• Based on a combination of X-ray diffraction, electrical transports, magnetic susceptibility, specific heat and pressure effect measurements, we report a series of BiS$_{2}$-based Sr$_{1-x}$Pr$_{x}$FBiS$_{2}$ superconductors with the maximum $T_c$ of 2.7 K for $x =$ 0.5 at ambient pressure. Superconductivity can be only observed at 0.4 $\leq$ x $\leq$ 0.7 while the normal state resistivity shows the semiconducting-like behaviors. $\chi(T)$ displays the low superconducting shielding volume fractions and $C(T)$ does not exhibit distinguishable anomaly around $T_c$, suggesting a filamentary superconductivity in the Pr-doped polycrystalline samples. By varying doping concentrations, an electrnoic phase diagram can thus be established. Upon applying pressure on the optimal doping Sr$_{0.5}$Pr$_{0.5}$FBiS$_{2}$ system, $T_c$ is abruptly enhanced, reaches 8.5 K at a critical pressure of $P_c =$ 1.5 GPa and remains a slight increase up to 9.7 K up to 2.5 GPa. Accompanied with the enhancement of superconductivity from the low-$T_c$ phase to the high-$T_c$ phase, the normal state undergoes a semiconductor-to-metal transition under pressure. The scenario can be linked to the enhancement of orbital overlap of Bi-6p and S-p, contributing to the bulk superconductivity above $P_c$. Phase diagram for Sr$_{0.5}$Pr$_{0.5}$FBiS$_{2}$ is also obtained.
  • For a class of 2D hybrid organic-inorganic perovskite semiconductors based on $\pi$-conjugated organic cations, we predict quantitatively how varying the organic and inorganic component allows control over the nature, energy and localization of carrier states in a quantum-well-like fashion. Our first-principles predictions, based on large-scale hybrid density-functional theory with spin-orbit coupling, show that the interface between the organic and inorganic parts within a single hybrid can be modulated systematically, enabling us to select between different type-I and type-II energy level alignments. Energy levels, recombination properties and transport behavior of electrons and holes thus become tunable by choosing specific organic functionalizations and juxtaposing them with suitable inorganic components.
  • We have grown the MoAs2 single crystal which crystallizes in a monoclinic structure with C12=m1 space group. Transport measurements show that MoAs2 displays a metallic behavior at zero field and undergoes a metal-to-semiconductor crossover below 70 K when the applied magnetic field is over 5 T. A robust resistivity plateau appears below 18 K and persists for the field up to 9 T. A large positive magnetoresistance, reaching about 2600% at 2 K and 9 T, is observed when the field is perpendicular to the current direction. The magnetoresistance becomes negative below 40 K when the field is parallel to the current direction. The Hall resistivity shows the non-linear field-dependence below 100 K. All these results enrich the transport properties of the transition-metal dipnictides, a large family which in general displays variable metallic and topological features.