-crystal neutron diffraction measurements on SrMn$_{2}$As$_{2}$ demonstrate that the Mn moments are ordered in a collinear N\'{e}el AFM phase with $180^\circ$ AFM alignment between a moment and all nearest neighbor moments in the basal plane and also perpendicular to it. Moreover, quasi-two-dimensional AFM order is manifested in SrMn$_{2}$As$_{2}$ as evident from the temperature dependence of the order parameter.
  • A hallmark of the iron-based superconductors is the strong coupling between magnetic, structural and electronic degrees of freedom. However, a universal picture of the normal state properties of these compounds has been confounded by recent investigations of FeSe where the nematic (structural) and magnetic transitions appear to be decoupled. Here, using synchrotron-based high-energy x-ray diffraction and time-domain Moessbauer spectroscopy, we show that nematicity and magnetism in FeSe under applied pressure are indeed strongly coupled. Distinct structural and magnetic transitions are observed for pressures, 1.0 GPa <= p <= 1.7 GPa, which merge into a single first-order phase line for p >= 1.7 GPa, reminiscent of what has been observed, both experimentally and theoretically, for the evolution of these transitions in the prototypical doped system, Ba(Fe[1-x]Co[x])2As2. Our results support a spin-driven mechanism for nematic order in FeSe and provide an important step towards a universal description of the normal state properties of the iron-based superconductors.
  • We use Angle Resolved Photoemission Spectroscopy (ARPES), Raman spectroscopy, Low Energy Electron Diffraction (LEED) and x-ray scattering to reveal an unusual electronically mediated charge density wave (CDW) in K0.9Mo6O17. Not only does K0.9Mo6O17 lack signatures of electron-phonon coupling, but it also hosts an extraordinary surface CDW, with TS CDW =220 K nearly twice that of the bulk CDW, TB CDW =115 K. While the bulk CDW has a BCS-like gap of 12 meV, the surface gap is ten times larger and well in the strong coupling regime. Strong coupling behavior combined with the absence of signatures of strong electron-phonon coupling indicates that the CDW is likely mediated by electronic interactions enhanced by low dimensionality.
  • YbBiPt is a heavy-fermion compound possessing significant short-range antiferromagnetic correlations below a temperature of $T^{\textrm{*}}=0.7$ K, fragile antiferromagnetic order below $T_{\rm{N}}=0.4$ K, a Kondo temperature of $T_{\textrm{K}} \approx1$ K, and crystalline-electric-field splitting on the order of $E/k_{\textrm{B}}=1\,\textrm{-}\,10$ K. Whereas the compound has a face-centered-cubic lattice at ambient temperature, certain experimental data, particularly those from studies aimed at determining its crystalline-electric-field scheme, suggest that the lattice distorts at lower temperature. Here, we present results from high-resolution, high-energy x-ray diffraction experiments which show that, within our experimental resolution of $\approx6\,\textrm{-}\,10\times10^{-5}$ \AA, no structural phase transition occurs between $T=1.5$ and $50$ K. In combination with results from dilatometry measurements, we further show that the compound's thermal expansion has a minimum at $\approx18$ K and a region of negative thermal expansion for $9<T<18$ K. Despite diffraction patterns taken at $1.6$ K which indicate that the lattice is face-centered cubic and that the Yb resides on a crystallographic site with cubic point symmetry, we demonstrate that the linear thermal expansion may be modeled using crystalline-electric-field level schemes appropriate for Yb$^{3+}$ residing on a site with either cubic or less than cubic point symmetry.
  • We present the results of elastic and inelastic neutron scattering measurements on non-superconducting Ba(Fe${_{0.957}}$Cu${_{0.043}}$)${_2}$As${_2}$, a composition close to a quantum critical point between AFM ordered and paramagnetic phases. By comparing these results with the spin fluctuations in the low Cu composition as well as the parent compound BaFe$_2$As$_2$ and superconducting Ba(Fe$_{1-x}$Ni$_x$)$_2$As$_2$ compounds, we demonstrate that paramagnon-like spin fluctuations are evident in the antiferromagnetically ordered state of Ba(Fe$_{0.957}$Cu$_{0.043}$)$_2$As$_2$, which is distinct from the AFM-like spin fluctuations in the superconducting compounds. Our observations suggest that Cu substitution decouples the interaction between quasiparticles and the spin fluctuations. We also show that the spin-spin correlation length, ${\xi(T)}$, increases rapidly as the temperature is lowered and find ${\omega/T}$ scaling behavior, the hallmark of quantum criticality, at an antiferromagnetic quantum critical point.
