• ### Saturation of ion irradiation effects in Cr2AlC(1601.05514)

Jan. 21, 2016 cond-mat.mtrl-sci
Cr2AlC materials were irradiated with 7 MeV Xe26+ ions and 500 keV He2+ ions at room temperature. A structural transition with an increased c lattice parameter and a decreased a lattice parameter occurs after irradiation to doses above 1 dpa. Nevertheless, the modified structure is stable up to the dose of 5.2 dpa without obvious lattice disorder. The three samples irradiated to doses above 1 dpa have comparable lattice parameters and hardness values, suggesting a saturation of irradiation effects in Cr2AlC. The structural transition and irradiation effects saturation are ascribed to irradiation-induced antisite defects (CrAl and AlCr) and C interstitials, which is supported by the calculations of the formation energies of various defects in Cr2AlC. The irradiation-induced antisite defects and C interstitials may be critical to understand the excellent resistance to irradiation-induced amorphization of MAX phases.
• ### Atomic Calligraphy: The Direct Writing of Nanoscale Structures using MEMS(1304.1334)

We present a micro-electromechanical system (MEMS) based method for the resist free patterning of nano-structures. Using a focused ion beam (FIB) to customize larger MEMS machines, we fabricate apertures as small as 50 nm on plates that can be moved with nanometer precision over an area greater than 20x20 {\mu}m^2. Depositing thermally evaporated gold atoms though the apertures while moving the plate results in the deposition of nanoscale metal patterns. Adding a shutter only microns above the aperture, enables high speed control of not only where but also when atoms are deposited. Using a shutter, different sized apertures can be selectively opened and closed for nano-structure fabrication with features ranging from nano- to micrometers in scale. The ability to evaporate materials with high precision, and thereby fabricate circuits and structures in situ, enables new kinds of experiments based on the interactions of a small number of atoms and eventually even single atoms.
• ### On Bayes' theorem for improper mixtures(1112.3228)

Dec. 14, 2011 math.ST, stat.TH
Although Bayes's theorem demands a prior that is a probability distribution on the parameter space, the calculus associated with Bayes's theorem sometimes generates sensible procedures from improper priors, Pitman's estimator being a good example. However, improper priors may also lead to Bayes procedures that are paradoxical or otherwise unsatisfactory, prompting some authors to insist that all priors be proper. This paper begins with the observation that an improper measure on Theta satisfying Kingman's countability condition is in fact a probability distribution on the power set. We show how to extend a model in such a way that the extended parameter space is the power set. Under an additional finiteness condition, which is needed for the existence of a sampling region, the conditions for Bayes's theorem are satisfied by the extension. Lack of interference ensures that the posterior distribution in the extended space is compatible with the original parameter space. Provided that the key finiteness condition is satisfied, this probabilistic analysis of the extended model may be interpreted as a vindication of improper Bayes procedures derived from the original model.
• ### CeNiAsO: an antiferromagnetic dense Kondo lattice(1103.3073)

A cerium containing pnictide, CeNiAsO, crystallized in the ZrCuSiAs type structure, has been investigated by measuring transport and magnetic properties, as well as specific heat. We found that CeNiAsO is an antiferromagnetic dense Kondo lattice metallic compound with Kondo scale $T_K \sim$ 15 K and shows an enhanced Sommerfeld coefficient of $\gamma_0 \sim$ 203 mJ/mol$\cdot$K$^{2}$. While no superconductivity can been observed down to 30 mK, Ce ions exhibit two successive antiferromagnetic (AFM) transitions. We propose that the magnetic moment of Ce ion could align in the G type AFM order below the first transition at $T_{N1}$=9.3 K, and it might be modified into the C type AFM order below a lower transition at $T_{N2}$=7.3 K. Our results indicate that the 3$d-4f$ interlayer Kondo interactions play an important role in Ni-based Ce-containing pnictide.