La-filled skutterudites LaxCo4Sb12 (x : 0.25 and 0.5) have been synthesized and sintered in one step under high-pressure conditions at 3.5 GPa in a piston-cylinder hydrostatic press. The structural properties of the reaction products were characterized by synchrotron X-ray powder diffraction, clearly showing an uneven filling factor of the skutterudite phases, confirmed by transmission electron microscopy. The non-homogeneous distribution of La filling atoms is adequate to produce a significant decrease in lattice thermal conductivity, mainly due to strain field scattering of high-energy phonons. Furthermore, the lanthanum filler primarily acts as an Einstein-like vibrational mode having a strong impact on the phonon scattering. Extra-low thermal conductivity values of 2.39 W/mK and 1.30 W/mK are measured for La0.25Co4Sb12 and La0.5Co4Sb12 nominal compositions at 780 K, respectively. Besides this, lanthanum atoms have contributed to increase the charge carrier concentration in the samples. In the case of La0.25Co4Sb12, there is an enhancement of the power factor and an improvement of the thermoelectric properties.

SmFeO3 has attracted considerable attention very recently due to the reported multiferroic properties above room-temperature. We have performed powder and single crystal neutron diffraction as well as complementary polarization dependent soft X-ray absorption spectroscopy measurements on floating-zone grown SmFeO3 single crystals in order to determine its magnetic structure. We found a k=0 G-type collinear antiferromagnetic structure that is not compatible with inverse Dzyaloshinskii-Moriya interaction driven ferroelectricity. While the structural data reveals a clear sign for magneto-elastic coupling at the N\'eel-temperature of ~675 K, the dielectric measurements remain silent as far as ferroelectricity is concerned.

How the magnetoelectric coupling actually occurs on a microscopic level in multiferroic BiFeO3 is not well known. By using the high-resolution single crystal neutron diffraction techniques, we have determined the electric polarization of each individual elements of BiFeO3, and concluded that the magnetostrictive coupling suppresses the electric polarization at the Fe site below TN. This negative magnetoelectric coupling appears to outweigh the spin current contributions arising from the cycloid spin structure, which should produce a positive magnetoelectric coupling.

High-resolution and high-flux neutron as well as X-ray powder-diffraction experiments were performed on the oxypnictide series LaO(1-x)FxFeAs with 0<x<0.15 in order to study the crystal and magnetic structure. The magnetic symmetry of the undoped compound corresponds to those reported for ReOFeAs (with Re a rare earth) and for AFe2As2 (A=Ba, Sr) materials. We find an ordered magnetic moment of 0.63(1)muB at 2 K in LaOFeAs, which is significantly larger than the values previously reported for this compound. A sizable ordered magnetic moment is observed up to a F-doping of 4.5% whereas there is no magnetic order for a sample with a F concentration of x=0.06. In the undoped sample, several interatomic distances and FeAs4 tetrahedra angles exhibit pronounced anomalies connected with the broad structural transition and with the onset of magnetism supporting the idea of strong magneto-elastic coupling in this material.

We have performed high resolution neutron diffraction and inelastic neutron scattering experiments in the frustrated multiferroic hexagonal compounds RMnO3 (R=Ho, Yb, Sc, Y), which provide evidence of a strong magneto-elastic coupling in the the whole family. We can correlate the atomic positions, the type of magnetic structure and the nature of the spin waves whatever the R ion and temperature. The key parameter is the position of the Mn ions in the unit cell with respect to a critical threshold of 1/3, which determines the sign of the coupling between Mn triangular planes.

We present a combined neutron and synchrotron powder diffraction study of the crystal and magnetic structure of VOCl. The occurrence of antiferromagnetic order in VOCl is accompanied by a monoclinic distortion. The high sensitivity of the magnetic interaction parameters on V-O-V bond angles and V-V distances yields strong magnetoelastic coupling which implies the structural distortion below T$_N$ as well as anomalous structural effects in the paramagnetic phase.

We present a combination of ab initio calculations, magnetic Compton scattering and polarized neutron experiments, which elucidate the density distribution of unpaired electrons in the kagome staircase system Co3V2O8. Ab initio wave functions were used to calculate the spin densities in real and momentum space, which show good agreement with the respective experiments. It has been found that the spin polarized orbitals are equally distributed between the t2g and the eg levels for the spine (s) Co ions, while the eg orbitals of the cross-tie (c) Co ions only represent 30% of the atomic spin density. Furthermore, the results reveal that the magnetic moments of the cross-tie Co ions, which are significantly smaller than those of the spine Co ions in the zero-field ferromagnetic structure, do not saturate by applying an external magnetic field of 2 T along the easy axis a, but that the increasing bulk magnetization originates from induced magnetic moments on the O and V sites. The refined individual magnetic moments are mu(Co_c)=1.54(4) mu_B, mu(Co_s)=2.87(3) mu_B, mu(V)=0.41(4) mu_B, mu(O1)=0.05(5) mu_B, mu(O2)=0.35(5) mu_B, and; mu(O3)=0.36(5) mu_B combining to the same macroscopic magnetization value, which was previously only attributed to the Co ions.

The crystal structure of LnFeAsO$_{1-y}$ (Ln = La, Nd) has been studied by the powder neutron diffraction technique. The superconducting phase diagram of NdFeAsO$_{1-y}$ is established as a function of oxygen content which is determined by Rietveld refinement. The small As-Fe bond length suggests that As and Fe atoms are connected covalently. FeAs$_4$-tetrahedrons transform toward a regular shape with increasing oxygen deficiency. Superconducting transition temperatures seem to attain maximum values for regular FeAs$_4$-tetrahedrons.