• Structure and composition of iron chalcogenides have a delicate relationship with magnetism and superconductivity. In this report we investigate the iron sulfide layered tetragonal phase (t-FeS), and compare with three-dimensional hexagonal phase (h-FeS). X-ray diffraction reveals the absence of structural transitions for both t- and h-FeS below room temperature, and gives phase compositions of Fe0.93(1)S and Fe0.84(1)S, respectively, for the samples studied here. The a lattice parameter of bigger than 3.68 A is significant for causing bulk superconductivity in iron sulfide, which is controlled by composition and structural details such as iron stoichiometry and concentration of vacancy. While h-FeS with a = 3.4436(1) A has magnetic ordering well above room temperature, our t-FeS with a =3.6779(8)A shows filamentary superconductivity below Tc = 4 K with less than 15% superconducting volume fraction. Also for t-FeS, the magnetic susceptibility shows an anomaly at ~ 15 K, and neutron diffraction reveals a commensurate antiferromagnetic ordering below TN = 116 K, with wave vector km= (0.25,0.25,0) and 0.46(2)uB/Fe. Although two synthesis routes are used here to stabilize t vs h crystal structures (hydrothermal vs solid-state methods), both FeS compounds order on two length-scales of ~1000 nm sheets or blocks and ~ 20 nm smaller particles, shown by neutron scattering. First principles calculations reveal a high sensitivity to the structure for the electronic and magnetic properties in t-FeS, predicting marginal antiferromagnetic instability for our compound (sulfur height of zS ~0.252) with an ordering energy of ~11 meV/Fe, while h-FeS is magnetically stable.
  • We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16 T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal was measured and confirms the presence of (non d-wave) nodes in the superconducting gap structure for measurements at 5 T and below. The nodal effects were suppressed at high fields. At low fields, a VL reorientation transition was observed between 1 T and 3 T, with the VL orientation changing by 45{\deg}. Below 1 T, the VL structure was strongly affected by pinning and the diffraction pattern had a fourfold symmetry. We suggest that this (and possibly also the VL reorientation) is due to pinning to defects aligned with the crystal structure, rather than being intrinsic.
  • The superconductor TmNi2B2C possesses a significant four-fold basal plane anisotropy, leading to a square Vortex Lattice (VL) at intermediate fields. However, unlike other members of the borocarbide superconductors, the anisotropy in TmNi2B2C appears to decrease with increasing field, evident by a reentrance of the square VL phase. We have used Small Angle Neutron Scattering measurements of the VL to study the field dependence of the anisotropy. Our results provide a direct, quantitative measurement of the decreasing anisotropy. We attribute this reduction of the basal plane anisotropy to the strong Pauli paramagnetic effects observed in TmNi2B2C and the resulting expansion of vortex cores near Hc2.