  • We present high-energy x-ray diffraction data under applied pressures up to p = 29 GPa, neutron diffraction measurements up to p = 1.1 GPa, and electrical resistance measurements up to p = 5.9 GPa, on SrCo2As2. Our x-ray diffraction data demonstrate that there is a first-order transition between the tetragonal (T) and collapsed-tetragonal (cT) phases, with an onset above approximately 6 GPa at T = 7 K. The pressure for the onset of the cT phase and the range of coexistence between the T and cT phases appears to be nearly temperature independent. The compressibility along the a-axis is the same for the T and cT phases whereas, along the c-axis, the cT phase is significantly stiffer, which may be due to the formation of an As-As bond in the cT phase. Our resistivity measurements found no evidence of superconductivity in SrCo2As2 for p <= 5.9 GPa and T >= 1.8 K. The resistivity data also show signatures consistent with a pressure-induced phase transition for p >= 5.5 GPa. Single-crystal neutron diffraction measurements performed up to 1.1 GPa in the T phase found no evidence of stripe-type or A-type antiferromagnetic ordering down to 10 K. Spin-polarized total-energy calculations demonstrate that the cT phase is the stable phase at high pressure with a c/a ratio of 2.54. Furthermore, these calculations indicate that the cT phase of SrCo2As2 should manifest either A-type antiferromagnetic or ferromagnetic order.
  • X-ray magnetic circular dichroism (XMCD) measurements on single-crystal and powder samples of Ba$_{0.6}$K$_{0.4}$Mn$_{2}$As$_{2}$ show that the ferromagnetism below $T_{\textrm{C}}\approx$ 100 K arises in the As $4p$ conduction band. No XMCD signal is observed at the Mn x-ray absorption edges. Below $T_{\textrm{C}}$, however, a clear XMCD signal is found at the As $K$ edge which increases with decreasing temperature. The XMCD signal is absent in data taken with the beam directed parallel to the crystallographic $\textrm{c}$ axis indicating that the orbital magnetic moment lies in the basal plane of the tetragonal lattice. These results show that the previously reported itinerant ferromagnetism is associated with the As $4p$ conduction band and that distinct local-moment antiferromagnetism and itinerant ferromagnetism with perpendicular easy axes coexist in this compound at low temperature.
  • We use nuclear magnetic resonance (NMR), high-resolution x-ray and neutron scattering to study structural and magnetic phase transitions in phosphorus-doped BaFe$_2$(As$_{1-x}$P$_x$)$_2$. Previous transport, NMR, specific heat, and magnetic penetration depth measurements have provided compelling evidence for the presence of a quantum critical point (QCP) near optimal superconductivity at $x=0.3$. However, we show that the tetragonal-to-orthorhombic structural ($T_s$) and paramagnetic to antiferromagnetic (AF, $T_N$) transitions in BaFe$_2$(As$_{1-x}$P$_x$)$_2$ are always coupled and approach to $T_N\approx T_s \ge T_c$ ($\approx 29$ K) for $x=0.29$ before vanishing abruptly for $x\ge 0.3$. These results suggest that AF order in BaFe$_2$(As$_{1-x}$P$_x$)$_2$ disappears in a weakly first order fashion near optimal superconductivity, much like the electron-doped iron pnictides with an avoided QCP.
  • Neutron diffraction measurements on a single crystal of CeGe1.76 reveal a complex series of magnetic transitions at low temperature. At T_N = 7 K, there is a transition from a paramagnetic state at higher temperature to an incommensurate magnetic structure characterized by a magnetic propagation vector (0 0 tau) with tau approx. 1/4 and the magnetic moment along the a axis of the orthorhombic unit cell. Below T_LI = 5 K, the magnetic structure locks in to a commensurate structure with tau = 1/4 and the magnetic moment remains along the a axis. Below T* = 4 K, we find additional half-integer and integer indexed magnetic Bragg peaks consistent with a second commensurately ordered antiferromagnetic state.
