• Single crystal neutron diffraction is combined with synchrotron x-ray scattering to identify the different superlattice phases present in $Cs_{0.8}Fe_{1.6}Se_2$. A combination of single crystal refinements and first principles modelling are used to provide structural solutions for the $\sqrt{5}\times\sqrt{5}$ and $\sqrt{2}\times\sqrt{2}$ superlattice phases. The $\sqrt{5}\times\sqrt{5}$ superlattice structure is predominantly composed of ordered Fe vacancies and Fe distortions, whereas the $\sqrt{2}\times\sqrt{2}$ superlattice is composed of ordered Cs vacancies. The Cs vacancies only order within the plane, causing Bragg rods in reciprocal space. By mapping x-ray diffraction measurements with narrow spatial resolution over the surface of the sample, the structural domain pattern was determined, consistent with the notion of a majority antiferromagnetic $\sqrt{5}\times\sqrt{5}$ phase and a superconducting $\sqrt{2}\times\sqrt{2}$ phase.
  • The crystal structure of layered metal IrTe2 is determined using single-crystal x-ray diffraction. At T=220 K, it exhibits Ir and Te dimers forming a valence-bond crystal. Electronic structure calculations reveal an intriguing quasi-two-dimensional electronic state, with planes of reduced density of states cutting diagonally through the Ir and Te layers. These planes are formed by the Ir and Te dimers, which exhibit a signature of covalent bonding character development. Evidence for significant charge disproportionation among the dimerized and non-dimerized Ir (charge order) is also presented.
  • Here we present neutron diffraction results on the mineral azurite. We have found that the crystal structure of azurite can be described in the space group $P2_1$ which is the next lower symmetric group of $P2_1/c$ as found in earlier work. This small change in symmetry does not greatly influence the lattice parameters or atomic fractional coordinates which are presented here for single crystal diffraction refinements. The ordered magnetic moment structure of this material has been determined and is comprised of two inequivalent magnetic moments on copper sites of magnitude 0.68(1) and 0.25(1) $\mu_{B}$. This result is discussed in terms of the anisotropic exchange and Dzyaloshinskii-Moriya interactions. It is found that the system is likely governed by one-dimensional behaviour despite the long-range ordered ground state. We also highlight the significance of strain in this material which is strongly coupled to the magnetism.
  • The sodium reordering in NaxCoO2 in the vicinity of room temperature is rationalized at high x in terms of phase transitions between square and striped phases. A striking hexagon-of-hexagons diffraction pattern observed for x=0.78 can be reproduced using coexisting square and striped phases that are related by simple shear deformations. All compositions exhibit a partial melting transition to a disordered stripe phase just below room temperature, which alters the topology of the electrical conduction pathways.
  • The influence of electrostatic interactions on the ordering of sodium ions in Na$_x$CoO$_2$ is studied theoretically through Monte-Carlo simulations. For large $x$ small di- or tri-vacancy clusters are stable with respect to isolated Na vacancies. At commensurate fillings these small clusters order in triangular superstructures. These results agree with recent electron diffraction data at $x=1/2$ and 3/4. We have performed neutron La\"ue diffraction experiments at higher $x$, which confirm the predictions of this simple model. The consequences on the properties of the electronic charges in the Co layers are discussed.