• Magnetic anisotropies of ferromagnetic thin films are induced by epitaxial strain from the substrate via strain-induced anisotropy in the orbital magnetic moment and that in the spatial distribution of spin-polarized electrons. However, the preferential orbital occupation in ferromagnetic metallic La$_{1-x}$Sr$_x$MnO$_3$ (LSMO) thin films studied by x-ray linear dichroism (XLD) has always been found out-of-plane for both tensile and compressive epitaxial strain and hence irrespective of the magnetic anisotropy. In order to resolve this mystery, we directly probed the preferential orbital occupation of spin-polarized electrons in LSMO thin films under strain by angle-dependent x-ray magnetic circular dichroism (XMCD). Anisotropy of the spin-density distribution was found to be in-plane for the tensile strain and out-of-plane for the compressive strain, consistent with the observed magnetic anisotropy. The ubiquitous out-of-plane preferential orbital occupation seen by XLD is attributed to the occupation of both spin-up and spin-down out-of-plane orbitals in the surface magnetic dead layer.
  • The strong perpendicular magnetic anisotropy of $L{\rm1_0}$-ordered FePt has been the subject of extensive studies for a long time. However, it is not known which element, Fe or Pt, mainly contributes to the magnetic anisotropy energy (MAE). We have investigated the anisotropy of the orbital magnetic moments of Fe 3$d$ and Pt 5$d$ electrons in $L{\rm1_0}$-ordered FePt thin films by Fe and Pt $L_{2,3}$-edge x-ray magnetic circular dichroism (XMCD) measurements for samples with various degrees of long-range chemical order $S$. Fe $L_{2,3}$-edge XMCD showed that the orbital magnetic moment was larger when the magnetic field was applied perpendicular to the film than parallel to it, and that the anisotropy of the orbital magnetic moment increased with $S$. Pt $L_{2,3}$-edge XMCD also showed that the orbital magnetic moment was smaller when the magnetic field was applied perpendicular to the film than parallel to it, opposite to the Fe $L_{2,3}$-edge XMCD results although the anisotropy of the orbital magnetic moment increases with $S$ like the Fe edge. These results are qualitatively consistent with the first-principles calculation by Solovyev ${\it et\ al.}$ [Phys. Rev. B $\bf{52}$, 13419 (1995).], which also predicts the dominant contributions of Pt 5$d$ to the magnetic anisotropy energy rather than Fe 3$d$ due to the strong spin-orbit coupling and the small spin splitting of the Pt 5$d$ bands in $L{\rm1_0}$-ordered FePt.
  • Thin films of the ferromagnetic metal SrRuO3 (SRO) show a varying easy magnetization axis depending on the epitaxial strain and undergo a metal-to-insulator transition with decreasing film thickness. We have investigated the magnetic properties of SRO thin films with varying thicknesses fabricated on SrTiO3(001) substrates by soft x-ray magnetic circular dichroism (XMCD) at the Ru M2,3 edge. Results have shown that, with decreasing film thickness, the film changes from ferromagnetic to non-magnetic around 3monolayer thickness, consistent with previous magnetization and magneto-optical Kerr effect measurements. The orbital magnetic moment perpendicular to the film was found to be ~ 0.1{\mu}B/Ru atom, and remained nearly unchanged with decreasing film thickness while the spin magnetic moment decreases. Mechanism for the formation of the orbital magnetic moment is discussed based on the electronic structure of the compressively strained SRO film.
  • We have studied the electronic and magnetic states of Co and Mn atoms at the interface of the Co$_\mathrm{2}$Mn$_{\beta}$Si (CMS)/MgO ($\beta$=0.69, 0.99, 1.15 and 1.29) magnetic tunnel junction (MTJ) by means of x-ray magnetic circular dichroism. In particular, the Mn composition ($\beta$) dependences of the Mn and Co magnetic moments were investigated. The experimental spin magnetic moments of Mn, $m_\mathrm{spin}$(Mn), derived from XMCD weakly decreased with increasing Mn composition $\beta$ in going from Mn-deficient to Mn-rich CMS films. This behavior was explained by first-principles calculations based on the antisite-based site-specific formula unit (SSFU) composition model, which assumes the formation of only antisite defect, not vacancies, to accommodate off-stoichiometry. Furthermore, the experimental spin magnetic moments of Co, $m_\mathrm{spin}$(Co), also weakly decreased with increasing Mn composition. This behavior was consistently explained by the antisite-based SSFU model, in particular, by the decrease in the concentration of Co$_\mathrm{Mn}$ antisites detrimental to the half-metallicity of CMS with increasing $\beta$. This finding is consistent with the higher TMR ratios which have been observed for CMS/MgO/CMS MTJs with Mn-rich CMS electrodes.