  • Ca10(Pt3As8)(Fe2As2)5 is the parent compound for a class of Fe-based high-temperature superconductors where superconductivity with transition temperatures up to 30 K can be introduced by partial element substitution. We present a combined high-resolution high-energy x-ray diffraction and elastic neutron scattering study on a Ca10(Pt3As8)(Fe2As2)5 single crystal. This study reveals the microscopic nature of two distinct and continuous phase transitions to be very similar to other Fe-based high-temperature superconductors: an orthorhombic distortion of the high-temperature tetragonal Fe-As lattice below T_S = 110(2) K followed by stripe-like antiferromagnetic ordering of the Fe moments below T_N = 96(2) K. These findings demonstrate that major features of the Fe-based high-temperature superconductors are very robust against variations in chemical constitution as well as structural imperfection of the layers separating the Fe-As layers from each other and confirms that the Fe-As layers primarily determine the physics in this class of material.
  • The crystallographic and physical properties of polycrystalline and single crystal samples of BaCo2As2 and K-doped Ba{1-x}K{x}Co2As2 (x = 0.06, 0.22) are investigated by x-ray and neutron powder diffraction, magnetic susceptibility chi, magnetization, heat capacity Cp, {75}As NMR and electrical resistivity rho measurements versus temperature T. The crystals were grown using both Sn flux and CoAs self-flux, where the Sn-grown crystals contain 1.6-2.0 mol% Sn. All samples crystallize in the tetragonal ThCr2Si2-type structure (space group I4/mmm). For BaCo2As2, powder neutron diffraction data show that the c-axis lattice parameter exhibits anomalous negative thermal expansion from 10 to 300 K, whereas the a-axis lattice parameter and the unit cell volume show normal positive thermal expansion over this T range. No transitions in BaCo2As2 were found in this T range from any of the measurements. Below 40-50 K, we find rho ~ T^2 indicating a Fermi liquid ground state. A large density of states at the Fermi energy D(EF) ~ 18 states/(eV f.u.) for both spin directions is found from low-T Cp(T) measurements, whereas the band structure calculations give D(EF) = 8.23 states/(eV f.u.). The {75}As NMR shift data versus T have the same T dependence as the chi(T) data, demonstrating that the derived chi(T) data are intrinsic. The observed {75}As nuclear spin dynamics are consistent with the presence of ferromagnetic and/or stripe-type antiferromagnetic spin fluctuations. The crystals of Ba{0.78}K{0.22}Co2As2 were grown in Sn flux and show properties very similar to those of undoped BaCo2As2. On the other hand, the crystals from two batches of Ba{0.94}K{0.06}Co2As2 grown in CoAs self-flux show evidence of weak ferromagnetism at T < 10 K with small ordered moments at 1.8 K of 0.007 and 0.03 muB per formula unit, respectively.
  • Charge-density-wave (CDW) correlations within the quintessential CuO$_2$ planes have been argued to either cause [1] or compete with [2] the superconductivity in the cuprates, and they might furthermore drive the Fermi-surface reconstruction in high magnetic fields implied by quantum oscillation (QO) experiments for YBa$_2$Cu$_3$O$_{6+{\delta}}$ (YBCO) [3] and HgBa$_2$CuO$_{4+{\delta}}$ (Hg1201) [4]. Consequently, the observation of bulk CDW order in YBCO was a significant development [5,6,7]. Hg1201 features particularly high structural symmetry and recently has been demonstrated to exhibit Fermi-liquid charge transport in the relevant temperature-doping range of the phase diagram, whereas for YBCO and other cuprates this underlying property of the CuO$_2$ planes is partially or fully masked [8-10]. It therefore is imperative to establish if the pristine transport behavior of Hg1201 is compatible with CDW order. Here we investigate Hg1201 ($T_c$ = 72 K) via bulk Cu L-edge resonant X-ray scattering. We indeed observe CDW correlations in the absence of a magnetic field, although the correlations and competition with superconductivity are weaker than in YBCO. Interestingly, at the measured hole-doping level, both the short-range CDW and Fermi-liquid transport appear below the same temperature of about 200 K. Our result points to a unifying picture in which the CDW formation is preceded at the higher pseudogap temperature by $q$ = 0 magnetic order [11,12] and the build-up of significant dynamic antiferromagnetic correlations [13]. Furthermore, the smaller CDW modulation wave vector observed for Hg1201 is consistent with the larger electron pocket implied by both QO [4] and Hall-effect [14] measurements, which suggests that CDW correlations are indeed responsible for the low-temperature QO phenomenon.
