• A quantum spin liquid with a $Z_2$ topological order has long been thought to be important for the application of quantum computing and may be related to high-temperature superconductivity. While a two-dimensional kagome antiferromagnet may host such a state, strong experimental evidences are still lacking. Here we show that the spin excitations from the kagome planes in magnetically ordered Cu$_4$(OD)$_6$FBr and non-magnetically ordered Cu$_3$Zn(OD)$_6$FBr are similarly gapped although the content of inter-kagome-layer Cu$^{2+}$ ions changes dramatically. This suggests that the spin triplet gap and continuum of the intrinsic kagome antiferromagnet are robust against the interlayer magnetic impurities. Our results show that the ground state of Cu$_3$Zn(OD)$_6$FBr is a gapped quantum spin liquid with Z$_2$ topological order.
  • Barlowite Cu$_4$(OH)$_6$FBr shows three dimensional (3D) long-range antiferromagnetism, which is fully suppressed in Cu$_3$Zn(OH)$_6$FBr with a kagome quantum spin liquid ground state. Here we report systematic studies on the evolution of magnetism in the Cu$_{4-x}$Zn$_x$(OH)$_{6}$FBr system, as a function of $x$, to bridge the two limits of Cu$_4$(OH)$_6$FBr ($x=0$) and Cu$_3$Zn(OH)$_6$FBr ($x=1$). Neutron diffraction measurements reveal a hexagonal-to-orthorhombic structural change with decreasing temperature in the $x$ = 0 sample. While confirming the 3D antiferromagnetic nature of low-temperature magnetism, the magnetic moments on some Cu$^{2+}$ sites in the kagome planes are found to be vanishingly small, suggesting strong frustration already exist in barlowite. Substitution of interlayer Cu$^{2+}$ with Zn$^{2+}$, with gradually increasing $x$, completely suppresses the bulk magnetic order at around $x$ = 0.4, but leaves a local, secondary magnetic order up to $x\sim 0.8$ with slight decrease of its transition temperature. The high-temperature magnetic susceptibility and specific heat measurements further suggest that the intrinsic magnetic properties of kagome spin liquid planes may already appear from $x>0.3$ samples. Our results therefore reveal that the Cu$_{4-x}$Zn$_x$(OH)$_6$FBr may be the long-thought experimental playground for the systematic investigations of the quantum phase transition from a long-range antiferromagnet to a topologically ordered quantum spin liquid.
  • We present neutron diffraction analysis of BaFe$_2$(As$_{1-x}$P$_x$)$_2$ over a wide temperature (10 to 300 K) and compositional ($0.11 \leq x \leq 0.79$) range, including the normal state, the magnetically ordered state, and the superconducting state. The paramagnetic to spin-density wave and orthorhombic to tetragonal transitions are first order and coincident within the sensitivity of our measurements ($\sim 0.5$ K). Extrapolation of the orthorhombic order parameter down to zero suggests that structural quantum criticality cannot exist at compositions higher than $x = 0.28$, which is much lower than values determined using other methods, but in good agreement with our observations of the actual phase stability range. The onset of spin-density wave order shows a stronger structural anomaly than the charge-doped system in the form of an enhancement of the $c/a$ ratio below the transition.
  • We use neutron scattering, to study magnetic excitations in crystals near the ideal superconducting composition of FeTe$_{0.5}$Se$_{0.5}$. Two types of excitations are found, a resonance at (0.5, 0.5, 0) and incommensurate fluctuations on either side of this position. We show that the two sets of magnetic excitations behave differently with doping, with the resonance being fixed in position while the incommensurate excitations move as the doping is changed. These unusual results show that a common behavior of the low energy magnetic excitations is not necessary for pairing in these materials.