• Under ambient conditions, we directly observed NaCl crystals experimentally in the rGO membranes soaked in the salt solution with concentration below and far below the saturated concentration. Moreover, in most probability, the NaCl crystals show stoichiometries behavior. We attribute this unexpected crystallization to the cation-{\pi} interactions between the ions and the aromatic rings of the rGO.
  • Cr2AlC materials were irradiated with 7 MeV Xe26+ ions and 500 keV He2+ ions at room temperature. A structural transition with an increased c lattice parameter and a decreased a lattice parameter occurs after irradiation to doses above 1 dpa. Nevertheless, the modified structure is stable up to the dose of 5.2 dpa without obvious lattice disorder. The three samples irradiated to doses above 1 dpa have comparable lattice parameters and hardness values, suggesting a saturation of irradiation effects in Cr2AlC. The structural transition and irradiation effects saturation are ascribed to irradiation-induced antisite defects (CrAl and AlCr) and C interstitials, which is supported by the calculations of the formation energies of various defects in Cr2AlC. The irradiation-induced antisite defects and C interstitials may be critical to understand the excellent resistance to irradiation-induced amorphization of MAX phases.
  • Irradiation effects in Ni-17Mo-7Cr alloy, which is an newly developed structural material for molten salt reactor (MSR), have been systematically investigated by using 3MeV Au ions at different fluences, corresponding to dpa number (displacement per atom) of 1~ 30. GIXRD measurement indicates that the microstrain of the irradiated samples increased from 0.14% to 0.22% as dpa increased from 1 to 30. In the meanwhile, nanoindentation results reveal the Ni-17Mo-7Cr alloy underwent radiation-induced hardening first and then softening at dpa of 30. The swelling rate of Ni-17Mo-7Cr alloy was found around 1.3% at 30 dpa, which means only 0.04% per dpa. Besides, Raman spectra shows that carbon segregation appeared after Au ions irradiation. Our results are very helpful for understanding irradiation damages in Nickel-base alloys, especially for those in purpose of being used in future MSR nuclear energy system.