  • We have investigated the electronic and magnetic properties of Co-doped Pr0.8Ca0.2MnO3 thin films using various spectroscopic techniques. X-ray absorption and hard x-ray photoemission spectroscopy revealed that the substituted Co ions are in the divalent state, resulting in hole doping on the Mn atoms. Studies of element-selective magnetic properties by x-ray magnetic circular dichroism found a large orbital magnetic moment for the Co ions. These spectroscopic studies reveal that the substituted Co ions play several roles of hole doping for Mn, ferromagnetic superexchange coupling between the Co2+ and Mn4+ ions, and orbital magnetism of the Co2+ ions. Competition among these complex interactions produces the unique electronic and magnetic behaviors including enhanced coercivity of the Co-doped Pr0.8Ca0.2MnO3.
  • We have investigated the spin and orbital magnetic moments of Fe in FePt nanoparticles in the $L$1$_{0}$-ordered phase coated with SiO$_{2}$ by x-ray absorption spectroscopy (XAS) and x-ray magnetic circular dichroism (XMCD) measurements at the Fe $L_{\rm 2,3}$ absorption edges. Using XMCD sum rules, we evaluated the ratio of the orbital magnetic moment ($M_{\rm orb}$) to the spin magnetic moment ($M_{\rm spin}$) of Fe to be $M_{\rm orb}/M_{\rm spin}$ = 0.08. This $M_{\rm orb}/M_{\rm spin}$ value is comparable to the value (0.09) obtained for FePt nanoparticles prepared by gas phase condensation, and is larger than the values ($\sim$0.05) obtained for FePt thin films, indicating a high degree of $L$1$_{0}$ order. The hysteretic behavior of the FePt component of the magnetization was measured by XMCD. The magnetic coercivity ($H_{\rm c}$) was found to be as large as 1.8 T at room temperature, $\sim$3 times larger than the thin film value and $\sim$50 times larger than that of the gas phase condensed nanoparticles. The hysteresis curve is well explained by the Stoner-Wohlfarth model for non-interacting single-domain nanoparticles with the $H_{\rm c}$ distributed from 1 T to 5 T.
  • In the perovskite-type Ca$_{1-x}$Ce$_{x}$MnO$_{3}$ (CCMO), one can control the transport and magnetic properties through varying Ce content. In the case of thin films, the properties can also be controlled by epitaxial strain from the substrate through changing it such as YAlO$_{3}$ (YAO), NdAlO$_{3}$ (NAO), and LaSrAlO$_{4}$ (LSAO). However, one cannot measure the magnetization of thin films on NAO substrates by conventional magnetization measurements because of the strong paramagnetic signals from the Nd$^{3+}$ ions. In order to eliminate the influence of Nd$^{3+}$ and to identify magnetic phases of the CCMO thin films, we have performed element-selective X-ray magnetic circular dichroism (XMCD) measurements of the Mn 2{\it p} core level. By studying the anisotropy of the XMCD intensity, we could unambiguously determine the magnetic phase diagram of the CCMO thin films.
  • The coercivity of La$_{1-x}$Sr$_x$MnO$_3$ thin films can be enhanced by Ru substitution for Mn. In order to elucidate its mechanism, we performed soft x-ray absorption and magnetic circular dichroism measurements at the Ru M$_{2,3}$ and Mn L$_{2,3}$ edges. We found that the spin direction of Ru and Mn are opposite and that Ru has a finite orbital magnetic moment. Cluster-model analysis indicated that the finite orbital magnetic moment as well as the reduced spin moment of Ru result from local lattice distortion caused by epitaxial strain from the SrTiO$_3$ substrate in the presence of spin-orbit interaction.
  • BiFeO$_3$ (BFO) shows both ferroelectricity and magnetic ordering at room temperature but its ferromagnetic component, which is due to spin canting, is negligible. Substitution of transition-metal atoms such as Co for Fe is known to enhance the ferromagnetic component in BFO. In order to reveal the origin of such magnetization enhancement, we performed soft x-ray absorption spectroscopy (XAS) and soft x-ray magnetic circular dichroism (XMCD) studies of BiFe$_{1-x}$Co$_x$O$_3$ ({\it x} = 0 to 0.30) (BFCO) thin films grown on LaAlO$_3$(001) substrates. The XAS results indicated that the Fe and Co ions are in the Fe$^{3+}$ and Co$^{3+}$ states. The XMCD results showed that the Fe ions show ferromagnetism while the Co ions are antiferromagnetic at room temperature. The XAS and XMCD measurements also revealed that part of the Fe$^{3+}$ ions are tetrahedrally co-ordinated by oxygen ions but that the XMCD signals of the octahedrally coordinated Fe$^{3+}$ ions increase with Co content. The results suggest that an impurity phase such as the ferrimagnetic $\gamma$-Fe$_2$O$_3$ which exists at low Co concentration decreases with increasing Co concentration and that the ferromagnetic component of the Fe$^{3+}$ ion in the octrahedral crystal fields increases with Co concentration, probably reflecting the increased canting of the Fe$^{3+}$ ions.
