• The physical properties of the spinel LiGaCr4S8 have been studied with neutron diffraction, X-ray diffraction, magnetic susceptibility and heat capacity measurements. The neutron diffraction and synchrotron X-ray diffraction data reveal negative thermal expansion (NTE) below 111(4) K. The magnetic susceptibility deviates from Curie-Weiss behavior with the onset of NTE. At low temperature a broad peak in the magnetic susceptibility at 10.3(3) K is accompanied by the return of normal thermal expansion. First principles calculations find a strong coupling between the lattice and the simulated magnetic ground state. These results indicate strong magnetoelastic coupling in LiGaCr4S8.
  • Prior to the superconducting transition at Tc = 2.3 K, Mo3Sb7 undergoes a symmetry-lowering, cubic-to-tetragonal structural transition at Ts = 53 K. We have monitored the pressure dependence of these two transitions by measuring the resistivity of Mo3Sb7 single crystals under various hydrostatic pressures up to 15 GPa. The application of external pressure enhances Tc but suppresses Ts until Pc ~ 10 GPa, above which a pressure-induced first order structural transition takes place and is manifested by the phase coexistence in the pressure range 8 < P < 12 GPa. The cubic phase above 12 GPa is also found to be superconducting with a higher Tc =6 K that decreases slightly with further increasing pressure. The variations with pressure of Tc and Ts satisfy the Bilbro-McMillan equation, i.e. Tc^nTs^(1-n) = constant, thus suggesting the competition of superconductivity with the structural transition that has been proposed to be accompanied with a spin-gap formation at Ts. This scenario is supported by our first-principles calculations which imply the plausible importance of magnetism that competes with the superconductivity in Mo3Sb7.
  • The structural and the magnetic properties of CeCu$_{6-x}$Ag$_x$ (0 $\leq$ $x$ $\leq$ 0.85) and CeCu$_{6-x}$Pd$_x$ (0 $\leq$ $x$ $\leq$ 0.4) have been studied using neutron diffraction, resonant ultrasound spectroscopy (RUS), heat capacity, x-ray diffraction measurements and first principles calculations. The structural and magnetic phase diagrams of CeCu$_{6-x}$Ag$_x$ and CeCu$_{6-x}$Pd$_x$ as a function of Ag/Pd composition are reported. The end member, CeCu$_6$, undergoes a structural phase transition from an orthorhombic ($Pnma$) to a monoclinic ($P2_1/c$) phase at 240 K. In CeCu$_{6-x}$Ag$_x$, the structural phase transition temperature (${T_{s}}$) decreases linearly with Ag concentration and extrapolates to zero at $x_{S}$ $\approx$ 0.1. The structural transition in CeCu$_{6-x}$Pd$_x$ remains unperturbed with Pd substitution within the range of our study. The lattice constant $b$ slightly decreases with Ag/Pd doping, whereas, $a$ and $c$ increase with an overall increase in the unit cell volume. Both systems, CeCu$_{6-x}$Ag$_x$ and CeCu$_{6-x}$Pd$_x$, exhibit a magnetic quantum critical point (QCP), at $x$ $\approx$ 0.2 and $x$ $\approx$ 0.05 respectively. Near the QCP, long range antiferromagnetic ordering takes place at an incommensurate wave vector ($\delta_1$ 0 $\delta_2$) where $\delta_1 \sim 0.62$, $\delta_2 \sim 0.25$, $x$ = 0.125 for CeCu$_{6-x}$Pd$_x$ and $\delta_1 \sim 0.64$, $\delta_2 \sim 0.3$, $x$ = 0.3 for CeCu$_{6-x}$Ag$_x$. The magnetic structure consists of an amplitude modulation of the Ce-moments which are aligned along the $c$-axis of the orthorhombic unit cell.
  • Single crystals of (Nd1-xCex)2Fe14B are grown out of Fe-(Nd,Ce) flux. Chemical and structural analysis of the crystals indicates that (Nd1-xCex)2Fe14B forms a solid solution until at least x = 0.38 with a Vegard-like variation of the lattice constants with x. Refinements of single crystal neutron diffraction data indicate that Ce has a slight site preference (7:3) for the 4g rare earth site over the 4f site. Magnetization measurements show that for x = 0.38 the saturation magnetization at 400 K, a temperature important to applications, falls from 29.8 for the parent Nd2Fe14B to 27.6 (mu)B/f.u., the anisotropy field decreases from 5.5 T to 4.7 T, and the Curie temperature decreases from 586 to 543 K. First principles calculations carried out within density functional theory are used to explain the decrease in magnetic properties due to Ce substitution. Though the presence of the lower-cost and more abundant Ce slightly affects these important magnetic characteristics, this decrease is not large enough to affect a multitude of applications. Ce-substituted Nd2Fe14B is therefore a potential high-performance permanent magnet material with substantially reduced Nd content.
  • The chiral helimagnet Cr1/3NbS2 has been investigated by magnetic, transport and thermal properties measurements on single crystals and by first principles electronic structure calculations. From the measured field and temperature dependence of the magnetization for fields applied perpendicular to the c axis, the magnetic phase diagram has been constructed in the vicinity of the phase transitions. A transition from a paramagnetic to a magnetically ordered phase occurs near 120 K. With increasing magnetic field and at temperatures below 120 K, this material undergoes transitions from a helimagnetic to a soliton-lattice phase near 900 Oe, and then to a ferromagnetic phase near 1300 Oe. The transitions are found to strongly affect the electrical transport. The resistivity decreases sharply upon cooling near 120 K, and the spin reorientation from the helimagnetic ground state to the commensurate ferromagnetic state is evident in the magnetoresistance. At high fields a large magnetoresistance (55 % at 140 kOe) is observed near the magnetic transition temperature. Heat capacity and electronic structure calculations show the density of states at the Fermi level is low in the magnetically ordered state. Effects of spin fluctuations are likely important in understanding the behavior of Cr1/3NbS2 near and above the magnetic ordering transitions.
  • The noncentrosymmetric ferromagnet Cr11Ge19 has been investigated by electrical transport, AC and DC magnetization, heat capacity, x-ray diffraction, resonant ultrasound spectroscopy, and first principles electronic structure calculations. Complex itinerant ferromagnetism in this material is indicated by nonlinearity in conventional Arrott plots, unusual behavior of AC susceptibility, and a weak heat capacity anomaly near the Curie temperature (88 K). The inclusion of spin wave excitations was found to be important in modeling the low temperature heat capacity. The temperature dependence of the elastic moduli and lattice constants, including negative thermal expansion along the c axis at low temperatures, indicate strong magneto-elastic coupling in this system. Calculations show strong evidence for itinerant ferromagnetism and suggest a noncollinear ground state may be expected.