  • Using inelastic neutron scattering, we show that the onset of superconductivity in underdoped Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$ coincides with a crossover from well-defined spin waves to overdamped and diffusive spin excitations. This crossover occurs despite the presence of long-range stripe antiferromagnetic order for samples in a compositional range from x=0.04-0.055, and is a consequence of the shrinking spin-density wave gap and a corresponding increase in the particle-hole (Landau) damping. The latter effect is captured by a simple itinerant model relating Co doping to changes in the hot spots of the Fermi surface. We argue that the overdamped spin fluctuations provide a pairing mechanism for superconductivity in these materials.
  • We report results from neutron scattering experiments on single crystals of YbBiPt that demonstrate antiferromagnetic order characterized by a propagation vector, $\tau_{\rm{AFM}}$ = ($\frac{1}{2} \frac{1}{2} \frac{1}{2}$), and ordered moments that align along the [1 1 1] direction of the cubic unit cell. We describe the scattering in terms of a two-Gaussian peak fit, which consists of a narrower component that appears below $T_{\rm{N}}~\approx 0.4$ K and corresponds to a magnetic correlation length of $\xi_{\rm{n}} \approx$ 80 $\rm{\AA}$, and a broad component that persists up to $T^*\approx$ 0.7 K and corresponds to antiferromagnetic correlations extending over $\xi_{\rm{b}} \approx$ 20 $\rm{\AA}$. Our results illustrate the fragile magnetic order present in YbBiPt and provide a path forward for microscopic investigations of the ground states and fluctuations associated with the purported quantum critical point in this heavy-fermion compound.
  • The relationship between antiferromagnetic spin fluctuations and superconductivity has become a central topic of research in studies of superconductivity in the iron pnictides. We present unambiguous evidence of the absence of magnetic fluctuations in the non-superconducting collapsed tetragonal phase of CaFe2As2 via inelastic neutron scattering time-of-flight data, which is consistent with the view that spin fluctuations are a necessary ingredient for unconventional superconductivity in the iron pnictides. We demonstrate that the collapsed tetragonal phase of CaFe2As2 is non-magnetic, and discuss this result in light of recent reports of high-temperature superconductivity in the collapsed tetragonal phase of closely related compounds.
  • Inelastic neutron scattering measurements of paramagnetic SrCo$_{2}$As$_{2}$ at T=5 K reveal antiferromagnetic (AFM) spin fluctuations that are peaked at a wavevector of $\textbf{Q}_{\mathrm{AFM}}=(1/2,1/2,1)$ and possess a large energy scale. These stripe spin fluctuations are similar to those found in $A$Fe$_{2}$As$_{2}$ compounds, where spin-density wave AFM is driven by Fermi surface nesting between electron and hole pockets separated by $\textbf{Q}_{\mathrm{AFM}}$. SrCo$_{2}$As$_{2}$ has a more complex Fermi surface and band structure calculations indicate a potential instability towards either a ferromagnetic or stripe AFM ground state. The results suggest that stripe AFM magnetism is a general feature of both iron and cobalt-based arsenides and the search for spin fluctuation-induced unconventional superconductivity should be expanded to include cobalt-based compounds.
  • Neutron and x-ray diffraction measurements are presented for powders and single crystals of CaCo{1.86}As2. The crystal structure is a collapsed-tetragonal ThCr2Si2-type structure as previously reported, but with 7(1)% vacancies on the Co sites corresponding to the composition CaCo{1.86(2)}As2. The thermal expansion coefficients for both the a- and c-axes are positive from 10 to 300 K. Neutron diffraction measurements on single crystals demonstrate the onset of A-type collinear antiferromagnetic order below the Neel temperature TN = 52(1) K with the ordered moments directed along the tetragonal c-axis, aligned ferromagnetically in the ab-plane and antiferromagnetically stacked along the c-axis.