• Lithium thioindate (LiInS$_{2}$) is a new nonlinear chalcogenide biaxial material transparent from 0.4 to 12 $\mu$m, that has been successfully grown in large sizes and good optical quality. We report on new physical properties that are relevant for laser and nonlinear optics applications. With respect to AgGaS(e)$_2$ ternary chalcopyrite materials, LiInS$_{2}$ displays a nearly-isotropic thermal expansion behavior, a 5-times larger thermal conductivity associated with high optical damage thresholds, and an extremely low intensity-dependent absorption allowing direct high-power downconversion from the near-IR to the deep mid-IR. Continuous-wave difference-frequency generation (5-11$ \mu$m) of Ti:sapphire laser sources is reported for the first time.
  • The pressure influence on the lattice vibration of $CaZnF_4$ has been studied by Raman diffusion up to 17 GPa. Most Raman frequencies increase with increasing pressure. Three singularities in the pressure induced frequency evolution are observed around 1.5 GPa, 10 GPa and 17 GPa. The samples pressurized to 17 GPa or higher do not revert to the ambient pressure phase after being released, the new phase showing different Raman spectra from the ordinary one. It is suggested that $CaZnF_4$ undergoes probably sudden lattice deformations at about 1.5 GPa and 10 GPa, and an irreversible phase transformation above 17 GPa.