  • We have studied the electronic structure of Ba(Fe$_{1-x}$Mn$_{x}$)$_{2}$As$_{2}$ ($x$=0.08), which fails to become a superconductor in spite of the formal hole doping like Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$, by photoemission spectroscopy and X-ray absorption spectroscopy (XAS). With decreasing temperature, a transition from the paramagnetic phase to the antiferromagnetic phase was clearly observed by angle-resolved photoemission spectroscopy. XAS results indicated that the substituted Mn atoms form a strongly hybridized ground state. Resonance-photoemission spectra at the Mn $L_{3}$ edge revealed that the Mn 3d partial density of states is distributed over a wide energy range of 2-13 eV below the Fermi level ($E_F$), with little contribution around $E_F$. This indicates that the dopant Mn 3$d$ states are localized in spite of the strong Mn 3d-As $4p$ hybridization and split into the occupied and unoccupied parts due to the on-site Coulomb and exchange interaction. The absence of superconductivity in Ba(Fe$_{1-x}$Mn$_{x}$)$_{2}$As$_{2}$ can thus be ascribed both to the absence of carrier doping in the FeAs plane, and to the strong stabilizaiton of the antiferromagnetic order by the Mn impurities.
  • Unusual low temperature magneto-resistance (MR) of ferromagnetic Sr$_{2}$FeMoO$_{6}$ polycrystals has been attributed to magnetically hard grain boundaries which act as spin valves. We detected the different magnetic hysteresis curves for the grains and the grain boundaries of polycrystalline Sr$_{2}$FeMoO$_{6}$ by utilizing the different probing depths of the different detection modes of x-ray absorption spectroscopy (XAS) and x-ray magnetic circular dichroism (XMCD), namely, the total electron yield (TEY) mode (probing depth $\sim$5 nm) and the total fluorescence yield (TFY) mode (probing depth $\sim$100 nm). At 20 K, the magnetic coercivity detected in the TEY mode ($H_{\rm c,TEY}$) was several times larger than that in the TFY mode ($H_{\rm c,TFY}$), indicating harder ferromagnetism of the grain boundaries than that of the grains. At room temperature, the grain boundary magnetism became soft and $H_{\rm c,TEY}$ and $H_{\rm c,TFY}$ were nearly the same. From line-shape analysis of the XAS and XMCD spectra, we found that in the grain boundary region the ferromagnetic component is dominated by Fe$^{2+}$ or well-screened signals while the non-magnetic component is dominated by Fe$^{3+}$ or poorly-screened signals.
  • We report on x-ray absorption spectroscopy (XAS) and x-ray magnetic circular dichroism (XMCD) studies of the paramagnetic (Mn,Co)-co-doped ZnO and ferromagnetic (Fe,Co)-co-doped ZnO nano-particles. Both the surface-sensitive total-electron-yield mode and the bulk-sensitive total-fluorescence-yield mode have been employed to extract the valence and spin states of the surface and inner core regions of the nano-particles. XAS spectra reveal that significant part of the doped Mn and Co atoms are found in the trivalent and tetravalent state in particular in the surface region while majority of Fe atoms are found in the trivalent state both in the inner core region and surface region. The XMCD spectra show that the Fe$^{3+}$ ions in the surface region give rise to the ferromagnetism while both the Co and Mn ions in the surface region show only paramagnetic behaviors. The transition-metal atoms in the inner core region do not show magnetic signals, meaning that they are antiferromagnetically coupled. The present result combined with the previous results on transition-metal-doped ZnO nano-particles and nano-wires suggest that doped holes, probably due to Zn vacancy formation at the surfaces of the nano-particles and nano-wires, rather than doped electrons are involved in the occurrence of ferromagnetism in these systems.
  • We have studied magnetism in anatase Ti$_{1-x}$Co$_x$O$_{2-\delta}$ ({\it x} = 0.05) thin films with various electron carrier densities, by soft x-ray magnetic circular dichroism (XMCD) measurements at the Co $L_{2,3}$ absorption edges. For electrically conducting samples, the magnetic moment estimated by XMCD was $<$ 0.3 $\mu_B$/Co using the surface-sensitive total electron yield (TEY) mode, while it was 0.3-2.4 $\mu_B$/Co using the bulk-sensitive total fluorescence yield (TFY) mode. The latter value is in the same range as the saturation magnetization 0.6-2.1 $\mu_B$/Co deduced by SQUID measurement. The magnetization and the XMCD intensity increased with carrier density, consistent with the carrier-induced origin of the ferromagnetism.